Hot isostatic pressing shape control method for titanium alloy thin-wall part

A hot isostatic pressing, titanium alloy technology, applied in metal processing equipment, transportation and packaging, etc., can solve the problems of thin-walled parts deformation, reduce the machining allowance of titanium alloy thin-walled parts, etc., to prevent high temperature and high pressure deformation, improve Dimensional change and crack phenomenon, the effect of improving stability

Inactive Publication Date: 2020-06-12
CHINA UNIV OF GEOSCIENCES (BEIJING)
View PDF4 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The object of the present invention is to provide a method for controlling the shape of titanium alloy thin-walled parts by hot isostatic pressing to solve the problems raised in the above-mentioned background technology: first, to overcome the deformation of thin-walled parts caus

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Hot isostatic pressing shape control method for titanium alloy thin-wall part
  • Hot isostatic pressing shape control method for titanium alloy thin-wall part
  • Hot isostatic pressing shape control method for titanium alloy thin-wall part

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0039] The following will clearly and completely describe the technical solutions in the embodiments of the present invention with reference to the accompanying drawings in the embodiments of the present invention. Obviously, the described embodiments are only some, not all, embodiments of the present invention. Based on the embodiments of the present invention, all other embodiments obtained by persons of ordinary skill in the art without making creative efforts belong to the protection scope of the present invention.

[0040] Please refer to Fig. 1, the present invention provides a kind of technical scheme:

[0041]A method for controlling the shape of titanium alloy thin-walled parts by hot isostatic pressure, which is characterized in that: designing and processing a reasonable sheath according to the size and shape of the outer surface of the titanium alloy thin-walled part, the sheath includes vacuum holes The cover, the top plate with the powder filling port, the cylind...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a hot isostatic pressing shape control method for a titanium alloy thin-wall part in the technical field of aerospace manufacturing. A cover plate with a vacuum hole, a top plate with a powder filling opening, a cylindrical wall, a rigid base plate for fixing a die, a bottom plate and titanium alloy powder. The method comprises the steps of die design and preparation, jacket preparation, hot isostatic pressing pretreatment, hot isostatic pressing process control, post treatment and the like, and provides a die shape and size design method aiming at the deformation problem of the titanium alloy thin-wall part in the whole forming process. According to the hot isostatic pressing shape control method constrained by the die and a jacket, the forming efficiency of the part and the utilization rate of raw materials can be improved, the compactness of the formed titanium alloy thin-wall part is high, the structure is uniform, the performance is excellent, an inner cavity of the formed titanium alloy thin-wall part can be near to the final shape, and the outer wall has enough machining allowance to meet the final size requirement.

Description

technical field [0001] The invention relates to the technical field of aerospace manufacturing, in particular to a hot isostatic pressure shape control method for titanium alloy thin-walled parts. Background technique [0002] Titanium alloy thin-walled parts have the characteristics of light weight, high strength and high temperature corrosion resistance, and have been widely used in the aerospace field. These titanium alloy thin-walled parts usually require high dimensional accuracy and surface quality. However, traditional titanium alloy thin-walled parts forming processes such as casting, forging, welding and machining have disadvantages such as unstable processing quality, long production cycle, and high manufacturing cost. Moreover, due to the poor rigidity of titanium alloy thin-walled parts, the processing process is extremely easy Problems such as deformation, instability and vibration occur. [0003] Hot isostatic pressing technology is an advanced manufacturing ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): B22F3/15B22F9/08B22F1/00B22F5/00
CPCB22F3/15B22F9/082B22F5/00B22F1/05B22F1/065
Inventor 黄西娜岳文丁首斌佘丁顺田斌康嘉杰付志强
Owner CHINA UNIV OF GEOSCIENCES (BEIJING)
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap