A kind of automobile mat TPE composite material and preparation method thereof

A technology for composite materials and automobile floor mats, applied in the field of TPE composite materials for automobile floor mats and their preparation, can solve the problems of aging, peculiar smell, easy discoloration, etc., and achieve the effects of high slip resistance and increased service life

Active Publication Date: 2022-01-04
福建恩迈特新材料有限公司
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Traditional car floor mat materials have great limitations, such as: odor, easy to change color, aging, insufficient comfort, etc., and the VOC emitted by some inferior floor mat products also seriously threaten people's physical and mental health

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0027] The preparation method of the automobile foot pad TPE composite material comprises the following steps:

[0028] 1) Weigh the raw materials for making the XPE high-elasticity flame-retardant layer, mix and dry them, and use the extrusion foaming process to produce the XPE high-elasticity flame-retardant layer. The barrel temperature and flange temperature of the extrusion section are set to 90-120℃ , the mold temperature is set to 115-125 ° C, the extruder speed is 25-30 rpm; The foaming temperature is 200-240℃, and the speed of the steel mesh is 1.5-3m / min.

[0029] 2) Weigh the raw materials required for the production of the TPE mask layer / TPE bottom film layer, mix and dry evenly, and produce the TPE mask layer / TPE bottom film layer through a casting process extruder;

[0030] 3) The composite material is obtained by thermally bonding the TPE mask layer, XPE high-elasticity flame-retardant layer, glass fiber, XPE high-elasticity flame-retardant layer, and TPE botto...

Embodiment 1

[0038] A TPE composite material for automobile foot pads, which sequentially includes a TPE mask layer, an XPE high-elasticity flame-retardant layer, a glass fiber toughening layer, an XPE high-elasticity flame-retardant layer, and a TPE bottom film layer from top to bottom, and the preparation method is as follows:

[0039] 1) Weigh 100 parts of PE resin, 30 parts of EVA resin, 2 parts of color masterbatch, 20 parts of AC granulation material, 30 parts of DCP granulation material, 6 parts of flame retardant particles, and 0.8 part of antibacterial agent. The raw materials are mixed for 30min, placed in a 110℃ oven for dehumidification and drying for more than 4h, and then the XPE high-elasticity flame retardant layer is produced by the extrusion foaming process. , 110°C, 110°C, 108°C, 105°C, flange temperature is set to 95°C, mold temperature is set to 120°C for zones 1 to 6, extruder speed is 25r, master sheet thickness is 2.0mm, width is 65cm, the foaming adopts three-stage...

Embodiment 2

[0046] A TPE composite material for automobile foot pads, which sequentially includes a TPE mask layer, an XPE high-elasticity flame-retardant layer, a glass fiber toughening layer, an XPE high-elasticity flame-retardant layer, and a TPE bottom film layer from top to bottom, and the preparation method is as follows:

[0047]1) Weigh 100 parts of PE resin, 40 parts of EVA resin, 2 parts of color masterbatch, 30 parts of AC granulation material, 26 parts of DCP granulation material, 10 parts of flame retardant granules, and 1 part of antibacterial agent, and put them in a mixing mixer Mix the raw materials for 30 minutes, put them in an oven at 110°C for dehumidification and drying for more than 4 hours, and use the extrusion foaming process to produce the XPE high-elasticity flame-retardant layer; 108°C, 108°C, 105°C, 103°C, the flange temperature is set to 95°C, the mold temperature zone 1 to 6 is set to 118°C, the extruder speed is 22r, the thickness of the mother sheet is 2.0...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
widthaaaaaaaaaa
Login to View More

Abstract

The invention discloses a TPE composite material for automobile floor mats and a preparation method thereof. The TPE composite material for automobile floor mats sequentially includes a TPE mask layer, an XPE high-elasticity flame-retardant layer, a glass fiber toughening layer, an XPE high-strength Elastic flame retardant layer, TPE bottom film layer. The invention improves the structure so that the life of the product is greatly increased, and the glass fiber is used for toughening, and the double-layer high-elastic XPE material will allow users to have a more comfortable experience physically and mentally. The product has high anti-skid performance, good flame-retardant performance, It has the advantages of high elasticity, anti-aging, easy cleaning, waterproof and oil-proof, and no irritating smell.

Description

technical field [0001] The invention relates to the field of automobile foot pads, in particular to a TPE composite material for automobile foot pads and a preparation method thereof. Background technique [0002] With the rapid development of society, automobiles have become a necessity for our life and travel, and the accompanying automobile interiors have attracted more and more attention from people and enterprises. Traditional car mat materials have great limitations, such as: odor, easy discoloration, aging, insufficient comfort, etc., and the VOCs emitted by some inferior mat products also seriously threaten people's physical and mental health. SUMMARY OF THE INVENTION [0003] The purpose of the present invention is to provide a TPE composite material for automobile foot pads and a preparation method thereof in view of the deficiencies of the prior art. [0004] In order to achieve the above object, the present invention adopts the following technical solutions: ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B32B27/32B32B17/02B32B27/02B32B27/08B32B27/12B32B27/06B32B25/04B32B27/18B32B27/20B32B17/06C08L53/02C08L23/06C08L23/08C08K3/22C08K5/03C08J9/10B29C44/20B29C44/60B29C48/08B29C48/92B29C69/02B60N3/04
CPCB32B27/08B32B27/12B32B27/06B32B5/02B32B25/045B32B5/18B32B27/18B32B27/20B32B17/066C08L53/025C08J9/103C08J9/0061C08J9/0095C08J9/0066C08J9/0019B29C69/02B29C44/20B29C44/60B29C48/08B29C48/92B29C48/0021B60N3/048C08J2323/06C08J2423/06C08J2423/08B29C2948/92704B32B2605/003B32B2307/3065B32B2307/744B32B2307/552B32B2307/73B32B2307/7265B32B2307/558B32B2307/51B32B2262/101B32B2266/025C08L23/06
Inventor 邓中文张宏旺王振祥陈庆荣郑美乾王光艳
Owner 福建恩迈特新材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com