Disposable nitrile glove with function of preventing sweat accumulation and preparation method thereof
A kind of nitrile gloves, disposable technology, applied in the direction of gloves, protective clothing, household utensils, etc., can solve the problems of airtightness, unfavorable hand protection, and affect the accuracy of operation
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Embodiment 1
[0074] The hand model used in this embodiment is a hand model capable of producing sweat and its water vapor discharge structure 2-1-2. Its basic structure is as follows: image 3 As shown, the surface of the hand mold has strip-shaped depressions 1-3, the cross-section of the strip-shaped depressions 1-3 is a semi-ellipse, the long diameter of the semi-ellipse is 0.58 mm, the short diameter is 0.46 mm, and the short diameter is 0.46 mm. perpendicular to the film surface. The distribution of the strip-shaped depressions 1-3 on the surface of the hand mold, such as Figure 4 shown, Figure 4 The right picture of is a front view of the hand mold capable of producing sweat and its water vapor discharge structure 2-1-2, and the left picture is a rear view. Each finger is provided with 6 strip-shaped depressions 1-3, a total of 30 strip-shaped depressions 1-3 are set on the surface of the hand mold, and each strip-shaped depression 1-3 extends to the wrist of the hand mold. The ...
Embodiment 2
[0092] The disposable nitrile gloves of the present invention are prepared by a preparation method comprising the following steps:
[0093] Step 1), step 3) to step 5), step 7) to step 9) are identical with embodiment 1;
[0094] Step 2) Prepare the nitrile latex for dipping to generate the middle-layer adhesive film 2-2: under the protection of the air that completely removes oxygen, weigh 100 parts of nitrile rubber latex, 1.1 parts of potassium hydroxide, Tween 80 according to parts by weight. (surfactant) 0.013 part, n-heptanol (defoamer) 0.091 part, zinc oxide 0.9 part, sulfur 0.59 part, titanium dioxide 1.8 part, zinc diethyldithiocarbamate (vulcanization accelerator) 0.11 part, nano The iron powder is 0.008 parts by weight, the nano iron powder is prepared by chemical method, the shape is spherical, the average diameter is 30-50 nanometers, and the water is 230 parts. After mixing, the mixture was stirred counterclockwise for 61 minutes, the stirring speed was 96 rpm, ...
Embodiment 3
[0099] The disposable nitrile gloves of the present invention are prepared by a preparation method comprising the following steps:
[0100] Step 2) to step 9) are identical with embodiment 1;
[0101] Step 1) prepare the nitrile latex for dipping to generate the inner layer adhesive film 2-1: respectively weigh 100 parts of nitrile rubber latex, 0.8 part of potassium hydroxide, 0.008 part of Tween 80 (surfactant) according to parts by weight, 0.083 part of heptanol (defoamer), 1.0 part of zinc oxide, 0.38 part of sulfur, 2.9 parts of titanium dioxide, 0.07 part of zinc diethyldithiocarbamate (vulcanization accelerator), 0.008 part by weight of polylysine, polylysine The amino acid is composed of 10-13 lysine residues, 0.003 parts by weight of dihydroxyphenylalanine, and 260 parts by weight of water. After mixing, stir clockwise for 46 minutes at a stirring speed of 116 rpm, and grind 3 times with a paint grinder. The pH of the obtained latex was 7.1 to 7.6.
[0102] The pre...
PUM
| Property | Measurement | Unit |
|---|---|---|
| diameter | aaaaa | aaaaa |
| surface tension | aaaaa | aaaaa |
| density | aaaaa | aaaaa |
Abstract
Description
Claims