High-strength low-density steel welding process

A welding process and low-density technology, which is applied in the field of steel processing, can solve problems such as oxidation, lower yield, and low density, and achieve the effects of improving adsorption efficiency, increasing efficiency, and reducing efficiency

Active Publication Date: 2021-03-02
广西天正钢结构有限公司
View PDF7 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] Fe-Mn-Al-C low-density steel, due to its excellent mechanical properties, low density, and corrosion resistance, can be developed as a lightweight automobile body material with low energy consumption and lo

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • High-strength low-density steel welding process
  • High-strength low-density steel welding process
  • High-strength low-density steel welding process

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0041] see figure 1 , a high-strength low-density steel welding process, comprising the following steps:

[0042] S1. Derust the surface of the steel to be welded, rinse it with deionized water for 2-3 times, and then dry it to complete the pretreatment of the steel;

[0043] S2. Pre-processing the welded part of the steel, cutting off the corner of the welded part, and sticking the two steels to each other, so that a V-shaped groove is formed at the welded part of the steel;

[0044] S3. Place the anti-oxidation sticker 1 on the surface of the steel and place it outside the V-shaped groove, then place the electrode in the V-shaped groove, and then perform spot welding on the electrode to complete the welding of the steel.

[0045] see Figure 2-5 , The anti-oxidation block 1 in S3 has a built-in storage cavity 2, and the inner wall of the built-in storage cavity 2 is drilled with a release hole 3, and the inner wall of the release hole 3 is connected with a pair of rubber s...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a high-strength low-density steel welding process, and belongs to the technical field of steel processing. The scheme can promote calcium bicarbonate powder in a built-in storage cavity to be heated and decomposed and generate a large amount of carbon dioxide gas through the temperature during welding, and along with the increase of air pressure and the increase of temperature, a heat-variable guide rope can be promoted to recover to the high-temperature phase state, so that rubber sealing sheets are lifted upwards to promote the release of carbon dioxide, on one hand,the possibility of overhigh external temperature of the steel is reduced by virtue of the thermal decomposition of calcium bicarbonate powder, on the other hand, by virtue of the release of carbon dioxide, the possibility of steel oxidation due to too high temperature in the welding process is reduced, meanwhile, by means of expansion of an attachment guide ball, magnetic shielding on a built-in magnetic ball can be relieved, the bottom side of an anti-oxidation attachment block is promoted to be tightly attached to the steel, thermal decomposition of the calcium bicarbonate powder can be accelerated, gaps between the anti-oxidation attachment block and the steel can be reduced, and therefore oxidation of the steel is reduced.

Description

technical field [0001] The invention relates to the technical field of steel processing, more specifically, to a high-strength low-density steel welding process. Background technique [0002] With the continuous and rapid development of China's economy, the number of motor vehicles continues to maintain a rapid growth trend. By the end of 2018, the number of motor vehicles in the country reached 327 million. Research shows that: the fuel consumption of automobiles has a linear relationship with the weight of the body, and other conditions remain unchanged. Under the premise that the vehicle weight is reduced by 10%, the fuel consumption can be reduced by 6-8%, and every 1L fuel consumption reduction will reduce the emission of 2.45kg of CO2. It can be seen that the impact of reducing vehicle exhaust emissions on the environment is very great. In addition, in the field of aerospace, the weight reduction of spacecraft is also of great significance. It not only reduces fuel con...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): B23K20/02B23K20/24B23K20/26
CPCB23K20/023B23K20/026B23K20/24B23K20/26
Inventor 谢振宁
Owner 广西天正钢结构有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap