A kind of preparation method of early-strength polycarboxylate water reducer

A technology of polycarboxylic acid and water reducing agent, applied in the field of polycarboxylic acid water reducing agent, can solve the problems of easy oxidation, affecting product performance, limited quantity, etc.

Active Publication Date: 2022-01-07
云南森博混凝土外加剂有限公司
View PDF8 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The traditional method is prepared by copolymerization of a large monomer and several small monomers such as methacrylic acid in aqueous solution. This method has the advantages of simple operation and easy access to raw materials, but there are also some shortcomings: in the molecular structure The functional groups and their numbers that can provide electrostatic repulsion and steric hindrance effects are limited; small monomers such as methacrylic acid are prone to oxidation and violent polymerization during the polymerization reaction, which affects the performance of the product

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of preparation method of early-strength polycarboxylate water reducer

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0022] A kind of preparation method of early-strength polycarboxylate superplasticizer, under normal temperature condition, in 1.5L glass flask, add the TPEG of 400g (brand: Shanghai Taijie Chemical Co., Ltd., TJ- 188), after fully dissolving, add 2g of ammonium persulfate, heat up to 40°C, and then dropwise add acrylic acid, quaternary ammonium salt cationic monomer methacryloyloxyethyltrimethylammonium chloride, N-[ 4-(sulfonamide) phenyl]acrylamide, 2-acrylamido-2-methylpropenesulfonic acid, solution A mixed with deionized water and 2g vitamin C as a reducing agent, 8g thioglycolic acid as a chain transfer agent, deionized water The solution B mixed with ionic water is subjected to aqueous polymerization reaction, and the dropping time is 2 hours. After the dropping is completed, it is heated to 50°C for stirring reaction for 3 hours. After reaching room temperature, the neutralizing agent sodium hydroxide solution is added to adjust the pH to 7. Add water to adjust the sol...

Embodiment 2

[0024] Wherein the mass ratio of TPEG, acrylic acid, methacryloxyethyltrimethylammonium chloride, N-[4-(sulfonamide) phenyl]acrylamide, 2-acrylamide-2-methylpropenesulfonic acid It is 100:3:1:0.5:2, and others are the same as in Example 1.

Embodiment 3

[0026] Wherein the mass ratio of TPEG, acrylic acid, methacryloxyethyltrimethylammonium chloride, N-[4-(sulfonamide) phenyl]acrylamide, 2-acrylamide-2-methylpropenesulfonic acid It is 100:3:1:1:1, and others are the same as in Embodiment 1.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
degree of polymerizationaaaaaaaaaa
degree of polymerizationaaaaaaaaaa
Login to View More

Abstract

[ 4‑(sulfonamide)phenyl]acrylamide, 2‑acrylamido‑2‑methacrylic acid, chain transfer agent, initiator, neutralizer, water. The present invention uses N-[4-(sulfonamide) phenyl]acrylamide and 2-acrylamido-2-methacrylic acid simultaneously, and utilizes the synergistic effect of the two and quaternary ammonium salt cationic monomers to achieve the best Good early strength effect.

Description

technical field [0001] The invention relates to a polycarboxylate water reducer, in particular to a preparation method of an early-strength polycarboxylate water reducer. Background technique [0002] The early-strength polycarboxylate polymer water-reducer has the advantages of small dosage, high water-reducing rate, and can improve the early strength of concrete. It is a hot research topic at present. The traditional method is prepared by copolymerization of a large monomer and several small monomers such as methacrylic acid in aqueous solution. This method has the advantages of simple operation and easy access to raw materials, but there are also some shortcomings: in the molecular structure The functional groups and their numbers that can provide electrostatic repulsion and steric hindrance effects are limited; small monomers such as methacrylic acid are prone to oxidation and violent polymerization during the polymerization reaction, which affects the performance of the...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08F283/06C08F220/06C08F220/34C08F220/60C08F220/58C04B24/26C04B103/30
CPCC08F283/065C04B24/2694C04B2103/302C08F220/06C08F220/34
Inventor 阿光强徐顺涛苏玉玲马清浩