Method for treating high-silicon vanadium liquid iron for vanadium extracting through converter two-blowing, two-pouring and one-time slag discharging method
A converter and molten iron technology, applied in the field of metallurgy, can solve the problems of high residual vanadium in semi-steel, decreased quality and grade of vanadium slag, low slag production rate, etc., so as to reduce residual vanadium in semi-steel, improve the grade and quality of vanadium slag, and be easy to popularize and apply. Effect
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0024] A method for extracting vanadium from high-silicon medium-vanadium hot metal by two-blowing, two-pouring, and one-time slag removal in a converter, comprising the following steps:
[0025] A. Ratio of molten iron and scrap steel: Add molten iron and scrap steel to the LD converter, control the temperature of the molten iron to 1200°C, and adjust the ratio of scrap steel into the converter to 0%;
[0026] B. Oxygen supply for silicon removal and slag removal: during the 2.9 minutes before converter oxygen blowing smelting, the flow rate of oxygen supply is 6800m 3 / h, control the gun position to 1350mm for 2.4 minutes of oxygen blowing smelting, then lower the gun position to 400mm and continue blowing for the rest of the time, then lift the gun and pour out the initial high silicon slag;
[0027] C. Secondary oxygen supply for vanadium extraction: After pouring out the initial high-silicon slag, shake the converter, control the gun position to 900-1200mm, and control th...
Embodiment 2
[0031] A method for extracting vanadium from high-silicon medium-vanadium hot metal by two-blowing, two-pouring, and one-time slag removal in a converter, comprising the following steps:
[0032] A. Ratio of molten iron and scrap steel: Add molten iron and scrap steel to the LD converter, control the temperature of the molten iron to 1250°C, and adjust the ratio of scrap steel into the converter to 2%;
[0033] B. Oxygen supply to remove silicon and slag: during the 3.1 minutes before converter oxygen blowing smelting, the flow rate of oxygen supply is 7500m 3 / h, control the gun position to 1500mm for 2.6 minutes of oxygen blowing smelting, then lower the gun position to 500mm and continue blowing for the rest of the time, then lift the gun and pour out the initial high silicon slag;
[0034] C. Secondary oxygen supply for vanadium extraction: After pouring out the initial high-silicon slag, shake the converter, control the position of the gun at 900-1200mm, and control the f...
Embodiment 3
[0041] A method for extracting vanadium from high-silicon medium-vanadium hot metal by two-blowing, two-pouring, and one-time slag removal in a converter, comprising the following steps:
[0042] A. Ratio of molten iron and scrap steel: Add molten iron and scrap steel to the LD converter, control the temperature of the molten iron to 1220°C, and adjust the ratio of scrap steel into the converter to 7%;
[0043] B. Oxygen supply to remove silicon and slag: during the first 3 minutes of converter oxygen blowing smelting, the flow rate of oxygen supply is 7000m 3 / h, control the gun position to 1400mm for 2.5 minutes of oxygen blowing smelting, then lower the gun position to 450mm and continue blowing for the rest of the time, then lift the gun and pour out the initial high silicon slag;
[0044] C. Secondary oxygen supply for vanadium extraction: After pouring out the initial high-silicon slag, shake the converter, control the gun position to 900-1200mm, and control the oxygen f...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com