Preparation method of spherical calcium alginate @ FeOOH desulfurizing agent
A technology of calcium alginate and desulfurizer, which is applied in chemical instruments and methods, alkali metal oxides/hydroxides, inorganic chemistry, etc., can solve the problems of difficult removal of FeOOH and no removal of anionic sulfur ions, and achieves easy storage, The effect of good adsorption performance and simple process
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0026] 16.20gFeCl 3 ·6H 2 O and 5.34g CH 3 (CH 2 ) 11 OSO 3 Dissolve Na in 60ml of deionized water respectively, stir and dissolve with a magnetic stirrer, and pour FeCl after fully dissolving 3 Add 1.20g nanometer ZnO to the solution and mix well, put CH 3 (CH 2 ) 11 OSO 3 Na solution was added dropwise at 3ml / min to the continuously stirring FeCl 3 , Nano-ZnO mixed solution was continuously stirred for 15min, and 1.2mol / L NaOH solution was added dropwise to the continuously stirred FeCl 3 , nano ZnO and CH 3 (CH 2 ) 11 OSO 3 In the Na mixed solution, after precipitation appears, stop the titration when the pH value of the mixed solution is 11.0, continue to stir for 60 minutes, transfer the solution with the precipitate to the reaction kettle, place the reaction kettle in an oven at 110°C, and heat After 12h, it was cooled to room temperature and taken out. Suction filter the precipitate in the reaction kettle, wash it, and dry it at 60°C for 18 hours to obtai...
Embodiment 2
[0029] 16.20gFeCl 3 ·6H 2 O and 5.34g CH 3 (CH 2 ) 11 OSO 3 Dissolve Na in 60ml of deionized water respectively, stir and dissolve with a magnetic stirrer, and pour FeCl after fully dissolving 3 Add 1.20g nanometer ZnO to the solution and mix well, put CH 3 (CH 2 ) 11 OSO 3 Na solution was added dropwise at 3ml / min to the continuously stirring FeCl 3 , Nano-ZnO mixed solution was continuously stirred for 15min, and 1.2mol / L NaOH solution was added dropwise to the continuously stirred FeCl 3 , nano ZnO and CH 3 (CH 2 ) 11 OSO 3 In the Na mixed solution, after precipitation appears, stop the titration when the pH value of the mixed solution is 11.0, continue to stir for 60 minutes, transfer the solution with the precipitate to the reaction kettle, place the reaction kettle in an oven at 110°C, and heat After 12h, it was cooled to room temperature and taken out. Suction filter the precipitate in the reaction kettle, wash it, and dry it at 60°C for 18 hours to obtai...
PUM
Property | Measurement | Unit |
---|---|---|
particle size (mesh) | aaaaa | aaaaa |
particle size (mesh) | aaaaa | aaaaa |
quality score | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction