A high-strength, enamel technology, which is applied in the field of ceramic glazes, can solve the problems that the glaze coating does not have high hardness and cannot improve the wear resistance of ceramic products, and achieves good glaze smoothness, wide firing range and high hardness. Effect

Pending Publication Date: 2019-09-10
山东华浩陶瓷有限公司
View PDF5 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Since ceramic products are mostly made into daily necessities, the surface hardness of ceramic products is very high, and ceramics need to have good wear resistance, so the glaze on the surface of ceramics needs to have high hardness and high wear resistance. However, the existing glaze The coating does not have high hardness and cannot improve the wear resistance of ceramic products

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0029] A high-strength enamel material comprises the following raw materials in parts by weight: 50 kg of feldspar, 8 kg of quartz, 4 kg of calcite, 6 kg of barium carbonate, 7 kg of calcined talc, 3 kg of kaolin, 3 kg of calcined kaolin, and 1 kg of zinc oxide.

[0030] The preparation method of described high-strength enamel material comprises the following steps:

[0031] (1) Pulverize each raw material respectively, and mix and stir evenly to obtain a mixture;

[0032] (2) Melting the mixture and quenching in water to obtain block glaze;

[0033] (3) After wet ball milling, the block glaze is sieved to obtain a glaze slurry, which is applied to the surface of the green body, dried, calcined, and cooled to obtain a high-strength porcelain glaze.

Embodiment 2

[0035] A high-strength enamel material comprises the following raw materials in parts by weight: 53 kg of feldspar, 9 kg of quartz, 5 kg of calcite, 7 kg of barium carbonate, 8 kg of calcined talc, 4 kg of kaolin, 4 kg of calcined kaolin, and 2 kg of zinc oxide.

[0036] The preparation method of described high-strength enamel material comprises the following steps:

[0037] (1) Pulverize each raw material respectively, and mix and stir evenly to obtain a mixture with a fineness of 100 mesh;

[0038] (2) Melting the mixture for 2 hours at a temperature of 1200°C, and quenching in water to obtain a block glaze;

[0039] (3) The block glaze is wet ball milled, and the weight ratio of the block glaze to water is 1:0.5, and the fineness is 300 mesh and the concentration is 1.5g / ml glaze slurry after sieving, Apply the glaze slurry to the surface of the body, dry at 40°C for 6 hours, then calcinate at 1000°C for 30 hours, and cool to obtain high-strength enamel.

Embodiment 3

[0041] A high-strength enamel material comprises the following raw materials in parts by weight: 60 kg of feldspar, 10 kg of quartz, 5 kg of calcite, 7 kg of barium carbonate, 8 kg of calcined talc, 4 kg of kaolin, 4 kg of calcined kaolin, and 2 kg of zinc oxide.

[0042] The preparation method of described high-strength enamel material comprises the following steps:

[0043] (1) Pulverize each raw material respectively, and mix and stir evenly to obtain a mixture with a fineness of 110 mesh;

[0044] (2) Melting the mixture for 2 hours at a temperature of 1250°C, and quenching in water to obtain a block glaze;

[0045] (3) The block glaze is wet ball milled, and the weight ratio of the block glaze to water is 1:0.6, and the fineness is 400 mesh and the concentration is 1.5g / ml glaze slurry after sieving, Apply the glaze slurry to the surface of the green body, dry at 43°C for 6 hours, then calcinate at 1100°C for 25 hours, and cool to obtain high-strength enamel.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a high-strength porcelain glaze and a preparation method thereof. The high-strength porcelain glaze comprises the following materials: 50-70 parts of feldspar, 8-12 parts of quartz, 4-6 parts of calcite, 6-8 parts of barium carbonate, 7-9 parts of calcined talc, 3-5 parts of kaolin, 3-5 parts of calcined kaolin, and 1-3 parts of zinc oxide. The beneficial effects are that the high-strength porcelain glaze has good glaze face smoothness, good glaze slurry performance, wide firing range, wide application range, high hardness, good wear resistance, and prolonged service life.

Description

technical field [0001] The invention relates to the technical field of ceramic glazes, in particular to a high-strength porcelain glaze and a preparation method thereof. Background technique [0002] China is one of the first countries in the world to apply ceramics. The so-called ceramics include pottery and porcelain. The products made from ceramics mainly include daily-use pottery, art pottery, and architectural pottery. Ceramics are widely used in the fields of tableware, decoration, and science because of their hard texture, fineness, and high temperature resistance. [0003] The surface of ceramic products often needs to be coated with a layer of smooth glaze. The glaze can not only prevent water, but also prevent adhesion and have good cleaning performance. Since ceramic products are mostly made into daily necessities, the surface hardness of ceramic products is very high, and ceramics need to have good wear resistance, so the glaze on the surface of ceramics needs t...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C03C8/04C04B41/86
CPCC03C8/04C04B41/5022C04B41/86C04B41/4539
Inventor 蒋永刚邢衍亮
Owner 山东华浩陶瓷有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap