Solid waste unfired water permeable brick and preparation method thereof

A permeable brick and adobe technology, which is applied in the field of solid waste burn-free permeable brick and its preparation, can solve the problems of surrounding sea area pollution and other problems, achieve simple production process, wide application range, and improve the effect of bending resistance

Inactive Publication Date: 2020-12-29
张延年
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Under normal circumstances, the alkali slag is treated by accumulating on the surface, and the deposition of a large amount of alkali slag is likely to cause pollution to the surrounding sea area

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0037] A solid waste burn-free permeable brick, characterized in that: the raw materials are composed of the following components according to weight percentage: 27 parts of phosphorus slag, 23 parts of alkali slag, 8 parts of silica fume, 18 parts of fly ash, and 10 parts of epoxy resin 14 parts of water.

[0038] The preparation process of permeable bricks is as follows:

[0039] (1) Dechlorinate the alkali slag produced by solid waste by water washing or electroosmosis;

[0040] (2) Weigh or prepare each component according to the proportion;

[0041] (3) Burn phosphorus slag and chlorine-alkali removal slag at a ratio of 5:3 and 5:6 at 1350-1450°C and 1450-1700°C respectively; Chlor-alkali slag accounts for 17 parts and 10 parts of the total weight respectively; phosphorus slag and chlorine-alkali removal slag under the condition of 1450-1750 °C account for 10 parts and 13 parts of the total weight respectively;

[0042] (4) Grind the fired phosphorus slag and chlorine-...

Embodiment 2

[0052] A solid waste burn-free permeable brick, characterized in that: the raw materials are composed of the following components according to weight percentage: 30 parts of phosphorus slag, 20 parts of alkali slag, 8 parts of silica fume, 17 parts of fly ash, and 10 parts of epoxy resin 15 parts, water 15 parts.

[0053] The preparation process of permeable bricks is as follows:

[0054] (1) Dechlorinate the alkali slag produced by solid waste by water washing or electroosmosis;

[0055] (2) Weigh or prepare each component according to the proportion;

[0056] (3) Burn phosphorus slag and chlorine-alkali removal slag at a ratio of 5:3 and 5:6 at 1350-1450°C and 1450-1700°C respectively; The chlor-alkali slag accounts for 19 parts and 9 parts of the total weight respectively; the phosphorus slag and the chlorine-alkali removal slag under the condition of 1450-1750 ℃ ​​respectively account for 11 parts and 11 parts of the total weight;

[0057] (4) Grind the fired phosphorus...

Embodiment 3

[0067] A solid waste burning-free permeable brick, characterized in that: the raw materials are composed of the following components according to weight percentage: 25 parts of phosphorus slag, 23 parts of alkali slag, 8 parts of silica fume, 20 parts of fly ash, and 10 parts of epoxy resin 14 parts of water.

[0068] The preparation process of permeable bricks is as follows:

[0069] (1) Dechlorinate the alkali slag produced by solid waste by water washing or electroosmosis;

[0070] (2) Weigh or prepare each component according to the proportion;

[0071] (3) Burn phosphorus slag and chlorine-alkali removal slag at a ratio of 5:3 and 5:6 at 1350-1450°C and 1450-1700°C respectively; The chlor-alkali slag accounts for 16 parts and 11 parts of the total weight respectively; the phosphorus slag and the chlorine-alkali removal slag under the condition of 1450-1750 ℃ ​​respectively account for 9 parts and 12 parts of the total weight;

[0072] (4) Grind the fired phosphorus sla...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
particle sizeaaaaaaaaaa
Login to View More

Abstract

The invention discloses a solid waste unfired water permeable brick and a preparation method thereof, and belongs to the technical field of building materials, the water permeable brick is composed ofthe following components by weight: 22-30 parts of phosphorus slag, 15-23 parts of alkaline slag, 6-10 parts of silica fume, 17-20 parts of fly ash, 8-10 parts of epoxy resin, and 10-15 parts of water. Alkaline slag and phosphorus slag adopted by the method belong to solid waste produced by factory production, and the solid waste is recycled and then treated to a certain extent for reuse, so thatenvironmental pollution caused by the phosphorus slag and the alkaline slag is reduced. Meanwhile, the utilization rate is also improved; chlorine in the alkaline residues is removed through a waterwashing method, water washing is conducted three times or more according to the water-solid ratio of 6: 1, pollution of chloride ions to the environment is prevented, and meanwhile the compressive strength and breaking strength of the water permeable brick are improved.

Description

technical field [0001] The invention relates to a solid waste burn-free permeable brick and a preparation method thereof, belonging to the technical field of building materials. Background technique [0002] Phosphorus slag is a kind of low melting point slag that is discharged regularly in the furnace when yellow phosphorus is produced by electric furnace method. About 8-10t of phosphorus slag is discharged for every 1t of yellow phosphorus produced. There are about 60 small and medium-sized yellow phosphorus factories in China all over the country. With the massive discharge of phosphorus slag, the environmental pollution is aggravated. In order to use phosphorus slag more effectively, my country formally formulated and implemented "GB6645-86 for granulated electric furnace phosphorus slag in cement" in 1986. Not much, effective use of phosphorus slag, turning waste into wealth, has obvious social and economic benefits, and has a broad prospect. [0003] Alkali slag is ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B28/00C04B7/26C04B7/24B28B3/00
CPCB28B3/00C04B7/24C04B7/26C04B28/00C04B2111/00017C04B24/281Y02P40/10
Inventor 张延年王铁源秦桂娟闫明程于洋李志军陈志燕杜松岩董宁李琦琦陈昊刘柏男张文洁崔长青王亭张于于康楠
Owner 张延年
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com