Water bag film and preparation method thereof

A water bag and cold-resistant agent technology, which is applied in the field of processing and preparation of hot water bags, can solve problems such as insufficient strength, fastness, and poor functionality, and achieve good strength, good fastness, and functionality, and improve structural strength and tensile strength. The effect of stretchability

Inactive Publication Date: 2020-06-05
浙江铭龙新材料科技有限公司
View PDF2 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At present, the water bag film used to make hot water bags in the market still has the problems of insufficient strength, poor fastness and poor functionality.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0023] The water bag film in the present embodiment comprises the following components by weight: 75 parts of polyvinyl chloride resin, 36.5 parts of dioctyl terephthalate, 2.3 parts of epoxy soybean oil, 3 parts of barium zinc liquid stabilizer , 4.7 parts of cold-resistant agent, 0.025 parts of colorant; cold-resistant agent is adipate diester.

[0024] The preparation method of the water bag film in the present embodiment comprises the steps:

[0025] S1: Accurately weigh the raw materials according to the proportion of the formula, including polyvinyl chloride resin, dioctyl terephthalate, epoxy soybean oil, barium zinc liquid stabilizer, cold resistance agent;

[0026] S2: Put polyvinyl chloride resin and dioctyl terephthalate into a kneader for high-temperature kneading to obtain a base material, wherein the kneading temperature is 100°C to 110°C;

[0027] S3: Put the obtained base material, epoxidized soybean oil, barium-zinc liquid stabilizer, cold resistance agent, a...

Embodiment 2

[0035] The difference between this embodiment and Embodiment 1 is that the water bag film in this embodiment includes the following components in parts by weight: 70 parts of polyvinyl chloride resin, 35 parts of dioctyl terephthalate, epoxy resin 2 parts of soybean oil, 2 parts of barium-zinc liquid stabilizer, 4.5 parts of cold-resistant agent, 0.01 part of colorant; the cold-resistant agent is adipate diester.

Embodiment 3

[0037] The difference between this embodiment and Embodiment 1 is that the water bag film in this embodiment includes the following components in parts by weight: 80 parts of polyvinyl chloride resin, 38 parts of dioctyl terephthalate, epoxy resin 2.6 parts of soybean oil, 4 parts of barium-zinc liquid stabilizer, 5 parts of cold-resistant agent, 0.04 part of colorant; the cold-resistant agent is adipate diester.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to a water bag film and a preparation method thereof. The problems that in the prior art, a water bag film is insufficient in strength and poor in fastness and functionality aresolved. The water bag film comprises the following components in parts by weight: 70-80 parts of polyvinyl chloride resin, 35-38 parts of dioctyl terephthalate, 2-2.6 parts of epoxy soybean oil, 2-4 parts of a barium-zinc liquid stabilizer and 4.5-5 parts of a cold-resistant agent. The water bag film is good in strength, and fastness and functionality of the water bag film are better than those ofan existing water bag film on the market.

Description

technical field [0001] The invention relates to a water bag film and a preparation method thereof, which are mainly used for processing and preparing hot water bags. Background technique [0002] The hot water bag is usually square, with a hot water inlet and outlet at one end, sealed with a plug, mostly a spiral plug, and its use is to pour hot water into it to keep warm. Now this traditional hot water bag is gradually being used as a storage type. Replaced by the electric hot water bag, the water storage type electric hot water bag is filled with liquid, has a heater inside, and plugs in the power to heat the liquid in the bag, so as to achieve the purpose of heating. The water bag film that is used to make hot water bag also has the problems of insufficient strength, fastness and poor functionality in the market now. Contents of the invention [0003] The purpose of the present invention is to overcome the above-mentioned deficiencies in the prior art, and provide a wa...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L27/06C08L91/00C08K5/12C08K5/11C08J5/18
CPCC08J5/18C08J2327/06C08J2491/00C08K5/11C08K5/12
Inventor 朱建华
Owner 浙江铭龙新材料科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap