A method for preparing patterned carbon nanotube film

Abstract

The invention discloses a method for preparing a patterned carbon nanotube film. The method comprises the following steps: cleaning a substrate; performing hydrophobic modification on the cleaned substrate to enable the contact angle of the substrate to be greater than 90 degrees; and carrying out hydrophilic treatment on the hydrophobically modified substrate, wherein the hydrophilic treatment area is matched with the area of the pattern. According to the method, patterning of the substrate can be rapidly realized, the formed pattern is clear, and the process is simple.

Description

technical field [0001] The invention relates to the field of carbon nanotubes, in particular to a method for preparing carbon nanotube films. Background technique [0002] Carbon nanotubes are a new type of carbon material discovered by Iijima of NEC Corporation in Japan in 1991, and can be divided into single-walled carbon nanotubes and multi-walled carbon nanotubes. The special structure of carbon nanotubes determines its special properties, such as high tensile strength and high thermal stability; with the change of the helical mode of carbon nanotubes, carbon nanotubes can exhibit metallic or semiconducting properties. Because carbon nanotubes have an ideal one-dimensional structure and excellent properties in the fields of mechanics, electricity, and heat, they have shown broad application prospects in interdisciplinary fields such as materials science, chemistry, and physics. They are widely used in scientific research and industrial applications. It has also received...

AI Technical Summary

Problems solved by technology

[0005] 1. There is a large area of ​​inhomogeneity;

[0006] 2. And the carbon tube film is multi-layered, which has a bad influence on the electrical performance (transistor). Because in the process of repeated extrusion, the carbon tubes will accumulate and form multiple layers, and this process cannot guarantee that each site really even

[0007] The defect of adopting Hongsik Park or Arnold et al.'s method to prepare carbon nanotubes is that the carbon nanotubes obtained by this method is not a continuous film, but a strip shape, which is not suitable for industrialized large-area processing technology; and Arnold et al. In the method, the trench size can be as small as 70nm, which has great limitations

[0008] In addition, the disadvantages of the above method also include: the solution cannot be used repeatedly, which is relatively wasteful, and the film layer is not uniform and the quality is not high