Anti-oxidation aluminum profile and preparation process thereof

A technology of anti-oxidation and preparation technology, which is applied in the field of aluminum profiles, can solve the problems of limited use range and service life, poor oxidation resistance, etc., to prolong the service life and use range, improve oxidation resistance, super wear resistance and The effect of corrosion resistance

Inactive Publication Date: 2019-11-12
RUIAN JIANGNAN ALUMINUM CO LTD
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] Aluminum is usually processed into castings, forgings, foils, plates, strips, tubes, rods, profiles, etc., and then processed through cold bending, sawing, drilling, assembling, and coloring. The metal element is aluminum, plus some alloy elements to improve the performance of aluminum, but the existing aluminum profile has poor oxidation resistance, which limits its application range and service life. Therefore, we propose an anti-oxidation Aluminum profile

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0029] A kind of anti-alumina profile, the aluminum profile is composed of aluminum, silicon, iron, copper, manganese, magnesium, titanium, rhodium, niobium, tungsten, iridium, aluminum oxide, chromium oxide, chlorosulfonated polyethylene, dispersant and carboxylate It is composed of acid salt, and its weight parts are: aluminum 100-150 parts; silicon 0.5-0.7 parts; iron 0.1-0.2 parts; copper 0.06-0.1 parts; manganese 0.15-0.25 parts; magnesium 0.9-1.1 parts; titanium 0.1-0.3 parts; rhodium 0.2-0.7 parts; niobium 0.08-0.15 parts; tungsten 0.1-0.6 parts; iridium 0.3-0.7 parts; aluminum oxide 0.4-0.7 parts; chromium oxide 2-5 parts; chlorosulfonated polyethylene 1-3 parts; 5-8 parts of dispersant; 2-4 parts of carboxylate.

[0030] Rhodium, tungsten, iridium and aluminum oxide are added to the raw materials, which can effectively improve the oxidation resistance of the aluminum profile. Chromium oxide and chlorosulfonated polyethylene are added to the raw materials to make the alum...

Embodiment 2

[0050] A kind of anti-alumina profile, the aluminum profile is composed of aluminum, silicon, iron, copper, manganese, magnesium, titanium, rhodium, niobium, tungsten, iridium, aluminum oxide, chromium oxide, chlorosulfonated polyethylene, dispersant and carboxylate The composition of the acid salt, the weight parts of which are 120-130 parts of aluminum; 0.55-0.65 parts of silicon; 0.13-0.17 parts of iron; 0.07-0.09 parts of copper; 0.18-0.22 parts of manganese; 0.95-1.05 parts of magnesium; 0.15-0.25 parts; rhodium 0.3-0.5 parts; niobium 0.11-0.13 parts; tungsten 0.2-0.4 parts; iridium 0.4-0.6 parts; aluminum oxide 0.5-0.6 parts; chromium oxide 3-4 parts; chlorosulfonated polyethylene 1.8-2.2 parts; dispersant 6-7 parts; carboxylate 2.5-3.5 parts.

[0051] Rhodium, tungsten, iridium and aluminum oxide are added to the raw materials, which can effectively improve the oxidation resistance of the aluminum profile. Chromium oxide and chlorosulfonated polyethylene are added to the r...

Embodiment 3

[0071] A kind of anti-alumina profile, the aluminum profile is composed of aluminum, silicon, iron, copper, manganese, magnesium, titanium, rhodium, niobium, tungsten, iridium, aluminum oxide, chromium oxide, chlorosulfonated polyethylene, dispersant and carboxylate The composition of the acid salt, the components by weight are: 125 parts of aluminum; 0.6 parts of silicon; 0.15 parts of iron; 0.08 parts of copper; 0.2 parts of manganese; 0.1 parts of magnesium; 0.2 parts of titanium; 0.4 parts of rhodium; 0.12 parts of niobium; 0.3 parts; 0.5 parts of iridium; 0.55 parts of aluminum oxide; 3.5 parts of chromium oxide; 2 parts of chlorosulfonated polyethylene; 6.5 parts of dispersant; 3 parts of carboxylate.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses an anti-oxidation aluminum profile and a preparation process thereof. The aluminum profile is composed of aluminum, silicon, iron, copper, manganese, magnesium, titanium, rhodium, niobium, tungsten, iridium, aluminum oxide, chromium oxide, chlorosulfonated polyethylene, a dispersant and carboxylate; and the components include, by weight, 100-150 parts of the aluminum, 0.5-0.7 part of the silicon, 0.1-0.2 part of the iron, 0.06-0.1 part of the copper, 0.15-0.25 part of the manganese, 0.9-1.1 parts of the magnesium, 0.1-0.3 part of the titanium, 0.2-0.7 part of the rhodium, 0.08-0.15 part of the niobium, 0.1-0.6 part of the tungsten, 0.3-0.7 part of the iridium, 0.4-0.7 part of the aluminum oxide, 2-5 parts of the chromium oxide, 1-3 parts of the chlorosulfonated polyethylene, 5-8 parts of the dispersant and 2-4 parts of carboxylate. According to the anti-oxidation aluminum profile, the rhodium, the tungsten, the iridium and the aluminum oxide are added in the rawmaterials, the oxidation resistance of the aluminum profile can be effectively improved; and the chromium oxide and the chlorosulfonated polyethylene are added in the raw materials, so that the aluminum profile has the super strong oxidation resistance and also has superior wear resistance and corrosion resistance, the service life of the aluminum profile is prolonged, and the application range of the aluminum profile is prolonged.

Description

Technical field [0001] The invention relates to the technical field of aluminum profiles, in particular to an aluminum oxide-resistant profile and a preparation process thereof. Background technique [0002] Aluminum is usually processed into castings, forgings, foils, plates, strips, tubes, rods, profiles, etc., and then cold bending, sawing, drilling, assembling, coloring and other processes. Its main The metal element is aluminum, plus some alloying elements to improve the performance of aluminum, but the existing aluminum profile has poor oxidation resistance, which limits its use range and service life. For this reason, we propose an anti-oxidation Aluminum profile. Summary of the invention [0003] The purpose of the present invention is to provide an anti-alumina profile and a preparation process thereof to solve the above-mentioned problems in the background art. [0004] In order to achieve the above objective, the present invention provides the following technical soluti...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C22C21/00C22C32/00C22C1/10C22C1/02
CPCC22C21/00C22C32/0094C22C1/1036C22C1/1047
Inventor 张琪浩
Owner RUIAN JIANGNAN ALUMINUM CO LTD