A plastic film and anti-static technology, applied in the field of packaging, can solve the problems of unhygienic food or articles, film or bag vacuuming or oil fume, etc., achieve low surface activity, good packaging effect, and avoid the effect of dust adsorption

Active Publication Date: 2020-04-17
浙江保禄包装科技股份有限公司
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The current packaging of fresh-keeping bags or plastic wraps is basically shrink film packaging, which will fall apart after opening, a...

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Anti-static anti-fouling plastic film for packaging
  • Anti-static anti-fouling plastic film for packaging
  • Anti-static anti-fouling plastic film for packaging

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0036] An antistatic and antifouling plastic film for packaging, made of the following raw materials in parts by weight: 50 g of low-density polyethylene, 40 g of linear low-density polyethylene, 3 g of plasticizer, 0.5 g of antistatic and antifouling additives, heat-stabilizing Agent 0.5g, lubricant 2g,

[0037] Described plasticizer is polyethylene glycol;

[0038] Described thermal stabilizer is triphenyl phosphite;

[0039] Described lubricant is magnesium stearate;

[0040] The production process of the antistatic and antifouling plastic film for packaging specifically includes the following steps:

[0041] The first step, premixing: mix low-density polyethylene, linear low-density polyethylene, plasticizer, antistatic and antifouling additives, heat stabilizer, and lubricant;

[0042]The second step, blow molding: inject the premixed material into the plastic blown film machine, melt it at high temperature in four stages of 130°C, 140°C, 150°C, and 160°C, and extrude ...

Embodiment 2

[0046] An antistatic and antifouling plastic film used for packaging is made of the following raw materials in parts by weight: 80g of low-density polyethylene, 30g of linear low-density polyethylene, 2g of plasticizer, 1.2g of antistatic and antifouling additives, heat-stabilizing Agent 1g, lubricant 1.5g,

[0047] Described plasticizer is polyethylene glycol;

[0048] Described thermal stabilizer is triphenyl phosphite;

[0049] Described lubricant is zinc stearate;

[0050] The production process of the antistatic and antifouling plastic film for packaging specifically includes the following steps:

[0051] The first step, premixing: mix low-density polyethylene, linear low-density polyethylene, plasticizer, antistatic and antifouling additives, heat stabilizer, and lubricant;

[0052] The second step, blow molding: inject the premixed material into the plastic blown film machine, melt it at high temperature in four stages of 130°C, 140°C, 150°C, and 160°C, and extrude i...

Embodiment 3

[0055] An antistatic and antifouling plastic film for packaging, made of the following raw materials in parts by weight: 70g of low-density polyethylene, 35g of linear low-density polyethylene, 3g of plasticizer, 1g of antistatic and antifouling additive, heat stabilizer 1g, lubricant 2g,

[0056] Described plasticizer is polyethylene glycol;

[0057] Described thermal stabilizer is triphenyl phosphite;

[0058] Described lubricant is sodium stearate;

[0059] The production process of the antistatic and antifouling plastic film for packaging specifically includes the following steps:

[0060] The first step, premixing: mix low-density polyethylene, linear low-density polyethylene, plasticizer, antistatic and antifouling additives, heat stabilizer, and lubricant;

[0061] The second step, blow molding: inject the premixed material into the plastic blown film machine, melt it at high temperature in four stages of 130°C, 140°C, 150°C, and 160°C, and extrude it into a film aft...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses an anti-static anti-fouling plastic film for packaging. The anti-static anti-fouling plastic film is prepared from the following raw materials in parts by weight: 50-80 parts of low-density polyethylene, 30-45 parts of linear low-density polyethylene, 2-5 parts of a plasticizer, 0.5-1.2 parts of an anti-static anti-fouling additive, 0.5-1 part of a heat stabilizer and 1-2 parts of a lubricant. According to the invention, the low-density polyethylene and the linear low-density polyethylene are used as main raw materials; in order to solve the problem that an existing packaging plastic film is not resistant to static electricity, the anti-static anti-fouling additive is added into a formula for the plastic film, so dust adsorption is avoided due to the excellent anti-static property of the manufactured plastic film; and a packaging bag is endowed with anti-pollution capacity since the plastic film is doped with organic silicon, the packaging effect of the packaging bag is better played, and the packaging bag is practical and convenient to use.

Description

technical field [0001] The invention belongs to the technical field of packaging, and in particular relates to an antistatic and antifouling plastic film used for packaging. Background technique [0002] At present, there are three main types of common plastic film packaging bags on the market: polyethylene (PE), polyvinyl chloride (PVC) and polyvinylidene chloride (PVDC) packaging bags. And fresh-keeping bag or fresh-keeping film are often used in people's daily life, are used for protecting the freshness of food, have made things convenient for people's life. The packaging of the current fresh-keeping bags or plastic wraps is basically shrink-wrapped, which will fall apart after opening, and the film or bag itself has static electricity and will absorb dust or oily fumes, which is unhygienic for packaging food or articles. Contents of the invention [0003] The object of the present invention is to provide a kind of antistatic and antifouling plastic film for packaging,...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08L23/06C08L23/08C08L71/02C08L43/04C08F230/08C08F220/16C08J5/18
CPCC08J5/18C08F230/08C08F220/16C08J2323/06C08J2423/08C08J2471/02C08J2443/04
Inventor 田朝义李雯雯王娟王巧云
Owner 浙江保禄包装科技股份有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap