A kind of high abrasion resistance moisture-proof coating composition and its preparation method and application

A technology with high wear resistance and composition, applied in anti-corrosion coatings, coatings, polyurea/polyurethane coatings, etc., can solve the problems of moisture-proof and moisture-proof limitation of moisture-proof agents, inability to spray electronic components, etc. The use process is safe and environmentally friendly, and the effect of good moisture-proof protection effect

Active Publication Date: 2022-03-01
北京信为兢创科技有限公司
View PDF18 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, in the preparation process of the above-mentioned fluorine-containing moisture-proof agents, water is used as a solvent additive, which cannot be directly used for spraying electronic components, so that the application of the prepared moisture-proof agents in the waterproof and moisture-proof aspects of electronic products is limited.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of high abrasion resistance moisture-proof coating composition and its preparation method and application
  • A kind of high abrasion resistance moisture-proof coating composition and its preparation method and application
  • A kind of high abrasion resistance moisture-proof coating composition and its preparation method and application

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0044] Add 100g TEMAc-6 (0.23mol), 0.3g HEMA (0.0023mol), 0.5g AIBN, 100g 7300 into a 500ml three-necked flask, N 2 After the replacement, react at 80°C for 6 hours to obtain a fluorine-containing polymer stock solution. The weight-average molecular weight of the fluorine-containing polymer was 31,000.

[0045] Add 0.22g of curing agent TDI and 9930g of 7200 to the fluoropolymer stock solution, and stir evenly in a mixing tank to obtain a coating composition.

[0046] The coating composition was dripped onto the substrate by means of drop coating, and after curing at room temperature for 72 hours, a coating was obtained. The coating properties are listed in Table 1. The coating formed by the coating composition has good hydrophobicity, hardness and wear resistance. The carbon steel corrosion test shows that the moisture-proof and water-proof effect of the coating composition coating on the carbon steel sheet has a good retarding effect on the corrosion of the carbon steel s...

Embodiment 2

[0051] Add 100g TEMAc-6 (0.23mol), 15g HEMA (0.12mol), 10g AIBN, 1000g 7200 into a 1000ml three-necked flask, N 2 After replacement, react at 70°C for 24 hours to obtain a fluoropolymer stock solution. The weight average molecular weight of the fluorine-containing polymer is 5,000.

[0052] Add 25.7g of curing agent IPDI and 150g of 7200 to the fluorine-containing polymer stock solution, and stir evenly in a mixing tank to obtain a coating composition.

[0053] The coating composition is sprayed onto the substrate by spraying, and after drying, it is cured at 200° C. for 0.01 h to obtain a coating. The coating properties are listed in Table 1. The FT-IR spectrum of the coating is as follows figure 2 As shown, it can be seen that the coating is a fluorine-containing copolymer.

Embodiment 3

[0055] Add 100g TEMAc-6 (0.24mol), 6.9g HPMA (0.05mol), 2g BPO, 200g 7100 into a 500ml three-necked flask, N 2 After replacement, react at 60°C for 24 hours to obtain a fluoropolymer stock solution. The weight-average molecular weight of the fluorine-containing polymer is 55,000.

[0056] Add 10.6g of curing agent IPDI, 2186g of 7100 and 243g of HFE-449 to the stock solution of fluoropolymer, and stir evenly in a mixing tank to obtain a coating composition.

[0057] The coating composition is sprayed onto the substrate by spraying, and after drying, it is cured at 120° C. for 2 hours to obtain a coating. The coating properties are listed in Table 1. The FT-IR spectrum of the coating is as follows image 3 As shown, it can be seen that the coating is a fluorine-containing copolymer.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
Login to View More

Abstract

The present invention relates to a high wear resistance moisture-proof coating composition and its preparation method and application, specifically a high wear resistance fluorine-containing polymer composite coating composition used between electronic devices and their connectors High wear resistance waterproof, moisture-proof, corrosion-resistant purposes. The high wear resistance and moisture-proof coating composition is characterized in that the composition contains the following components by weight: 1-9 parts of fluoropolymer, 0.02-2 parts of curing agent, 89-99 parts of fluorine-based Solvent, the fluorine-containing polymer is made of the following raw materials: fluorine-containing monomers, hydroxyester monomers, initiators, fluorine-based solvents, the fluorine-containing monomers, hydroxyester monomers, initiators, fluorine-based solvents The weight ratio is: 100:(3-15):(0.5-10):(100-1000). The coating composition can be directly coated on electronic components, and can form a coating with good wear resistance after being cured, and the composite coating can have a good moisture-proof protection effect on the substrate; the coating composition adopts Safe, non-toxic, non-flammable fluorine-based solvents, safe and environmentally friendly during preparation and use, and can be used directly without additional protection.

Description

technical field [0001] The present invention relates to a high wear resistance moisture-proof coating composition and its preparation method and application, specifically a high wear resistance fluorine-containing polymer composite coating composition used between electronic devices and their connectors High wear resistance waterproof, moisture-proof, corrosion-resistant purposes. Background technique [0002] With the continuous development of electronic technology, the use of portable electronic products is becoming more and more popular, and its use places and environments are becoming more and more complex and harsh. This puts forward higher requirements for the waterproof, moisture-proof and corrosion resistance of portable electronic products. Using a fluorine-based solvent solution of a fluorine-containing alkyl acrylate polymer as a coating agent can form a waterproof and moisture-proof coating with a thickness of less than 1 μm on electronic devices, and thus has at...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C09D175/04C09D5/08C09D5/00C09D7/20C08G18/62
CPCC09D175/04C09D5/08C09D5/00C09D7/20C08G18/6279
Inventor 米欣肖强陈琦李猛
Owner 北京信为兢创科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com