Carbon-containing nickel-iron alloy material

A nickel-iron alloy and alloy material technology, applied in the field of metallurgy, can solve the problems of high cost, cumbersome forging, deviation of strength and practical application, etc., and achieve the effect of low cost and easy forging

Inactive Publication Date: 2020-03-03
TAIZHOU HONGHUA METALLURGICAL MACHINERY
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The existing carbon-containing nickel-iron alloy forging is extremely cumbersome and needs to go through multiple processes, the cost is high, and the strength has a large deviation from the actual application

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0015] Embodiment one kind of carbon-containing nickel-iron alloy material is characterized in that: described carbon-containing nickel-iron alloy material is made up of following chemical composition by weight percentage: nickel 20-30%, iron 65-75%, carbon 3-5%, cobalt Cobalt 0.55-1.1%, silicon 0.08-0.2%, phosphorus 0.04-0.08%, sulfur 0.035-0.09%, chromium 0.1-0.55%, gallium 0.2-0.85%, strontium 0.18-0.35%, rhenium 0.1-0.25%.

Embodiment 2

[0016] Embodiment two: the carbon-containing nickel-iron alloy material is composed of the following chemical components by weight percentage: nickel 23%, iron 70%, carbon 4%, cobalt cobalt 0.8%, silicon 0.1%, phosphorus 0.07%, sulfur 0.025%, chromium 0.21%, gallium 0.4%, strontium 0.24%, rhenium 0.17%.

Embodiment 3

[0017] Embodiment three: the carbon-containing nickel-iron alloy material is composed of the following chemical components by weight percentage: nickel 29%, iron 61%, carbon 5%, cobalt cobalt 1%, silicon 0.17%, phosphorus 0.08%, sulfur 0.028%, chromium 0.32%, gallium 0.45%, strontium 0.3%, rhenium 0.18%.

[0018] A carbon-containing nickel-iron alloy and a preparation process thereof, comprising the following steps:

[0019] (1) take described raw material by weighing above-mentioned percentage by weight and mix at a high speed in a high-speed mixer to obtain alloy powder, and the high-speed mixing time is 30min-60min;

[0020] (2) Put the mixed raw materials into the impurity removal machine for refining, sieve for 5-10 minutes, and sieve out the high-density mixture,

[0021] (3) Put the mixed alloy powder into a vacuum melting furnace and melt for 2-5 hours at a temperature of 640-720°C;

[0022] (4) Increase the temperature in the vacuum melting furnace to 1120-1150° C.,...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a carbon-containing nickel-iron alloy material. The carbon-containing nickel-iron alloy material is prepared from the following chemical components including, by weight, 20-30%of nickel, 65-75% of iron, 3-5% of carbon, 0.55-1.1% of cobalt, 0.08-0.2% of silicon, 0.04-0.08% of phosphor,0.035-0.09% of sulfur, 0.1-0.55% of chromium, 0.2-0.85% of gallium, 0.18-0.35% of strontium and 0.1-0.25% of rhenium. The carbon-containing nickel-iron alloy material is extremely convenient to forge, needless for multiple working procedures, low in cost and extremely suitable for industrial mass production, and the strength of the carbon-containing nickel-iron alloy material is close to practical application.

Description

technical field [0001] The invention relates to the technical field of metallurgy, in particular to a carbon-containing nickel-iron alloy material. Background technique [0002] Nickel-iron alloys are all alloys. Chromium-nickel stainless steel is the main stainless steel variety that consumes nickel. Due to its excellent comprehensive performance, it is widely used, accounting for 60% to 75% of the total stainless steel output. The growth of stainless steel production will drive the growth of nickel metal consumption. As the impact of the financial crisis subsides, the price of nickel returns to more than 20,000 US dollars, and the advantages of nickel-iron alloys in reducing the cost of stainless steel smelting are gradually reflected, and nickel-iron alloys occupy an important position in stainless steel raw materials. The existing carbon-containing nickel-iron alloy forging is extremely cumbersome and needs to go through multiple processes, the cost is high, and the str...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C22C38/56C22C38/52C22C38/02C22C38/60C22C33/04
CPCC22C33/04C22C38/002C22C38/02C22C38/52C22C38/56C22C38/60
Inventor 刘华山
Owner TAIZHOU HONGHUA METALLURGICAL MACHINERY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products