Zifs derived metal nitride/carbon composite material and its preparation method and use

A carbon composite material and composite material technology, applied in the field of ZIFs-derived metal nitride/carbon composite material and its preparation, can solve the problems of long preparation cycle, limited amplification and industrialization, poor electrical conductivity, etc. content, the effect of avoiding agglomeration

Active Publication Date: 2021-12-28
SICHUAN UNIV
View PDF9 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, limited by the structure and composition of the nitride itself, most of the nitrides prepared by conventional methods are bulk, with poor electrical conductivity. The synthesis conditions of high temperature and high pressure also pose great challenges to production equipment and energy consumption. And the preparation cycle is long, which limits the scale-up and industrialization

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Zifs derived metal nitride/carbon composite material and its preparation method and use
  • Zifs derived metal nitride/carbon composite material and its preparation method and use
  • Zifs derived metal nitride/carbon composite material and its preparation method and use

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0055] A kind of preparation method of ZIFs derived metal nitride / carbon composite material, such as figure 1 Shown is a schematic diagram of the synthesis of ZIFs-derived metal nitride / carbon composites prepared in Example 1 of the present invention, including: Synthetic NiCo 2 o 4 , then NiCo 2 o 4 Co in the high-temperature molten state is assembled with 2-methylimidazole to form ZIF-67, and then further nitrided, the specific steps are as follows:

[0056] (1) Weigh 248.84mg (1mM) of nickel acetate tetrahydrate, 498.12mg (2mM) of cobalt acetate tetrahydrate and 2.37g (30mM) of ammonium bicarbonate, respectively, and disperse them in a mixed solution of 15mL deionized water and 35mL ethylene glycol , add a stirrer, and use a magnetic stirrer to stir evenly for 30 minutes at room temperature;

[0057] (2) Put the uniformly mixed solution into a 50mL polytetrafluoroethylene reactor, set the oven parameters to 200°C, and conduct a hydrothermal reaction for 12 hours. After...

Embodiment 2

[0067] A kind of preparation method of ZIFs derived metal nitride / carbon composite material, such as Figure 4 As shown, it is a schematic diagram of the synthesis of ZIFs-derived metal nitride / carbon composite material (Ni-CoN / NC in the figure) prepared in Example 2 of the present invention, and the steps (1)-(3) to prepare NiCo 2 o 4 The same as the preparation process of Example 1, the difference is:

[0068] (4) Weigh 200mg NiCo 2 o 4 1. 5g polyvinylpyrrolidone (PVP), put into a beaker with 50mL methanol, add a stir bar, and stir at room temperature for 30min on a magnetic stirrer;

[0069] (5) Weigh 0.8924g of zinc nitrate hexahydrate and dissolve it in 10mL of methanol, weigh 4g of 2-methylimidazole and dissolve it in 30mL of methanol, and quickly pour the methanol solution of 2-methylimidazole into the methanol of zinc nitrate hexahydrate In the solution, stir at room temperature for 30 minutes and then let it stand for 3 hours, then pour it into the methanol soluti...

Embodiment 3

[0082] A method for preparing a ZIFs-derived metal nitride / carbon composite material is basically the same as in Example 2, except that in step (5), 1.7848 g of zinc nitrate hexahydrate and 8 g of 2-methylimidazole are used. The obtained ZIFs-derived metal nitride / carbon composite is designated as sample 3.

[0083] like Figure 15 Shown is the oxygen reduction performance comparison chart of the samples prepared in Example 1, Example 2 and Example 3. It can be seen from the figure that the onset potential of sample 2 is about 0.95V (vs.RHE), and the half-wave potential is 0.77 V(vs.RHE), the limiting current density is about 5.0mA cm -2 , showing optimal oxygen reduction activity, indicating that an appropriate proportion of nitrogen reacts with metals in this example to obtain metal nitrides, and adding an appropriate proportion of 2-methylimidazole forms nitrogen-doped carbon compounds with abundant pore structures. To a certain extent, the number of active sites is incre...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
Login to view more

Abstract

The invention discloses a metal nitride / carbon composite material derived from ZIFs and its preparation method and application. The method comprises: NiCo 2 o 4 Mix and grind nanospheres and 2-methylimidazole, and sinter at 700-900°C in a mixed gas of ammonia and inert gas to obtain composite materials; or, obtain zinc salt and 2-methylimidazole in methanol solution ZIFs precursor, adding the ZIFs precursor to NiCo 2 o 4 Stir in the methanol solution of nanospheres and dispersant, separate the solid, heat the solid to 700-900°C under the protection of inert gas, and then sinter in the mixed gas of ammonia and inert gas, and wait until the sintering is completed under the protection of inert gas The temperature is lowered to obtain a composite material. The method of the invention effectively avoids the agglomeration of metal particles and the structural collapse of ZIFs during the nitriding process, significantly accelerates the electron conduction rate and improves the reaction efficiency.

Description

technical field [0001] The invention relates to a metal nitride / carbon composite material and a preparation method thereof, in particular to a ZIFs (Zeolitic Imidazolate Frameworks, zeolitic imidazolate framework material) derived metal nitride / carbon composite material and a preparation method thereof. Background technique [0002] A fuel cell is a device that can directly convert the chemical energy of fuel into electrical energy. It has a relatively high energy conversion rate and is highly efficient and environmentally friendly during operation. It has been successfully applied to the energy supply of portable mobile devices and vehicles. The cathode oxygen reduction reaction (ORR) of the fuel cell has relatively high requirements on the catalyst. Whether the reaction process is a 4-electron or 2-electron process mainly depends on the inherent electrocatalytic properties of the catalyst. For a given electrocatalyst, a highly selective 4-electron process leads to better e...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): H01M4/86H01M4/88
CPCH01M4/8878H01M4/8647Y02E60/50
Inventor 王瑞林张洁陈金伟王刚罗艳
Owner SICHUAN UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap