Aluminum foil for aluminum plastic film of lithium battery and manufacturing process of aluminum foil

A preparation process and technology of aluminum-plastic film, applied in the field of aluminum alloy materials, can solve the problems of insufficient drawing depth, intolerant of electrolyte, etc., and achieve the effects of high elongation, low oxygen and moisture permeability, and scientific process.

Active Publication Date: 2019-12-20
江苏大亚电子新材料科技有限公司
View PDF1 Cites 14 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] At present, the performance of aluminum foil products for aluminum-plastic film for lithium batteries in my country, only a few technical indicators of enterprises can re

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0025] The composition and mass percentage of aluminum foil for aluminum-plastic film for lithium batteries are: Si: 0.08%; Fe: 1.35%; Cu: 0.03%; Mn: 0.03%; Mg: 0.01%; Zn: 0.03%; Cr: 0.03%; Ti: 0.01%; the balance is Al and other unavoidable impurity elements, the blank is made of 8021 alloy, the tensile strength is 142MPa, and the elongation is 3.85%.

[0026] The preparation process of the aluminum foil for the aluminum-plastic film of the lithium battery comprises the following steps:

[0027] (1). Rough rolling: rough rolling is divided into two passes, the thickness of the billet used for rough rolling is 260 μm, and the thickness of the product after rough rolling is 120 μm;

[0028] (2). Intermediate rolling: the 120 μm aluminum plate obtained by rough rolling is subjected to one pass of intermediate rolling to obtain an aluminum plate with an exit thickness of 66 μm;

[0029] (3). Double-folding: double-folding aluminum foil with a thickness of 66 μm;

[0030] (4)....

Embodiment 2

[0039] The composition and mass percentage of aluminum foil for aluminum-plastic film for lithium batteries are: Si: 0.08%; Fe: 1.40%; Cu: 0.03%; Mn: 0.03%; Mg: 0.01%; Zn: 0.03%; Cr: 0.03%; Ti: 0.02%; the balance is Al and other unavoidable impurity elements, the blank is made of 8021 alloy, the tensile strength is 156MPa, and the elongation is 3.62%.

[0040] The preparation process of the aluminum foil for the aluminum-plastic film of the lithium battery comprises the following steps:

[0041] (1). Rough rolling: rough rolling is divided into two passes, the thickness of the billet used for rough rolling is 260 μm, and the thickness of the product after rough rolling is 120 μm;

[0042] (2). Intermediate rolling: the 120 μm aluminum plate obtained by rough rolling is subjected to one pass of intermediate rolling to obtain an aluminum plate with an exit thickness of 66 μm;

[0043] (3). Double-folding: double-folding aluminum foil with a thickness of 66 μm;

[0044] (4)....

Embodiment 3

[0053] The composition and mass percentage of aluminum foil for aluminum-plastic film for lithium batteries are: Si: 0.08%; Fe: 1.45%; Cu: 0.03%; Mn: 0.03%; Mg: 0.01%; Zn: 0.03%; Cr: 0.03%; Ti: 0.03%; the balance is Al and other unavoidable impurity elements. The blank is made of 8021 alloy with a tensile strength of 160MPa and an elongation of 3.55%.

[0054] The preparation process of the aluminum foil for the aluminum-plastic film of the lithium battery comprises the following steps:

[0055] (1). Rough rolling: rough rolling is divided into two passes, the thickness of the billet used for rough rolling is 260 μm, and the thickness of the product after rough rolling is 120 μm;

[0056] (2). Intermediate rolling: the 120 μm aluminum plate obtained by rough rolling is subjected to one pass of intermediate rolling to obtain an aluminum plate with an exit thickness of 66 μm;

[0057] (3). Double-folding: double-folding aluminum foil with a thickness of 66 μm;

[0058] (4)...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Tensile strengthaaaaaaaaaa
Thicknessaaaaaaaaaa
Thicknessaaaaaaaaaa
Login to view more

Abstract

The invention belongs to the technical field of aluminum alloy materials, and relates to an aluminum foil for an aluminum plastic film of a lithium battery and a manufacturing process of the aluminumfoil. The aluminum foil comprises the following components in percentage by mass: 0.08% of Si, 1.35-1.45% of Fe, 0.03% of Cu, 0.03% of Mn, 0.01% of Mg; 0.03% of Zn, 0.03% of Cr, 0.01-0.03% of Ti, andthe balance Al and other unavoidable impurity elements. The manufacturing process comprises the steps of rough rolling, middle rolling, coiling, finish rolling, slitting and annealing. According to the aluminum foil and the manufacturing method, the improved 8021 alloy is adopted, the alloy element proportion is reasonable, the 8021 alloy is adopted to be adjusted in the alloy components within the national standard range, and four passes of high-speed rolling with large reduction amount is adopted during aluminum foil rolling; and medium-high temperature annealing is adopted, so that the deepdrawing performance and the water brushing A-level effect of the product are guaranteed. The manufactured aluminum foil is high in elongation rate, good in corrosion resistance, low in oxygen permeability and moisture permeability and high in composite strength, and capable of meeting the use requirements of the aluminum plastic film of the lithium battery on the aluminum foil.

Description

technical field [0001] The invention belongs to the technical field of aluminum alloy materials, and relates to an aluminum foil for an aluminum-plastic film of a lithium battery and a preparation process thereof. Background technique [0002] With the rapid popularization and development of new energy vehicles, the requirements for safety, weight and capacity are getting higher and higher, so the requirements for improving the safety of lithium batteries are becoming more and more urgent. Soft-pack lithium batteries are widely used in consumer electronics, automobiles, military, medical, power tools and other industries due to their advantages of good safety performance, light weight, large capacity, low internal resistance, and flexible design. The essence of the soft-pack lithium battery is actually a liquid lithium-ion battery covered with a polymer shell, and its performance is so excellent, the most important thing is the aluminum-plastic film in the polymer shell, and...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C22F1/04C21D9/46C22C21/00B21B1/40B21B3/00
CPCC22F1/04C21D9/46C22C21/00B21B1/40B21B3/00B21B2003/001
Inventor 李俊夏俊杰颜建军赵岩毛国回张德林
Owner 江苏大亚电子新材料科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap