Printing process for forming leather surface foaming effect on spinning base material

A technology of leather surface foaming and printing technology, which is applied in printing, post-processing of printing, copying/marking methods, etc. It can solve the problems of easy-to-wear, long-time consumption, and high cost, so as to ensure the quality of use and reduce production costs , the effect of improving work efficiency

Active Publication Date: 2019-09-06
叶王建
View PDF14 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In the prior art, if a surface with leather foaming effect is to be formed on the textile base material, embossing must be carried out on the leather base material, and the selection of the base material is limited. Process, mold embossing needs to engrave copper mold, which is costly and time consuming. Moreover, because the embossing is directly on the leather surface, the formed pattern area and the leather surface have obvious concave and convex marks, the integrity is not strong, and the edge of the pattern is easy to be damaged. The base material, the pressed pattern will appear hard, and it will be easy to lose shape after a long time, which will affect the quality of the product

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Printing process for forming leather surface foaming effect on spinning base material
  • Printing process for forming leather surface foaming effect on spinning base material

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0025] A printing process for forming leather surface foaming effects on textile substrates, specifically comprising the following steps:

[0026] (1) Get the release PET film, print black TPU ink on the release surface of the release PET film, dry or dry for use;

[0027] (2) print elastic TPU transparent oil on the black TPU ink surface that step (1) forms, dry or dry stand-by;

[0028] (3) Print foaming pattern glue on the elastic TPU transparent oil surface formed in step (2), dry or dry for later use;

[0029] (4) Print hot melt adhesive on the surface of the foamed glue formed in step (3), dry it or dry it for 10 minutes, put it in an oven at 120°C, bake it for 20 minutes, take it out and cool it;

[0030] (5) Take the textile substrate, and compound the hot melt adhesive surface formed in step (4) with the textile substrate by a pressing machine, the temperature of the pressing machine is 100°C, the pressure is 30kg, and the composite time is 30s;

[0031] (6) Cool th...

Embodiment 2

[0035] A printing process for forming leather surface foaming effects on textile substrates, specifically comprising the following steps:

[0036] (1) Get the release PET film, print black TPU ink on the release surface of the release PET film, dry or dry for use;

[0037] (2) print elastic TPU transparent oil on the black TPU ink surface that step (1) forms, dry or dry stand-by;

[0038] (3) Print foaming pattern glue on the elastic TPU transparent oil surface formed in step (2), dry or dry for later use;

[0039] (4) Print hot melt adhesive on the surface of the foamed glue formed in step (3), dry it or dry it for 30 minutes, put it in an oven at 160°C, bake it for 10 minutes, take it out and cool it;

[0040] (5) Get the textile substrate, and compound the hot melt adhesive surface formed in step (4) with the textile substrate by a pressing machine, the temperature of the pressing machine is 180°C, the pressure is 10kg, and the composite time is 10s;

[0041] (6) Cool the...

Embodiment 3

[0045] A printing process for forming leather surface foaming effects on textile substrates, specifically comprising the following steps:

[0046] (1) Get the release PET film, print black TPU ink on the release surface of the release PET film, dry or dry for use;

[0047] (2) print elastic TPU transparent oil on the black TPU ink surface that step (1) forms, dry or dry stand-by;

[0048] (3) Print foam glue on the elastic TPU transparent oil surface formed in step (2), dry or dry for later use;

[0049] (4) Print hot melt adhesive on the surface of the foamed glue formed in step (3), dry it or dry it for 25 minutes, put it in an oven at 150°C, bake it for 15 minutes, take it out and cool it;

[0050] (5) Take the textile substrate, and compound the hot melt adhesive surface formed in step (4) with the textile substrate by a pressing machine, the temperature of the pressing machine is 150°C, the pressure is 15kg, and the composite time is 20s;

[0051] (6) Cool the finished ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a printing process for forming a leather surface foaming effect on a spinning base material. The printing process specifically comprises the following steps that (1) black TPUink is printed on the release face of a release PET film, and the release PET film is aired or dried for standby application; (2) elastic TPU transparent oil is printed on the black TPU ink face, andthe release PET film is aired or dried for standby application; (3) foaming pattern mucilage is printed on the elastic TPU transparent oil face, and the release PET film is aired or dried for standbyapplication; (4) hot melt glue is printed on the foaming mucilage face formed in the step (3), after being aired or dried for 10 min to 30 min, the release PET film is placed in a drying box of 120 DEG C-160 DEG C, and the release PET film is taken out to be cooled after being baked for 10 min to 20 min; (5) the hot melt glue face and the spinning base material are compounded through a pressing machine; and (6) a product obtained after compounding is cooled, the PET film is finally stripped, and a spinning product with the surface with the leather surface foaming effect is formed. By means ofthe printing process, the leather surface foaming effect can be formed on multiple spinning base materials, foaming patterns protrude from inside to outside, and third dimension is high.

Description

technical field [0001] The invention relates to the field of printing, in particular to a printing process for forming a foaming effect on a leather surface on a textile substrate. Background technique [0002] Printing is a comprehensive technology integrating chemistry, physics and machinery. Printing is the process of making color paste from dyes or paints and applying them on textiles to print patterns. The processing methods used in textile printing , called the printing process. In the prior art, if a surface with leather foaming effect is to be formed on the textile base material, embossing must be carried out on the leather base material, and the selection of the base material is limited. Process, mold embossing needs to engrave copper mold, which is costly and time consuming. Moreover, because the embossing is directly on the leather surface, the formed pattern area and the leather surface have obvious concave and convex marks, the integrity is not strong, and the ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): B41M5/382B41M5/00B41M7/00
CPCB41M5/00B41M5/382B41M7/009
Inventor 叶王建
Owner 叶王建
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com