White bamboo charcoal fiber dyeing method

A dyeing method and bamboo charcoal polyester fiber technology, applied in the field of dyeing, can solve problems such as poor dyeing of white bamboo charcoal fibers, and achieve the effects of reducing influence, increasing dyeing rate, color fastness and softness to hand.

Inactive Publication Date: 2020-01-07
艾绳瑞
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The purpose of this invention is to provide a kind of dyeing method of white bamboo charcoal fiber, solve the problem of poor dyeing of white bamboo charcoal fiber existing in the prior art

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0041] Step 1. Desizing the white bamboo charcoal polyester fiber with a desizing enzyme concentration of 3 g / L, a steaming temperature of 112° C., and a steaming time of 50 minutes.

[0042] Step 2, drop the white bamboo charcoal polyester fiber after the desizing treatment in the dyeing solution that contains leveling agent and carry out dyeing process, wherein, the dyeing solution comprises that reactive dye concentration is 2%, sodium sulfate concentration is 3%, ammonium sulfate concentration is 0.4%, the dispersant concentration is 0.2%, and the pH value is adjusted to 5.5;

[0043] The dyeing conditions are: the bath ratio is 1:40, the initial dyeing temperature is adjusted to 60°C, then the temperature is raised to 120°C at a rate of 1°C / min, kept for 50 minutes, and then cooled to 60°C at a rate of 2°C / min.

[0044] Wherein, the leveling agent is obtained as follows:

[0045] (1) N, N-dimethylethanolamine, N-phenyl-2-naphthylamine, triethanolamine, triphenylmethane t...

Embodiment 2

[0053] Step 1. Desizing the white bamboo charcoal polyester fiber with a desizing enzyme concentration of 4 g / L, a steaming temperature of 111° C., and a steaming time of 45 minutes.

[0054] Step 2, drop the white bamboo charcoal polyester fiber after the desizing treatment in the dyeing solution that contains leveling agent and carry out dyeing process, wherein, the dyeing solution comprises that reactive dye concentration is 4%, sodium sulfate concentration is 4%, ammonium sulfate concentration is 0.3%, the dispersant concentration is 0.1%, and the pH value is adjusted to 5.0;

[0055] The dyeing conditions are: the bath ratio is 1:45, the initial dyeing temperature is adjusted to 40°C, then the temperature is raised to 130°C at a rate of 1°C / min, kept for 40 minutes, and then cooled to 70°C at a rate of 3°C / min.

[0056] Wherein, the leveling agent is obtained as follows:

[0057] (1) N, N-dimethylethanolamine, N-phenyl-2-naphthylamine, triethanolamine, triphenylmethane tri...

Embodiment 3

[0065] Step 1. Desizing the white bamboo charcoal polyester fiber with a desizing enzyme concentration of 5 g / L, a steaming temperature of 110° C., and a steaming time of 55 minutes.

[0066] Step 2, drop the white bamboo charcoal polyester fiber after the desizing treatment in the dyeing solution that contains leveling agent and carry out dyeing process, wherein, the dyeing solution includes that the concentration of reactive dye is 5%, the concentration of sodium sulfate is 2%, and the concentration of ammonium sulfate is 5%. 0.2%, the dispersant concentration is 0.1%, and the pH value is adjusted to 6.0;

[0067] The dyeing conditions are: the bath ratio is 1:50, the initial dyeing temperature is adjusted to 50°C, then the temperature is raised to 140°C at a rate of 2°C / min, kept for 60 minutes, and then cooled to 80°C at a rate of 3°C / min.

[0068] Wherein, the leveling agent is obtained as follows:

[0069] (1) N, N-dimethylethanolamine, N-phenyl-2-naphthylamine, trietha...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a white bamboo charcoal fiber dyeing method which includes the steps: (1) desizing white bamboo charcoal polyester fibers by a pad steaming one-bath process; (2) placing the desized white bamboo charcoal polyester fibers into dyeing solution containing leveling agents and dyeing the desized white bamboo charcoal polyester fibers; (3) placing the dyed white bamboo charcoal polyester fibers into alkali-minimization solution for alkali-minimization treatment; (4) placing the white bamboo charcoal polyester fibers after alkali-minimization treatment into reduction cleaningsolution for reduction cleaning treatment and drying. The white bamboo charcoal fiber dyeing method has the advantages that the influence of a dyeing and finishing process on healthcare functions of bamboo charcoals can be decreased, dye-uptake, color fastness and soft hand feel performances are improved, and various dyes can be adopted to obtain fibers and fabrics in different colors.

Description

technical field [0001] The invention belongs to the technical field of dyeing, in particular to a method for dyeing white bamboo charcoal fibers. Background technique [0002] Bamboo charcoal has a loose and porous structure, its molecules are fine and porous, its texture is hard, and it has strong adsorption capacity. It can purify the air, eliminate odors, absorb moisture, prevent mildew, inhibit bacteria and repel insects. It can dehumidify and absorb sweat when in contact with the human body, and promote blood circulation in the human body. And metabolism, relieve fatigue. [0003] In recent years, nano-scale bamboo charcoal powder (bamboo charcoal micropowder) has been selected, added to the slice melt or spinning solution through a special process, and then spun near the spinneret to form a new fiber variety. Due to its high strength, good elasticity, heat resistance, corrosion resistance and low manufacturing cost, polyester fiber is an important variety of synthetic...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): D06P3/52D06P1/38D06P1/52D06P1/00D06P5/10D06L1/00
CPCD06L1/00D06P1/0032D06P1/38D06P1/5285D06P3/528D06P5/10
Inventor 艾绳瑞
Owner 艾绳瑞
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap