A kind of glaze composition and its preparation method and application

A composition and glaze technology, applied in the field of glaze composition and preparation thereof, can solve the problems of low wear resistance of ceramic floor tiles, inability to achieve effective anti-skid, short service life, etc., and reduce personnel slipping and falling. Injury, increase in slip resistance, and the effect of improving slip resistance

Active Publication Date: 2021-12-07
FOSHAN UNIVERSITY
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] However, the ceramic floor tiles in the prior art cannot be effectively anti-slip, and even if more special materials are used, they cannot meet the conditions such as wet and slippery ground, and the cost of such special materials is relatively high, resulting in high production costs. The prepared ceramic floor tiles There are problems of low wear resistance and short service life, which cannot meet actual needs

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of glaze composition and its preparation method and application

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0020] A glaze composition, which is mainly prepared from the following raw material components in parts by weight: 55Kg of Yaoli glaze fruit, 5-6Kg of feldspar, 2Kg of expanded perlite, 5Kg of superfine quartz powder, 10Kg of wollastonite, Boron 25Kg, magnesium oxide 1Kg, barium oxide 1Kg, sodium tripolyphosphate 0.2-1Kg, carboxymethyl cellulose 0.1Kg and ethylene glycol 5Kg. The specific preparation process is as follows: Weigh the raw materials according to the above raw material components, wherein the ultrafine quartz powder has a particle size of 200nm, put all the raw materials into the mixer, and then add water whose mass is twice the total mass of the raw materials for mixing to obtain a slurry The slurry was dried, ball-milled for 3 hours, and passed through an 800-mesh sieve to obtain glaze composition 1.

Embodiment 2

[0022] A glaze composition, which is mainly prepared from the following raw material components in parts by weight: 55Kg of Yaoli glaze fruit, 5Kg of feldspar, 10Kg of expanded perlite, 5Kg of superfine quartz powder, 10Kg of wollastonite, and 33Kg of boron oxide , magnesium oxide 3Kg, barium oxide 3Kg, sodium tripolyphosphate 1Kg, carboxymethyl cellulose 0.1Kg and propylene glycol 5Kg. The specific preparation process is as follows: Weigh the raw materials according to the above raw material components, wherein the ultrafine quartz powder has a particle size of 200nm, put all the raw materials into the mixer, and then add water whose mass is twice the total mass of the raw materials for mixing to obtain a slurry The slurry was dried, ball-milled for 3 hours, and passed through an 800-mesh sieve to obtain glaze composition 2.

Embodiment 3

[0024] A glaze composition, which is mainly prepared from the following raw material components in parts by weight: 55Kg of Yaoli glaze fruit, 6Kg of feldspar, 5Kg of expanded perlite, 5Kg of superfine quartz powder, 10Kg of wollastonite, and 25Kg of boron oxide , magnesium oxide 1Kg, barium oxide 3Kg, sodium tripolyphosphate 0.2Kg, carboxymethyl cellulose 0.2Kg and propylene glycol 10Kg. The specific preparation process is as follows: Weigh the raw materials according to the above raw material components, wherein the ultrafine quartz powder has a particle size of 200nm, put all the raw materials into the mixer, and then add water whose mass is twice the total mass of the raw materials for mixing to obtain a slurry The slurry was dried, ball-milled for 3 hours, and passed through an 800-mesh sieve to obtain glaze composition 3.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
Login to View More

Abstract

The invention belongs to the field of glaze compositions, and discloses a method for preparing the glaze composition. The raw materials mainly include Yaoli glaze fruit, feldspar, expanded perlite, ultrafine quartz powder, wollastonite, boron oxide, Magnesium oxide, barium oxide, sodium tripolyphosphate, carboxymethyl cellulose and solvents, among them, the superimposed use of expanded perlite and wollastonite can effectively improve the static friction coefficient of the surface of the glaze composition, making its anti-skid level greatly improved Improvement, so that when the glaze composition is used to prepare ceramic tiles, it is not necessary to increase the anti-slip property by adding concave-convex textures on the surface of the glaze. The invention also discloses the glaze composition prepared by the preparation method, which has good anti-slip performance and is suitable for the preparation of anti-slip tiles, especially for kitchens, toilets, washrooms and other places, and has a long service life and strong practicability , which can meet the needs of practical use. The preparation process of the invention is simple, the raw materials are easy to obtain, the cost is low, and the application prospect is wide.

Description

technical field [0001] The invention relates to the field of glaze compositions, in particular to a glaze composition and its preparation method and application. Background technique [0002] With the development of the economy and the improvement of people's living standards, the grade of architectural decoration has been continuously improved, especially the floors of luxurious and high-end public buildings (hotels, office buildings, commercial buildings, high-end apartments, etc.), while beautifying the environment, it is easy to ignore the floor tiles. Potential safety hazards of slipping and falling. Wet and slippery ground can easily lead to accidental falls, injuries, and disability. With the rapid development of society, slip-related injuries account for an increasing proportion of work and family accidents. According to the incomplete statistics of the Ministry of Health of China, there are more than 10,000 incidents of slipping and falling injuries due to the slip...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C03C8/00C04B41/86
CPCC03C8/00C04B41/5022C04B41/86C04B41/4539
Inventor 李玲玲吴斌
Owner FOSHAN UNIVERSITY