Antibacterial mildew-proof transparent ABS master batch and preparation method thereof

A technology of antibacterial and antifungal, antibacterial and antifungal agent, applied in the field of polymer material modification, can solve the problems of transparency and antibacterial effect to be improved, and achieve the effect of efficient bactericidal performance and maintaining transparency

Inactive Publication Date: 2021-04-09
珠海格力绿色再生资源有限公司
View PDF5 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

There are also some spray-free materials and non-transparent materials in the prior art, but their transparency and antibacterial effect need to be improved

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Antibacterial mildew-proof transparent ABS master batch and preparation method thereof
  • Antibacterial mildew-proof transparent ABS master batch and preparation method thereof
  • Antibacterial mildew-proof transparent ABS master batch and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 8

[0040] A preparation method of antibacterial and mildew-proof transparent ABS masterbatch, is characterized in that, comprises the following steps:

[0041] S1. Raw material pretreatment;

[0042] S2. Put the masterbatch raw material into the high-speed mixer according to the weight ratio and stir evenly;

[0043] S3. Control the temperature of each zone of the twin-screw extruder within the range of 160°C-200°C, keep the vacuum degree of the vacuum vent hole of the extruder within the range of -0.1MPa--0.09MPa, and add the mixed raw materials into the twin-screw extruder Melt blending in a screw extruder, extruded into strips, cooled, dried, pelletized, and packaged to complete the preparation of transparent ABS antibacterial and anti-mildew masterbatch.

[0044] In the present invention, the masterbatch is prepared by a method of melt blending.

[0045] Further, in step S1, it includes pre-treating the transparent ABS resin and the antibacterial and antifungal agent respec...

Embodiment 9

[0049] A preparation method of antibacterial and mildew-proof transparent ABS masterbatch, is characterized in that, comprises the following steps:

[0050] S1. Raw material pretreatment;

[0051]S2. Put the masterbatch raw material into the high-speed mixer according to the weight ratio and stir evenly;

[0052] S3. Control the temperature of each zone of the twin-screw extruder within the range of 160°C-200°C, keep the vacuum degree of the vacuum vent hole of the extruder within the range of -0.1MPa--0.09MPa, and add the mixed raw materials into the twin-screw extruder Melt blending in a screw extruder, extruded into strips, cooled, dried, pelletized, and packaged to complete the preparation of transparent ABS antibacterial and anti-mildew masterbatch.

[0053] In the present invention, the masterbatch is prepared by a method of melt blending.

[0054] Further, in step S1, it includes pre-treating the transparent ABS resin and the antibacterial and antifungal agent respect...

Embodiment 10

[0058] A preparation method of antibacterial and mildew-proof transparent ABS masterbatch, is characterized in that, comprises the following steps:

[0059] S1. Raw material pretreatment;

[0060] S2. Put the masterbatch raw material into the high-speed mixer according to the weight ratio and stir evenly;

[0061] S3. Control the temperature of each zone of the twin-screw extruder within the range of 160°C-200°C, keep the vacuum degree of the vacuum vent hole of the extruder within the range of -0.1MPa--0.09MPa, and add the mixed raw materials into the twin-screw extruder Melt blending in a screw extruder, extruded into strips, cooled, dried, pelletized, and packaged to complete the preparation of transparent ABS antibacterial and anti-mildew masterbatch.

[0062] In the present invention, the masterbatch is prepared by a method of melt blending.

[0063] Further, in step S1, it includes pre-treating the transparent ABS resin and the antibacterial and antifungal agent respec...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
transparencyaaaaaaaaaa
antibacterial rateaaaaaaaaaa
Login to view more

Abstract

The invention belongs to the technical field of high polymer material modification, and provides an antibacterial mildew-proof transparent ABS master batch which comprises the following components in parts by weight: 72-82 parts of transparent ABS resin, 2-8 parts of a first dispersing agent, 15-23 parts of an antibacterial mildew-proof agent, 1.5-3.2 parts of a second dispersing agent, 0.01-1 part of a hindered phenol antioxidant, 0.02-1.3 parts of a phosphite antioxidant and 0-0.1 part of ultramarine pigment powder. According to the invention, through pretreatment of the antibacterial mildew-proof agent, a raw material mixing process and a melt blending process, uniform dispersion of the antibacterial mildew-proof agent in the ABS resin is ensured, so that the antibacterial mildew-proof agent has broad-spectrum and high-efficiency bactericidal performance of an organic antibacterial mildew-proof agent and the characteristics of safety, long-acting effect, temperature resistance and the like of an inorganic antibacterial mildew-proof agent, and simultaneously keeps the transparency of ABS workpieces.

Description

technical field [0001] The invention belongs to the technical field of polymer material modification, and in particular relates to an antibacterial and antifungal transparent ABS masterbatch and a preparation method thereof. Background technique [0002] The development and utilization of antibacterial plastics is one of the research hotspots in the field of functional plastics. Traditional plastic substrates such as polycaprolactone (PCL), low-density polyethylene (LDPE), high-density polyethylene (HDPE), polypropylene (PP) , Ethylene-vinyl acetate copolymer (EVA), polylactic acid (PLA), acrylonitrile-butadiene-styrene copolymer (ABS) can be modified by adding antibacterial agents. [0003] ABS (acrylonitrile-butadiene-styrene) resin is an important general-purpose synthetic resin. The main body is a blend or terpolymer of acrylonitrile, butadiene and styrene. It is a tough and rigid thermoplastic. plastic. It has a wide range of uses. The automobile industry is often use...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L55/02C08L91/06C08L23/06C08K13/02C08K5/134C08K5/526C08K3/015C08K5/00C08J3/22
CPCC08J3/226C08J2455/02C08J2491/06C08J2423/06C08K13/02C08K5/1345C08K5/526C08K3/015C08K5/0058
Inventor 唐梓健张奇王琳刘冬丽丁龙龙张志平
Owner 珠海格力绿色再生资源有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap