Waterborne fire board marble paint
A slabstone and water-based technology, applied in the direction of coating, etc., can solve the problems of unfavorable energy saving and environmental protection, increase the load-bearing pressure of the main building body, poor color consistency, etc., and achieve the effect of convenient renovation and repair, lower load-bearing pressure, and easy batch color difference
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0013] The water-based fired marble paint of the present invention is made of the following materials in parts by weight: 400 parts of glass beads, 100 parts of ultra-thin resin composite sheet, 15 parts of inorganic gel, 120 parts of silicon acrylic emulsion, 0.5 parts of organic bentonite 200 parts of water, 0.5 parts of fungicide, and 0.5 parts of defoamer.
[0014] It is prepared by the following steps:
[0015] a. Preparation of the dispersion: Add silicon-acrylic emulsion, anti-sedimentation agent, bactericide, and defoamer to the water to disperse for 5 minutes, and adjust the pH value of the mixture to 8.5-9 to obtain the dispersion;
[0016] B, the preparation of base paint: add the inorganic gel in the dispersion liquid that a step makes, make base paint;
[0017] c. Preparation of water-based fire-fired marble paint: add glass beads and ultra-thin resin composite sheets to the basic paint prepared in step b, and stir evenly to obtain the finished product.
Embodiment 2
[0019] The water-based fire-fired marble paint of the present invention is made of the following materials in parts by weight: 500 parts of glass microspheres, 150 parts of ultra-thin resin composite sheets, 30 parts of inorganic gel, 200 parts of silicon-acrylic emulsion, gas phase dioxide 2 parts of silicon, 300 parts of water, 1 part of fungicide, 1 part of defoamer.
[0020] Its preparation method is with embodiment 1.
Embodiment 3
[0022] The water-based fired marble paint of the present invention is made of the following materials in parts by weight: 300 parts of glass particles, 120 parts of ultra-thin resin composite sheets, 20 parts of inorganic gel, 180 parts of silicon-acrylic emulsion, 1 polyolefin wax parts, 250 parts of water, 0.8 parts of LWJ-688 fungicide, and 0.8 parts of defoamer.
[0023] Its preparation method is with embodiment 1.
[0024] The method that the water-based fire-fired board marble paint spraying that application embodiment 1-3 makes makes imitation marble may further comprise the steps:
[0025] a. Base treatment: remove the attachments on the surface of the base, scrape the base with putty to make it smooth, maintain for 18 hours, and complete the base treatment; the amount of putty applied is 1kg / ㎡;
[0026] b. Primer painting: Spray or roll the primer from top to bottom on the treated base in step a, dry for 3 hours, and then complete the primer brushing. The coating amo...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com