Basalt fiber reactive powder concrete and preparation method thereof

A technology of basalt fiber and active powder, which is applied in the field of high-performance concrete, can solve the problems of high production cost of steel fiber, poor bonding between synthetic fiber and cement, and poor corrosion resistance, and achieve the goal of improving low brittleness, increasing strength, and improving mechanical properties Effect

Inactive Publication Date: 2020-10-09
JILIN UNIV
View PDF5 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The high production cost and poor corrosion resistance of steel fibers will affect the ion erosion resistance of reactive powder concrete and reduce the service life of reactive powder concrete in harsh environments
Synthetic fibers can avoid the problems caused by steel fibers, but the combination of synthetic fibers and cement is poor, and the gain effect is low. High content of fibers is often required to enhance the performance of reactive powder concrete, and high content of fibers is difficult to disperse , a special mixing method must be used

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Basalt fiber reactive powder concrete and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0031] A kind of basalt fiber active powder concrete, its preparation raw material is composed of the following components by weight: 800 parts of cement, 240 parts of silica fume, 400 parts of quartz sand fine sand, 640 parts of quartz sand medium sand, 250 parts of quartz powder, water 150 parts, 52 parts of water reducing agent, 8 parts of basalt fiber;

[0032] The specific preparation method is as follows:

[0033] Step 1, weighing the composition material of basalt fiber active powder concrete according to the metering ratio, mixing 150 parts of water and 52 parts of water reducing agent in proportion;

[0034] Step 2, take 400 parts of fine quartz sand, 640 parts of medium sand, 250 parts of quartz powder and 8 parts of basalt fiber and mix them at low speed for 2 minutes, then add 800 parts of cement and 240 parts of silica fume into the mixture and stir at low speed for 3 minutes;

[0035] Step 3, pour half of the pre-mixed water reducing agent solution, stir at low ...

Embodiment 2

[0039] A kind of basalt fiber active powder concrete, its preparation raw material is composed of the following components by weight: 740 parts of cement, 290 parts of silica fume, 400 parts of quartz sand fine sand, 640 parts of quartz sand medium sand, 230 parts of quartz powder, water 150 parts, 52 parts of water reducing agent, 6 parts of basalt fiber;

[0040] The preparation method is the same as that of Example 1, except that the formula of Example 1 is changed into that of Example 2.

Embodiment 3

[0042] A kind of basalt fiber active powder concrete, its preparation raw material is composed of the following components by weight: 730 parts of cement, 290 parts of silica fume, 390 parts of quartz sand fine sand, 624 parts of quartz sand medium sand, 230 parts of quartz powder, water 170 parts, 51 parts of water reducing agent, 4 parts of basalt fiber;

[0043] The preparation method is the same as that of Example 1, except that the formula of Example 1 is changed into that of Example 3.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
particle size (mesh)aaaaaaaaaa
Login to view more

Abstract

The invention discloses basalt fiber reactive powder concrete and a preparation method thereof. The concrete is prepared from the following raw materials in parts by weight: 730 to 800 parts of cement, 240 to 290 parts of silica fume, 390 to 400 parts of quartz sand fine sand, 624 to 640 parts of quartz sand medium sand, 230 to 260 parts of quartz powder, 140 to 170 parts of water, 50 to 52 partsof a water reducing agent and 4 to 8 parts of basalt fibers. The axial compressive strength of the basalt fiber reactive powder concrete is close to that of steel fiber reactive powder concrete, and the breaking strength of the basalt fiber reactive powder concrete is greater than that of the steel fiber reactive powder concrete. According to the method disclosed by the invention, the dry materialand the basalt fibers are firstly mixed and stirred, so that the basalt fibers are promoted to be fully dispersed during stirring, the stirring time is shortened, and the strength of the basalt fiberreactive powder concrete is improved.

Description

technical field [0001] The invention relates to a key technology of high-performance concrete with high axial compressive strength and high flexural strength prepared by using basalt fiber and active powder. Specifically, it relates to a basalt fiber active powder concrete and a preparation method. Background technique [0002] With the advancement of structural theory and the development of construction technology, bridges are developing in the direction of large span, light weight and high strength. The disadvantages of ordinary concrete, such as heavy weight, higher compressive strength than tensile strength, poor deformation capacity and brittle failure, limit the application of concrete in bridge structures. Reactive powder concrete is a high-strength, high-durability cement-based material. Compared with ordinary concrete, reactive powder concrete is added with active powder such as mineral admixtures and admixtures. A denser gradation can be formed between the mineral...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C04B28/04
CPCC04B28/04C04B2201/50C04B2201/52C04B18/146C04B14/06C04B14/4643C04B2103/302
Inventor 宫亚峰宋加祥毕海鹏刘师琪高鑫杨建星
Owner JILIN UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products