A kind of halogen-free flame retardant resin and preparation method thereof

A flame retardant resin and flame retardant technology, applied in the field of halogen-free flame retardant polymers, can solve the problems of personnel injury, ash formation, secondary damage, etc., and achieve enhanced mechanical strength, improved flame retardant performance, and good mechanical strength Effect

Active Publication Date: 2022-03-18
CATHAY R&D CENT CO LTD +1
View PDF14 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, these flame-retardant polymers are only flame-retardant, and will eventually form ashes when exposed to open flames or high-temperature combustion. In the application of electronic appliances and wires, it will cause short circuit or personal injury, causing secondary damage.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of halogen-free flame retardant resin and preparation method thereof
  • A kind of halogen-free flame retardant resin and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0036] The halogen-free flame retardant resin of this embodiment includes the following components in parts by weight:

[0037] Polyamide PA56: 100 parts

[0038] Aluminum hypophosphite: 20 parts

[0039] Fiberglass: 33 parts

[0040] WAX-E: 0.3 parts

[0041] WAX-C: 0.6 parts

[0042] Antioxidant 1010: 0.4 parts

[0043] The preparation method of the halogen-free flame retardant resin of the present embodiment comprises the following steps:

[0044] 1) prepare materials according to the above ratio;

[0045] 2) Mix PA56, aluminum hypophosphite, WAX-E, WAX-C and antioxidant 1010 to obtain a premix;

[0046] 3) Use a twin-screw extruder to blend and melt the premix, and while blending and melting, use a feeder to forcibly feed the glass fibers into the premix, and after 5 minutes, extrude through a twin-screw The machine extruded strands, cooled the strands to below the melting point of PA56 with water as the cooling medium, and cut and granulated to obtain the halogen-f...

Embodiment 2

[0054] The halogen-free flame retardant resin of this embodiment includes the following components in parts by weight:

[0055] Polyamide PA56: 100 parts

[0056] Aluminum hypophosphite: 15 parts

[0057] Fiberglass: 33 parts

[0058] WAX-E: 0.3 parts

[0059] WAX-C: 0.6 parts

[0060] Antioxidant 1098: 0.2 parts

[0061] The preparation method of the halogen-free flame retardant resin of the present embodiment comprises the following steps:

[0062] 1) prepare materials according to the above ratio;

[0063] 2) Mix PA56, aluminum hypophosphite, WAX-E, WAX-C and antioxidant 1098 to obtain a premix;

[0064] 3) Use a twin-screw extruder to blend and melt the premix, and while blending and melting, use a feeder to forcibly feed the glass fibers into the premix, and after 5 minutes, extrude through a twin-screw The machine extruded strands, cooled the strands to below the melting point of PA56 with water as the cooling medium, and cut and granulated to obtain the halogen-f...

Embodiment 3

[0072] The halogen-free flame retardant resin of this embodiment includes the following components in parts by weight:

[0073] Polyamide PA56: 100 parts

[0074] Aluminum hypophosphite: 10 parts

[0075] Fiberglass: 33 parts

[0076] WAX-E: 0.3 parts

[0077] WAX-C: 0.6 parts

[0078] Antioxidant 1098: 0.2 parts

[0079] The preparation method of the halogen-free flame retardant resin of the present embodiment comprises the following steps:

[0080] 1) prepare materials according to the above ratio;

[0081] 2) Mix PA56, aluminum hypophosphite, WAX-E, WAX-C and antioxidant 1098 to obtain a premix;

[0082] 3) Use a twin-screw extruder to blend and melt the premix, and while blending and melting, use a feeder to forcibly feed the glass fibers into the premix, and after 5 minutes, extrude through a twin-screw The machine extruded strands, cooled the strands to below the melting point of PA56 with water as the cooling medium, and cut and granulated to obtain the halogen-f...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
melting pointaaaaaaaaaa
diameteraaaaaaaaaa
melting pointaaaaaaaaaa
Login to view more

Abstract

The invention provides a halogen-free flame-retardant resin and a preparation method thereof. The halogen-free flame-retardant resin comprises the following components in parts by weight: 100 parts of polyamide 56, 5-20 parts of organic halogen-free flame retardant, and 5-20 parts of glass fiber 40 parts, lubricant 0.05-0.5 part, antioxidant 0.05-0.5 part. The halogen-free flame-retardant resin of the present invention not only adopts renewable substances as main raw materials, is environmentally friendly, but also has good flame-retardant properties and mechanical properties.

Description

technical field [0001] The invention relates to a resin, in particular to a halogen-free flame-retardant resin and a preparation method thereof, and belongs to the technical field of halogen-free flame-retardant polymers. Background technique [0002] Due to their excellent mechanical and formability properties, polyamides are often used for sheathing and insulation of electrical cables, as well as for components in electrical and electronic equipment and many other applications. The flame-retardant modified polyamide has good flame retardancy, is a self-extinguishing material, and has good electrical insulation performance. However, these flame-retardant polymers are only flame-retardant, and will eventually form ashes when exposed to open flames or high-temperature combustion. In the application of electronic appliances and wires, they will cause short circuits or personal injury, causing secondary damage. Contents of the invention [0003] The invention provides a halo...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C08L77/06C08L91/06C08L77/00C08K7/14C08K3/32C08K5/134C08K5/20C08K5/526
CPCC08L77/06C08L2205/03C08L2201/22C08L2201/02C08L91/06C08L77/00C08K7/14C08K3/32C08K5/1345C08K5/20C08K5/526
Inventor 蒋龙高伯爵陈万钟周豪宏刘修才
Owner CATHAY R&D CENT CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap