High-speed permanent magnet synchronous motor composite rotor spiral winding preparation method

A permanent magnet synchronous motor and helical winding technology, applied in the manufacture of motor generators, stator/rotor bodies, inductors/transformers/magnets, etc., can solve the problems of continuous winding between layers, high-speed motor rotor stress concentration, time-consuming, etc.

Active Publication Date: 2020-10-27
BEIHANG UNIV +1
View PDF5 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] In order to solve the problems of eddy current loss and high-speed motor rotor stress concentration caused by harmonics in the rotor of high-speed permanent magnet synchronous motors, the present invention uses magnetic powder film and carbon fiber prepreg to form a composite magnetic material. Considering the special multi-layer structure of the high-speed permanent magnet synchronous motor, the present invention proposes a met

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • High-speed permanent magnet synchronous motor composite rotor spiral winding preparation method
  • High-speed permanent magnet synchronous motor composite rotor spiral winding preparation method
  • High-speed permanent magnet synchronous motor composite rotor spiral winding preparation method

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0029] The present invention will be further described below with reference to the accompanying drawings and embodiments, and it should be understood that the following embodiments are intended to facilitate the understanding of the present invention, but do not have any limiting effect on it.

[0030] like figure 1 and 2 As shown, the method for preparing the helical winding of the composite rotor of the high-speed permanent magnet synchronous motor of the present implementation comprises the following steps:

[0031] Step 1: prepare composite magnetic material 1;

[0032] 1) Mix carbon fiber and epoxy resin to prepare carbon fiber prepreg;

[0033] 2) Mix the magnetic powder with a series of additives such as epoxy resin binder, coupling agent, curing agent, plasticizer, etc. to prepare the magnetic powder adhesive film, and then heat the magnetic powder adhesive film at 80 ℃ to make it in a molten state;

[0034] 3) In the composite material preparation equipment, the p...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention belongs to the field of motor rotor manufacturing, and particularly relates to a high-speed permanent magnet synchronous motor composite rotor spiral winding preparation method which comprises the following steps: preparing a composite magnetic material; adhering the inner surface of the permanent magnet to the surface of the motor spindle; connecting and mounting circular truncatedcone metal supporting pieces at two ends of the permanent magnet; continuously and spirally winding multiple layers of prepared composite magnetic materials on the outer surface of the carbon fiber ofthe permanent magnet in the circumferential direction, and applying a pre-tightening force in the winding process; and after winding of the composite magnetic material is completed, continuously performing winding at the surface of the composite magnetic material to form a carbon fiber protective sleeve, then performing curing, cleaning, circular truncated cone metal supporting piece dismountingand turning treatment sequentially, and preparing the composite rotor. In the spiral winding process, it can be guaranteed that each layer of magnetic powder adhesive film is evenly distributed, particularly, the problem of interlayer continuous winding can be solved, and the problem that due to continuous winding, the end of the rotating shaft is wrinkled in a winding mode or time is wasted in the cutting and re-winding process is fundamentally solved.

Description

technical field [0001] The invention belongs to the field of motor rotor manufacturing, and in particular relates to a preparation method for spiral winding of a high-speed permanent magnet synchronous motor compound rotor. Background technique [0002] The helical winding technology of composite rotor of high speed permanent magnet synchronous motor is an important step in forming the rotor of high speed permanent magnet synchronous motor. [0003] Chinese application 201920489298.5 discloses a reinforced HDPE-PTFE composite winding pipe, in which the winding method is a spiral superposition winding method, which is mainly aimed at some strips suitable for lamination winding, and for some unsuitable lamination forms such as Composite magnetic materials, this method will cause inhomogeneity of the magnetic material. In addition, this method only solves the single-layer continuous winding, and does not solve the problem of multi-layer winding. Chinese application 2012800295...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): H02K15/03H01F41/094H01F41/098H01F41/06B29C70/34
CPCB29C70/34H01F41/06H02K15/03H01F41/094H01F41/098
Inventor 王惠军张凤阁姚金宇
Owner BEIHANG UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap