Wollastonite extracted mineral substance ink with good bonding effect and making method

A technology of bonding effect and minerals, applied in the direction of ink, household utensils, application, etc., can solve the problems of easy delamination and decolorization, inconvenient to store, and the ink sticking effect is not good enough, and achieves high sticking effect, strong sticking strength, good looking effect

Inactive Publication Date: 2020-04-07
华协书画院有限公司
View PDF2 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the pasting effect of the ink produced by the above two inventions is not good enough, and it is easy to delaminate and decolorize, which makes it inconvenient to preserve

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Wollastonite extracted mineral substance ink with good bonding effect and making method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0026] An ink with good bonding effect of minerals extracted from silica graphite and a preparation method thereof, comprising the following steps:

[0027] S1. Initial processing:

[0028] (1) Put 1 part of anionic active agent, 1 part of nonionic active agent, 2 parts of solid glue surfactant, 1 part of animal glue, and 2 parts of plant glue into special chemical equipment according to the batching procedure, Formulated;

[0029] (2) Pour the prepared solid powder into the prepared storage box;

[0030] (3) Turn on the prepared storage switch, run the equipment production line, turn on the gas switch, and adjust the radiation of the spray gun;

[0031] (4) Enter balanced antistatic treatment;

[0032] S2, reprocessing: pour the materials to be ground into the grinder according to the weight, and grind until the particle size is 5 microns;

[0033] S3. (1) First add part of the prescribed amount of water into the container, add the linking material under stirring, and hea...

Embodiment 2

[0038] An ink with good bonding effect of minerals extracted from silica graphite and a preparation method thereof, comprising the following steps:

[0039] S1. Initial processing:

[0040] (1) Put 4 parts of anionic active agent, 4 parts of nonionic active agent, 4 parts of solid glue surfactant, 1 part of animal glue, and 2 parts of vegetable glue, and put these materials into special chemical equipment according to the batching procedure, Formulated;

[0041] (2) Pour the prepared solid powder into the prepared storage box;

[0042] (3) Turn on the prepared storage switch, run the equipment production line, turn on the gas switch, and adjust the radiation of the spray gun;

[0043] (4) Enter balanced antistatic treatment;

[0044] S2, reprocessing: pour the materials to be ground into the grinder according to the weight part, and grind until the particle size is 6 microns;

[0045] S3. (1) First add part of the prescribed amount of water into the container, add the link...

Embodiment 3

[0050] An ink with good bonding effect of minerals extracted from silica graphite and a preparation method thereof, comprising the following steps:

[0051] S1. Initial processing:

[0052] (1) 8 parts of anionic active agent, 8 parts of nonionic active agent, 6 parts of solid glue surfactant, 2 parts of animal glue, 3 parts of vegetable glue, these several kinds of materials are put into special chemical equipment according to the batching procedure, Prepared as inorganic nano solid powder;

[0053] (2) Pour the prepared solid powder into the prepared storage box;

[0054] (3) Turn on the prepared storage switch, run the equipment production line, turn on the gas switch, and adjust the radiation of the spray gun;

[0055] (4) Enter balanced antistatic treatment;

[0056] S2, reprocessing: pour the materials to be ground into the grinder according to the weight part, and grind until the particle size is 6 microns;

[0057] S3. (1) First add part of the prescribed amount of...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

Relating to the technical field of preparation of ink ingots, the invention discloses a wollastonite extracted mineral substance ink with good bonding effect and a making method. The ink comprises thefollowing components by weight: 1-8 parts of an anionic active agent, 1-8 parts of a nonionic active agent, 2-6 parts of a solid gum surfactant, 1-2 parts of animal gum, 2-3 parts of vegetable gum, 10-15 parts of a thickener, 10-15 parts of a dispersant, 15-25 parts of deionized water, 30-32 parts of wollastonite, 5-8 parts of a stabilizer, 2-3 parts of an aromatic agent and the balance soft water. The ink produced by the method is non-toxic and harmless, has high pasting effect, strong permeability and high adhesion strength, not only is beautiful in appearance, but also is free of delamination and decoloration.

Description

technical field [0001] The invention relates to the technical field of ink ingot preparation, in particular to an ink with good binding effect of minerals extracted from silica graphite and a preparation method thereof. Background technique [0002] Generally speaking, ink refers to black liquid or solid. Chinese people seem to have a preference for black. Not to mention calligraphy, painting and literature for two thousand years, pottery as far back as four thousand years ago, except for adding ink to painted pottery. In addition, oriental all-black pottery is used. Yin and Shang inscriptions used ink to write symbols on oracle bones first and then engraved them. Zhou and Qin documents also used ink to write on bamboo slips, wooden slips, and silk. The users are different, some are natural ore graphite, and some may also be silicon graphite fired with charcoal. [0003] The traditional black ink formula is made of organic matter, the main materials: silica graphite, bone ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C09D11/16
CPCC09D11/16
Inventor 刘广文
Owner 华协书画院有限公司