Preparation method of building shock insulation rubber support and building shock insulation rubber support prepared by applying same

A vibration-isolating rubber and construction technology, which is applied to buildings, building components, building types, etc., can solve problems such as low vulcanization efficiency, and achieve the effects of reducing energy consumption, precise vulcanization time control, and shortening vulcanization time.

Active Publication Date: 2020-04-28
SINO RUBBER TECH CO LTD
View PDF5 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

For shock-isolating rubber bearings with a pure rubber layer thickness of more than 100mm, the vulcanization time is usually 400-500 minutes, and for large-scale thick products, the vulcanization time can reach 1200 minutes, that is to say, the shock-isola...

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method of building shock insulation rubber support and building shock insulation rubber support prepared by applying same
  • Preparation method of building shock insulation rubber support and building shock insulation rubber support prepared by applying same
  • Preparation method of building shock insulation rubber support and building shock insulation rubber support prepared by applying same

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0043] The invention provides a building shock-isolation rubber bearing, and the preparation method comprises the following steps:

[0044] a) Preparation of rubber compound: preparing and processing the rubber compound according to the formula;

[0045] b) Cut the steel plate according to the size requirements;

[0046] c) After the mixed rubber is rolled back and cut into pieces, the adhesive is bonded to the cut steel plate to form a semi-finished product to be molded;

[0047]d) Put the semi-finished product to be molded into the heating device for preheating. After the preheating process is raised to 75°C-85°C at a speed of 5°C / min, the holding time is longer than 4h; the preset temperature upper limit is 85°C, according to the rubber The shear elastic modulus G value of the rubber is different, and the preheating time is different, but the preheating time is not less than 4 hours;

[0048] After the preheating time is reached, measure the temperature of the center of t...

Embodiment 1

[0059] A building shock-isolation rubber bearing, the preparation method comprising the steps of:

[0060] a) Preparation of rubber compound: prepare and process the rubber compound according to the following formula:

[0061] b) 100 parts of natural rubber, 5 parts of zinc oxide, 2 parts of stearic acid, 2 parts of paraffin, 3 parts of anti-aging agent 4010NA, 1.5 parts of anti-aging agent, 1.5 parts of anti-aging agent RD, 1.5 parts of accelerator CZ, 1.5 parts of sulfur, 30 parts of N774 carbon black, 20 parts of aromatic oil; after masticating and kneading, a mixed rubber is formed; the masticating and kneading process is carried out according to the conventional method, and will not be repeated here.

[0062] c) Cut the steel plate according to the size requirements; the size requirements should be in accordance with the LNR-D1000 building isolation rubber bearing;

[0063] d) After the mixed rubber is rolled back and cut into pieces, the adhesive is bonded to the cut st...

Embodiment 2

[0070] A building shock-isolation rubber bearing, the preparation method comprising the steps of:

[0071] Preparation of rubber compound: prepare and process the rubber compound according to the following formula: the formula of the rubber compound described in step a) is as follows:

[0072] a) 100 parts of natural rubber, 5 parts of zinc oxide, 2 parts of stearic acid, 1.5 parts of paraffin, 1.5 parts of flow exhaust agent CH236, 2 parts of anti-aging agent 4010NA, 1.5 parts of anti-aging agent RD, 1 part of anti-aging agent D, accelerator 1.5 parts of CZ, 0.8 parts of vulcanizing agent DTDM, 0.3 parts of vulcanizing agent PDM, 1.5 parts of sulfur, 30 parts of N774 carbon black, 15 parts of aromatic oil, 6.7 parts of liquid small molecule materials; after mastication and mixing, a compound rubber is formed; Wherein the masticating and mixing processes are carried out according to conventional methods, and details are not repeated here;

[0073] b) Cut the steel plate accor...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention provides a preparation method of a building shock insulation rubber support and the building shock insulation rubber support product prepared by applying the same. The preparation methodcomprises the following steps that firstly, a rubber compound material is prepared, a steel plate is cut, and laminating and forming are carried out on the rubber compound material and the cut steelplate subjected to shot blasting to obtain a semi-finished product to be subjected to mold filling; the semi-finished product to be subjected to mold filling is placed into a heating device for preheating, and after the temperature rises to 75-85 DEG C at the speed of 5 DEG C/min in the preheating process, the temperature is kept for more than 4 hours; mold filling and vulcanizing are carried outon the preheated semi-finished product; and demolding and trimming are carried out to obtain the building shock insulation rubber support. By adding the preheating step, adjusting the formula and improving the process, the vulcanization uniformity and the vulcanization efficiency of the building shock insulation rubber support are effectively improved.

Description

technical field [0001] The invention relates to the technical field of preparation of building shock-isolation rubber bearings, in particular to a method for preparing building shock-isolation rubber bearings and products thereof. Background technique [0002] The traditional anti-seismic technology is to firmly connect the superstructure and the foundation of the building. In order to build a stronger house, thicker steel bars and more concrete are poured, but the anti-seismic effect is not ideal. The seismic isolation bearing is to add a seismic isolation layer between the upper structure and the foundation, and install a rubber seismic isolation bearing to play a role of soft connection with the ground. Through this technology, about 80% of the energy of the earthquake can be offset. The rubber shock-isolation bearing is a kind of shock-isolation bearing, which is composed of multiple layers of steel plates and rubber alternately laminated. It can not only reduce the hor...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): B29C43/18E04B1/98E04H9/02C08L7/00C08L91/00C08L91/06C08K13/02C08K3/22C08K5/09C08K5/18C08K5/3437C08K3/04C08K3/06
CPCB29C43/003B29C43/18C08K2003/2296C08L7/00C08L2205/03E04B1/98E04H9/022C08L91/00C08L91/06C08K13/02C08K3/22C08K5/09C08K5/18C08K5/3437C08K3/04C08K3/06
Inventor 刘新良赵贵英谷立宁张红永常广忠苏伟
Owner SINO RUBBER TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap