Thin film mask pack having excellent wear sensation, electrical conductivity and antibacterial property, and manufacturing method therefor
A mask and mask paper technology, which can be used in medical preparations containing active ingredients, electrotherapy, and preparations for skin care, etc., can solve problems such as reduced adhesion
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Embodiment 1
[0081] A knitting machine was used to produce a knitted fabric consisting of 5% by weight of conductive nylon fibers containing copper having a thickness of 60 denier, 5% by weight of Glotech fibers having a thickness of 70 denier, and 90% by weight Made of 130-denier cotton fibers, and knitted with alternating stripes of conductive nylon fibers containing copper and Glotech fibers. The knitted knitted fabric is refined and cut into such figure 1 Mask sheet shapes as shown to prepare mask sheets. On the cotton 10 base, conductive nylon fibers 20 containing copper and non-conductive nylon fibers 30 containing copper alternately form stripes, respectively.
[0082] Wrap the socket of the bulb used to measure conductivity with a refined knitted face mask and confirm that the bulb is lit. Such as figure 2 , confirming that the bulb is lit. Elasticity is measured on refined knitted fabrics.
[0083] Antimicrobial properties were measured on refined knitted fabrics. Such as ...
Embodiment 2
[0087] A knitting machine was used to make a knitted fabric consisting of 10% by weight of the conductive nylon fibers containing copper, 10% by weight of Glotech fibers and 80% by weight of cotton fibers of 130 denier, and containing copper Conductive nylon fibers and Glotech fibers alternate in stripes. Refining the knitted fabric and cutting it into the shape of facial mask paper to prepare facial mask paper.
Embodiment 3
[0101] The conductive nylon fiber containing copper, the Glotech fiber, black polyester strands of 50 denier, and black polyurethane strands of 30 denier were prepared in a knitting machine, and coils of each fiber were adjusted length, polyester and polyurethane fibers are then alternately knitted so that conductive nylon fibers and Glotech fibers form alternating stripes.
[0102] Textured knitting into a striped form using 5 wt% conductive nylon fibers containing copper, 5 wt% Glotech, 85 wt% polyester fibers, and 5 wt% polyurethane fibers, which were refined to produce a striped knit thing.
[0103] Such as Figure 5 As shown, the prepared knitted fabric was cut into facial mask paper. On the polyester and polyurethane fiber blend 10 substrate, conductive nylon fibers 20 containing copper and non-conductive nylon fibers 30 containing copper alternately form stripes. The prepared facial mask paper is soaked in the essence and put into a packaging container to prepare a f...