Sound insulation coating for building floor and preparation method thereof

A floor and sound insulation technology, which is applied in the field of sound insulation coatings for building floors and its preparation, can solve problems such as lack of water resistance, achieve good heat preservation and fire resistance, good sound insulation and shock absorption, and prevent the spread of fire

Inactive Publication Date: 2020-12-01
惠州市百胜声学科技有限公司
View PDF4 Cites 11 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0007] The purpose of the present invention is to provide a sound-insulating coating for building floors in view of the defects and deficiencies of the existing sound-insulating and shock-absorbing coatings for floor slabs, which are mainly based on rubber-like substances for shock absorption and noise reduction, and do not have water resistance.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Sound insulation coating for building floor and preparation method thereof
  • Sound insulation coating for building floor and preparation method thereof
  • Sound insulation coating for building floor and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0049] The building floor slab of the present embodiment uses the sound insulation coating, by weight percentage, comprises the following components:

[0050] Acrylic emulsion 10%, floating beads 6%, stone-free mineral wool 42%, mica powder 5%, nitrile rubber powder 3.5%, water 32.5%, defoamer 0.20%, preservative 0.20%, hydroxyethyl cellulose 0.2 %, ferric oxide 0.4%.

[0051] Wherein, the acrylic emulsion is a composite emulsion of acrylic elastic emulsion and acrylic styrene-acrylic emulsion in a mass ratio of 13:7.

[0052] The bulk density of the floating beads is 550kg / m 3 , the particle size is 100 mesh. Stone-free mineral wool refers to mineral wool with a heavy metal content of less than 5mg / kg, a fiber diameter of no more than 9μm, a slag ball content of no more than 10wt%, and a bulk density of 70kg / m 3 . The particle size of mica powder is 180 mesh.

[0053] The dry density of the building floor slab of the present embodiment is 514kg / m 3 .

[0054] Prepare t...

Embodiment 2

[0062] The building floor slab of the present embodiment uses the sound insulation coating, by weight percentage, comprises the following components:

[0063] Acrylic emulsion 8%, floating beads 7%, stone-free mineral wool 45%, mica powder 4%, nitrile rubber powder 1%, water 34%, defoamer 0.25%, preservative 0.15%, hydroxyethyl cellulose 0.2 %, ferric oxide 0.4%.

[0064] Wherein, the acrylic emulsion is a composite emulsion of acrylic elastic emulsion and acrylic styrene-acrylic emulsion in a mass ratio of 11:9.

[0065] The bulk density of the floating beads is 550kg / m 3 , the particle size is 100 mesh. The stone-free mineral wool is mineral wool with a heavy metal content of less than 5 mg / kg, a fiber diameter of no more than 9 μm, a slag ball content of no more than 10 wt%, and a bulk density of 80 kg / m 3 . The particle size of the mica powder is 200 mesh.

[0066] The dry density of the building floor slab of the present embodiment is 526kg / m 3 .

[0067] Prepare t...

Embodiment 3

[0075] The building floor slab of the present embodiment uses the sound insulation coating, by weight percentage, comprises the following components:

[0076] Acrylic emulsion 12%, floating beads 5%, stone-free mineral wool 38%, mica powder 4%, nitrile rubber powder 5%, water 35%, defoamer 0.22%, preservative 0.18%, hydroxyethyl cellulose 0.2 %, ferric oxide 0.4%.

[0077] Wherein, the acrylic emulsion is a composite emulsion of acrylic elastic emulsion and acrylic styrene-acrylic emulsion in a mass ratio of 15:8.

[0078] The bulk density of the floating beads is 600kg / m 3 , the particle size is 100 mesh. The stone-free mineral wool is mineral wool with a heavy metal content of less than 5 mg / kg, a fiber diameter of no more than 9 μm, a slag ball content of no more than 10 wt%, and a bulk density of 100 kg / m 3 . The particle size of the mica powder is 150 mesh.

[0079] The dry density of the building floor slab of the present embodiment is 507kg / m 3 .

[0080] Prepare...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
densityaaaaaaaaaa
particle size (mesh)aaaaaaaaaa
diameteraaaaaaaaaa
Login to View More

Abstract

The invention discloses a sound insulation coating for a building floor and a preparation method of the sound insulation coating. The sound insulation coating for the building floor comprises the following components in percentage by weight: 8%-15% of an acrylic emulsion, 5%-7% of floating beads, 38%-45% of stone-free mineral wool, 3%-5% of mica powder, 1%-5% of butadiene-acrylonitrile rubber powder, 30%-35% of water and 1% of auxiliary materials, wherein the acrylic emulsion is a compound emulsion of an acrylic elastic emulsion and an acrylic styrene-acrylic emulsion in a mass ratio of (11-15): (6-9). According to the sound insulation coating for the building floor, the compound emulsion of the acrylic acid elastic emulsion and the acrylic acid styrene-acrylic emulsion is used as a basicglue emulsion of the coating, and the components such as the floating beads, the stone-free mineral wool, the mica powder and the butyronitrile rubber powder are matched for use, so the sound insulation coating has good sound insulation and shock absorption effects and also has excellent water resistance. The preparation method is mild in conditions and low in energy consumption, and can effectively prepare and produce the sound insulation coating for the building floor on a large scale.

Description

technical field [0001] The invention relates to the technical field of architectural coatings, in particular to a sound-insulating coating for building floors and a preparation method thereof. Background technique [0002] Noise refers to the sound that hinders people's normal rest, study and work, and the sound that interferes with the sound that people want to listen to. In today's society, noise has been listed as an important pollution. Noise pollution is likely to cause trouble and harm to people's health and daily life, cause people's irritability and depression, and is not conducive to people's physical and mental health. [0003] Today, with the rapid development of cities, there are more and more commercial housing, and people's requirements for commercial housing are also getting higher and higher. In commercial housing, due to the low density between buildings, the close connection between floors, and the low thickness of the floors, small sounds or vibrations s...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D133/04C09D125/14C09D109/02C09D5/18C09D7/61
CPCC08K2003/2272C08K2201/003C08K2201/005C08L2201/02C08L2205/035C09D5/18C09D133/04C09D7/61C09D7/70C08L25/14C08L9/02C08L1/284C08K13/04C08K7/10C08K3/34C08K3/22C08K7/26
Inventor 邓琦
Owner 惠州市百胜声学科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com