Machine-made sand conditioning agent
A sand conditioner and mechanism technology, applied in the field of construction, can solve the problems of lack of functional change, such as performance change, and achieve the effect of solving bleeding and segregation, good adaptability and performance change, and good thickening effect.
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0029] Embodiment 1: A machine-made sand conditioner, including the following raw materials in parts by weight: 1 part of hardener, 5 parts of polyester carboxylic acid water reducer, 2 parts of binder, 2 parts of thickener, additives 2 parts, 2 parts of drought strength agent.
[0030] A method for preparing a machine-made sand conditioner, comprising the following steps:
[0031] (1) Production of hardening agent: after mixing one or more combinations of calcium aluminate compounds, colloidal silica, Portland cement, calcium sulfoaluminate and silica in proportion, in Stir evenly in a mixer, sequentially add hot water at 65°C with a water-to-material ratio of 0.57, and stir rapidly for 2 minutes to prepare a hardener for rapid-hardening concrete shipped in the form of ready-mixed concrete.
[0032] (2) Production of water reducing agent: Feed polyvinyl alcohol, monomethyl ether and methacrylic acid in proportion, add initiator dropwise at 65°C, keep warm for 0.5 hours after...
Embodiment 2
[0038] Embodiment 2: A machine-made sand conditioner, including the following raw materials in parts by weight: 5 parts of hardener, 10 parts of polyester carboxylic acid water reducer, 10 parts of binder, 10 parts of thickener, additives 10 parts, 10 parts of drought strength agent.
[0039] A method for preparing a machine-made sand conditioner, comprising the following steps:
[0040] (1) Production of hardening agent: after mixing one or more combinations of calcium aluminate compounds, colloidal silica, Portland cement, calcium sulfoaluminate and silica in proportion, in Stir evenly in a mixer, sequentially add hot water at 75°C with a water-to-material ratio of 1, and stir rapidly for 5 minutes to prepare a hardener for rapid-hardening concrete shipped in the form of ready-mixed concrete.
[0041] (2) Production of water reducing agent: Feed polyvinyl alcohol, monomethyl ether and methacrylic acid in proportion, add initiator dropwise at 90°C, keep warm for 3 hours afte...
Embodiment 3
[0047] Embodiment 3: A machine-made sand conditioner, including the following raw materials in parts by weight: 3 parts of hardener, 7 parts of polyester carboxylic acid water reducer, 5 parts of binder, 5 parts of thickener, additives 5 parts, 5 parts of drought strength agent.
[0048] A method for preparing a machine-made sand conditioner, comprising the following steps:
[0049] (1) Production of hardening agent: after mixing one or more combinations of calcium aluminate compounds, colloidal silica, Portland cement, calcium sulfoaluminate and silica in proportion, in Stir evenly in a mixer, sequentially add hot water at 70°C with a water-to-material ratio of 0.8, and stir rapidly for 3 minutes to prepare a hardener for rapid-hardening concrete shipped in the form of ready-mixed concrete.
[0050] (2) Production of water reducing agent: Feed polyvinyl alcohol, monomethyl ether and methacrylic acid in proportion, add initiator dropwise at 80°C, keep warm for 2 hours after a...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com