A production method and leather technology, applied in leather surface treatment, special leather manufacturing, small raw hide/large raw hide/leather/fur treatment, etc., can solve the problem that the production method of transparent leather has not been reported, and the quality of finished products is difficult to be guaranteed and reduced. Leather physical and mechanical properties and other issues, to achieve the effect of strong practicability, flexible production and simple operation

Active Publication Date: 2020-07-28
SICHUAN UNIV
View PDF3 Cites 11 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

As we all know, excessive expansion of bare leather, especially acid expansion, will greatly reduce the physical and mechanical properties of leather. In severe cases, even rotten skin accidents will occur during the expansion process. Therefore, there are certain risks in the production process of this method. also difficult to guarantee
In addition, there is no report about the production method of transparent leather

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Production method of transparent leather

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0020] The deashed and softened pig head skin (thickness 1.0mm) is fully washed in the drum until the total ash content of the bare hide is less than 0.5%, and then it is taken out of the drum for 30 minutes, and weighed as the following operating materials; The polyoxypropylene stearate surfactant (HLB value 8.0) is dissolved in water with 10% of the weight of the bare hide, and then added to the drum, and rotated for 60 minutes after casting the skin; dissolve an appropriate amount of sodium hydroxide with 15% of the weight of the bare hide, Add to the drum in 4 times, rotate the drum for 20 minutes after each addition, and continue to rotate for 45 minutes after the addition. At this time, the pH value of the bath liquid is 11.5; the skins that have completed the above operations are taken out of the drum and then stretched to dry. The drying temperature is 35 ℃, the production of transparent leather is completed after complete drying.

Embodiment 2

[0022] The deashed and softened pig split skin (thickness 0.5mm) is fully washed in the drum until the total ash content of the bare hide is less than 0.2%, and then it is taken out of the drum for 30 minutes, and weighed as the following operating material benchmark; % of sorbitan trioleate surfactant (HLB value 1.8) is dissolved in 20% of the weight of bare hide in water, then added to the drum, and rotated for 30 minutes after casting the skin; dissolve an appropriate amount of sodium carbonate with 5% of the weight of bare hide in water , adding to the drum in 2 times, rotating the drum for 10 minutes after each addition, and continuing to rotate for 15 minutes after adding, at this time, the pH value of the bath solution is 9.5; after the above-mentioned operations are completed, the skin is stretched out of the drum and dried on a stretcher. 35°C, the production of transparent leather is completed after complete drying.

Embodiment 3

[0024] The deashed and softened cow split hide (thickness 2.0mm) is fully washed in the drum until the total ash content of the bare hide is less than 0.5%, and then it is taken out of the drum for 30 minutes, and weighed as the following operation material benchmark; % ethylene glycol fatty acid ester surfactant (HLB value 2.7) is dissolved in 15% water of the weight of bare skin, and then added to the drum, and rotated for 180 minutes after casting the skin; dilute an appropriate amount of formic acid with 10% water of the weight of bare skin, and divide it into 3 Add to the drum one time, and rotate the drum for 60 minutes after each addition, and continue to rotate for 90 minutes after the addition. At this time, the pH value of the bath liquid is 4.3; after the skins that have completed the above operations are taken out of the drum, they are stretched and dried at a drying temperature of 30 ° C. The production of transparent leather is completed after complete drying.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
Login to view more

Abstract

The invention discloses a production method of transparent leather. The production method of the transparent leather disclosed by the invention comprises the following four steps: 1, fully washing deashed and softened pelt with water until a total ash content is less than 0.5%, then taking the pelt out of a drum, carrying out stacking and standing for 30 minutes, and weighing the pelt, wherein theweight of the pelt is used as a reference for materials used in subsequent operation; 2, dissolving a surfactant or a polyfunctional amphiphilic substance such as a fatting agent for leather by usinga proper amount of water, adding the dissolved substance into a rotary drum, and then feeding the leather and carrying out rotating for at least 30 minutes; 3, dissolving or diluting acid or alkali with a proper amount of water, adding the dissolved or diluted acid or alkali into the rotary drum in batches, rotating the rotary drum for at least 10 minutes after each time of addition, continuing to rotate for at least 15 minutes after all the acid or alkali is added, and controlling the pH value of a bath solution to be 3.5-5.5 or 9.5-11.5; and 4, carrying out toggling and drying at a temperature not higher than 35 DEG C to finish the production of the transparent leather. Equipment and materials used in the method are widely used by leather making enterprises, and the types and the usingamounts of the materials and processing technological parameters can be adjusted according to product requirements, so practicability is high. Meanwhile, the pelt does not undergo violent expansion any more in the production process, so the production accident of breakage of the pelt is avoided, operation is easy, and risks are low.

Description

technical field [0001] The invention belongs to the technical field of leather production and processing, and in particular relates to a production method of leather with good softness and light transmission. Background technique [0002] Leather production is the production of natural polymer materials with a certain softness, fullness, chemical and microbial degradation resistance through a series of complex physical, chemical and mechanical processing of various animal skin by-products produced by animal husbandry and meat processing industries. . As we all know, conventional leather, whether it is shoe upper leather, garment leather, sofa leather or luggage leather, is a soft opaque sheet material. Some special-purpose leathers, such as drumheads for traditional drums and parchment for writing, have a certain degree of light transmittance, but these leathers are often hard and brittle, and will produce creases that are difficult to recover after bending. Even breakage ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C14C11/00C14C13/00C14C1/08
CPCC14C11/00C14C11/003C14C13/00
Inventor 张金伟
Owner SICHUAN UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap