Aluminum foil reinforced TPO butyl rubber self-adhesive waterproof coiled material with backing and preparation method thereof

A self-adhesive waterproof membrane, butyl glue technology, applied in the direction of adhesive, film/sheet adhesive, etc., can solve the problem of poor adhesion between the substrate and the base layer, no adhesion, etc., to improve reliability The effect of improving the performance, convenience of construction, and construction limitations

Inactive Publication Date: 2020-04-17
SICHUAN SHUYANG WATERPROOF MATERIAL
View PDF8 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] However, the back of this type of material is a TPO waterproof membrane substrate, and the adhesion between the substrate and the base layer is extremely poor, or even has no adhesion.
For facade construction, only mechanical fixation and other methods can be adopted, which has certain limitations

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Aluminum foil reinforced TPO butyl rubber self-adhesive waterproof coiled material with backing and preparation method thereof
  • Aluminum foil reinforced TPO butyl rubber self-adhesive waterproof coiled material with backing and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0029] Step 1): Add polypropylene resin, propylene-based elastomer and TPO masterbatch according to 25%: 50%: 25% and add to cylinder A; take M-TPO resin and add to cylinder B; start extrusion, at temperature Extrude a sheet of specified thickness in mold A at 190°C-210°C, wherein TPO is on the back and M-TPO is on the front to obtain a TPO-M-TPO composite sheet; the temperature of the extruder A screw is : The feeding section is 170°C-180°C, the plasticizing section is 180°C-190°C, the metering section is 190°C-200°C; the temperature of the extruder B screw is: the feeding section is 170°C-180°C, and the plasticizing section is 190°C -200°C, metering section 200°C-210°C;

[0030] The TPO masterbatch is prepared by the following steps: 65 parts of magnesium hydroxide, 10 parts of PP resin K8003, 15 parts of POE 6102, 2 parts of light stabilizer 2020, 0.5 parts of antioxidant B60 and 6 parts of stearic acid 1801 After mixing evenly at high speed, add it to the parallel twin-sc...

Embodiment 2

[0037] Step 1): Add polypropylene resin, propylene-based elastomer and TPO masterbatch according to 35%: 35%: 30% and add to cylinder A; take M-TPO resin and add to cylinder B; start extrusion, at temperature Extrude a sheet of specified thickness in mold A at 190°C-210°C, wherein TPO is on the back and M-TPO is on the front to obtain a TPO-M-TPO composite sheet; the temperature of the extruder A screw is : The feeding section is 170°C-180°C, the plasticizing section is 180°C-190°C, the metering section is 190°C-200°C; the temperature of the extruder B screw is: the feeding section is 170°C-180°C, and the plasticizing section is 190°C -200°C, metering section 200°C-210°C;

[0038] The TPO masterbatch is prepared through the following steps: Take 75 parts of magnesium hydroxide, 5 parts of PP resin K8003, 30 parts of POE6102, 0.5 parts of light stabilizer 2020, 2 parts of antioxidant B60 and 2 parts of stearic acid 1801 high speed After mixing evenly, add it to the parallel tw...

Embodiment 3

[0045] Step 1): Add polypropylene resin, propylene-based elastomer and TPO masterbatch according to 30%: 45%: 25% and add to cylinder A; take M-TPO resin and add to cylinder B; start extrusion, at temperature Extrude a sheet of specified thickness in mold A at 190°C-210°C, wherein TPO is on the back and M-TPO is on the front to obtain a TPO-M-TPO composite sheet; the temperature of the extruder A screw is : The feeding section is 170°C-180°C, the plasticizing section is 180°C-190°C, the metering section is 190°C-200°C; the temperature of the extruder B screw is: the feeding section is 170°C-180°C, and the plasticizing section is 190°C -200°C, metering section 200°C-210°C;

[0046] The TPO masterbatch is prepared by the following steps: take 70 parts of magnesium hydroxide, 5 parts of PP resin K8003, 20 parts of POE6102, 1 part of light stabilizer 2020, 1 part of antioxidant B60 and 3 parts of stearic acid 1801 high speed After mixing evenly, add it to the parallel twin-screw ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
Login to view more

Abstract

The invention discloses an aluminum foil reinforced TPO butyl rubber self-adhesive waterproof coiled material with a backing. The invention relates to the field of self-adhesive polymer waterproof coiled materials, and aims to provides the aluminum foil reinforced TPO butyl rubber self-adhesive waterproof coiled material with the backing. According to the aluminum foil reinforced TPO butyl rubberself-adhesive waterproof coiled material with the backing, high-elasticity polyester fibers are compounded on a TPO base material, the fibers can be well bonded with mortar and other conventional bonding materials, the construction efficiency is greatly improved, and resource waste is reduced; the aluminum foil reinforced TPO butyl rubber self-adhesive waterproof coiled material with the backing sequentially comprises an isolation layer, a self-adhesive layer, a base material and the backing from top to bottom, and the backing is made of high-elasticity polyester fibers. The invention furtherprovides a preparation method of the aluminum foil reinforced TPO butyl rubber self-adhesive waterproof coiled material with the backing.

Description

technical field [0001] The invention relates to the field of self-adhesive polymer waterproof coiled material, in particular to an aluminum foil reinforced TPO butyl adhesive self-adhesive waterproof coiled material with a backing and a preparation method thereof. Background technique [0002] In recent years, the polymer waterproof membrane represented by TPO self-adhesive waterproof membrane has many advantages such as no pollution, long life, recyclability, reflection and energy saving, good flexibility, excellent welding performance, etc., and its momentum has developed rapidly. More and more people are willing to use TPO self-adhesive waterproof membrane. The polymer self-adhesive TPO waterproofing membrane not only has strong constructability, but also can be permanently bonded with the concrete structure layer, and there is no hidden danger of water channeling in the middle, forming a perfect waterproof system, which greatly improves the reliability of the waterproof ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09J7/29C09J7/24C09J7/25
CPCC09J2400/163C09J2423/00C09J2423/106C09J2467/006C09J7/243C09J7/255C09J7/29C09J2301/122
Inventor 骆晓彬王磊
Owner SICHUAN SHUYANG WATERPROOF MATERIAL
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap