Preparation process of nickel-plated carbon fiber felt

A nickel-plated carbon fiber and preparation process technology, applied in the field of fiber products, can solve the problems of reducing the quality of fiber felt and poor fiber effect, and achieve the effects of reducing knots and agglomeration, improving felt quality and improving dispersibility.

Active Publication Date: 2021-02-26
南京柯普新材料科技有限公司
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] In view of the related technologies mentioned above, the inventor believes that: in the process of preparing the fiber felt, if the fiber effect is not good in the early stage, the quality of the fiber felt will be reduced.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation process of nickel-plated carbon fiber felt
  • Preparation process of nickel-plated carbon fiber felt
  • Preparation process of nickel-plated carbon fiber felt

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0041] The following is attached Figure 1-5 The application is described in further detail.

[0042] The embodiment of the application discloses a double deflagging machine.

[0043] Such as figure 1 with figure 2 As shown, the double deflagging machine mainly includes a stirring and deflaking device 1 and a high-frequency deflaking device 2, wherein the high-frequency deflaking device 2 is a commercially available high-frequency deflaking device, and the stirring and deflaking device 1 includes a first stirring device 11 and a second stirring device 12 , the feeding ends of the first stirring device 11 and the second stirring device 12 are all connected with a main feed pipe 4, the fifth control valve 41 is connected between the first stirring device 11 and the main feed pipe 4, the second stirring device 12 A sixth control valve 42 is connected with the main feed pipe 4 . Open the fifth control valve 41 to feed into the first stirring device 11 , and open the sixth con...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a preparation process of a nickel-plated carbon fiber felt, and relates to the field of fiber products. The preparation process includes the steps of fiber pretreatment: dispersing fibers; and felt making and forming: performing felt making and forming on the dispersed fibers, then applying glue to the formed fibers, and obtaining felt after the glue is cured. The fiber pretreatment includes the steps of mixing the fibers and water, stirring and dispersing to obtain pretreated slurry, and carrying out secondary defibering on the pretreated slurry to obtain dispersed fiber slurry. According to the preparation process of the nickel-plated carbon fiber felt, the quality of the fiber felt can be effectively improved.

Description

technical field [0001] The present application relates to the field of fiber products, in particular to a preparation process of nickel-plated carbon fiber felt. Background technique [0002] Fiber is a substance composed of continuous or discontinuous filaments, and is widely used in textiles, military, environmental protection, medicine, construction, biology and other fields; among them, carbon fiber is mainly composed of carbon atoms, and carbon fiber has high stiffness and high tensile strength. Advantages of strength, low weight, high chemical resistance, high temperature resistance and low thermal expansion. These properties make carbon fiber very popular in aerospace, civil engineering, and military. [0003] Carbon fiber is often made into felt. Carbon fiber felt not only has the advantages of highly developed microporous structure, large adsorption capacity, fast desorption speed, and good purification effect, but also has the advantages of broad absorption, large...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): D04H1/08
CPCD04H1/08
Inventor 谢双庆龚健龚毅谢德荣
Owner 南京柯普新材料科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com