Method for extrusion forging composite near-net forming of titanium alloy thin-wall profile

A near-net forming and extrusion forging technology, which is applied in the direction of manufacturing tools, metal processing equipment, forging/pressing/hammer devices, etc., can solve the problems of low material utilization rate and high production cost, reduce forming temperature, improve plasticity, Solve the effect of low material utilization

Active Publication Date: 2019-10-18
TAIYUAN UNIVERSITY OF SCIENCE AND TECHNOLOGY
View PDF0 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] In view of the above technical problems, a method of extrusion forging composite near-net forming of titanium alloy thin-walled profiles is provided, which solves the problems of low material utilization rate and high production cost in the prior art

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method for extrusion forging composite near-net forming of titanium alloy thin-wall profile
  • Method for extrusion forging composite near-net forming of titanium alloy thin-wall profile
  • Method for extrusion forging composite near-net forming of titanium alloy thin-wall profile

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0022] The following will clearly and completely describe the technical solutions in the embodiments of the present invention with reference to the accompanying drawings in the embodiments of the present invention. Obviously, the described embodiments are only some, not all, embodiments of the present invention. Based on the embodiments of the present invention, all other embodiments obtained by persons of ordinary skill in the art without making creative efforts belong to the protection scope of the present invention.

[0023] S1. Billet hydrogenation: put the titanium alloy billet in a 100°C hydrogen furnace, and vacuum to 10°C -3 Pa, at 2~20℃min -1 Heat to the hydrogen temperature at a certain speed, put a certain amount of high-purity hydrogen into the hydrogen furnace, and keep the hydrogen partial pressure in the furnace for 1-5 hours after the partial pressure tends to be balanced. -1 The speed is cooled to room temperature to obtain a hydrogen-retained titanium alloy ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention belongs to the technical field of material forming, and particularly relates to a method for extrusion forging composite near-net forming of a titanium alloy thin-wall profile. The method comprises the following steps that S1, a titanium alloy blank is subjected to hydrogen treatment; S2, the titanium alloy blank subjected to hydrogen treatment is extruded and formed; S3, an extrusion profile is subjected to high-frequency forging and shaping into a forged profile; and S4, the forged profile is subjected to annealing and hydrogen removal treatment. The forming temperature of a titanium alloy is reduced through a thermohydrogen treatment process, plasticity of the titanium alloy is improved, large deformation is completed through extrusion forming, and thickness thinning and surface finishing are completed through forging and shaping. According to the method, near-net forming of the titanium alloy thin-wall profile can be achieved, and the problems that in the prior art, the material utilization rate is low and the production cost is high are solved. The method is used for extrusion forging composite near-net forming of the titanium alloy thin-wall profile.

Description

technical field [0001] The invention belongs to the technical field of material forming, in particular to a method for extrusion forging composite near-net forming of titanium alloy thin-walled profiles. Background technique [0002] Titanium alloy thin-walled profiles have very broad application prospects in the aerospace field, but the high processing and manufacturing costs seriously restrict their wide application, and near-net shape is an important way to reduce manufacturing costs. The advantage of extrusion processing is that the extrusion temperature can be at T p (titanium alloy phase transition temperature), at this time, the plasticity of the titanium alloy is good; the conditions for the blank to complete deformation under three-dimensional compressive stress are good, the forming efficiency is high, and most of the deformation can be completed; but because the wall thickness of the profile cannot meet the requirements, and The surface roughness is poor; extrusi...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): B21C23/02B21C23/32B21J5/06B21J13/00
CPCB21C23/001B21C23/002B21C23/02B21C23/32B21J5/002B21J5/06B21J13/00
Inventor 牛勇朱艳春马立峰
Owner TAIYUAN UNIVERSITY OF SCIENCE AND TECHNOLOGY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap