Nano-resin multifunctional ceramic tile interface agent

A multi-functional, interface agent technology, applied in the direction of coating, can solve the problems of insufficient surface uniformity, reduced production efficiency, prone to coagulation, etc., to ensure coating uniformity, reduce production costs, and solve coagulation problems Effect

Inactive Publication Date: 2021-04-16
孙龙海
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] However, the existing interface agent components are relatively complex, which is not conducive to controlling the process flow during preparation and production, which not only greatly reduces production efficiency and increases costs, but also has insufficient performance of the interface agent. Coagulation occurs, resulting in insufficient surface uniformity, poor improvement effect, and affects production and use effects

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0027] As preferably, the preparation method of described interface agent comprises the steps:

[0028] S1. Weigh each raw material according to the mass percentage and set aside;

[0029] S2. Add water into the reaction kettle, heat to 50-60 degrees Celsius, mix polyvinyl alcohol, and stir evenly for 30 minutes to 45 minutes at a rate of 35 rpm to 40 rpm, and mix to obtain a mixed raw material ;

[0030] S3. Stir the latex defoamer in the mixed raw materials evenly for 5 minutes to 8 minutes to eliminate air bubbles and obtain the processed raw materials;

[0031] S4. Heating the processing raw materials to 85-90 degrees Celsius, melting the polyvinyl alcohol particles, adding nano-resin fibers, and stirring evenly for 20 to 30 minutes at a rate of 80 to 100 rpm to obtain the reaction raw materials;

[0032] S5, cooling the reaction raw materials to 30°C to 35°C, adding cement penetrating agent and preservative, stirring evenly for 5 minutes to 8 minutes, to obtain the proc...

Embodiment 1

[0046] A nano-resin multi-functional interface agent for tiles, which is made of the following raw materials: 82.8% water, 15% polyvinyl alcohol, 0.2% defoamer, 0.5% nano-resin fiber, cement penetrating agent 1 % and preservatives 0.5%.

[0047] As preferably, the preparation method of described interface agent comprises the steps:

[0048] S1. Weigh each raw material according to the mass percentage and set aside;

[0049] S2. Add water into the reaction kettle, heat to 50-60 degrees Celsius, mix polyvinyl alcohol, and stir evenly for 30 minutes to 45 minutes at a rate of 35 rpm to 40 rpm, and mix to obtain a mixed raw material ;

[0050] S3. Stir the latex defoamer in the mixed raw materials evenly for 5 minutes to 8 minutes to eliminate air bubbles and obtain the processed raw materials;

[0051] S4. Heating the processing raw materials to 85-90 degrees Celsius, melting the polyvinyl alcohol particles, adding nano-resin fibers, and stirring evenly for 20 to 30 minutes at...

Embodiment 2

[0065] A nano-resin multi-functional interface agent for tiles, which is made of the following raw materials: 76.2% water, 20% polyvinyl alcohol, 0.3% defoamer, 1% nano-resin fiber, and 1.5% cement penetrating agent % and preservatives 1%.

[0066] As preferably, the preparation method of described interface agent comprises the steps:

[0067] S1. Weigh each raw material according to the mass percentage and set aside;

[0068] S2. Add water into the reaction kettle, heat to 50-60 degrees Celsius, mix polyvinyl alcohol, and stir evenly for 30 minutes to 45 minutes at a rate of 35 rpm to 40 rpm, and mix to obtain a mixed raw material ;

[0069] S3. Stir the latex defoamer in the mixed raw materials evenly for 5 minutes to 8 minutes to eliminate air bubbles and obtain the processed raw materials;

[0070] S4. Heating the processing raw materials to 85-90 degrees Celsius, melting the polyvinyl alcohol particles, adding nano-resin fibers, and stirring evenly for 20 to 30 minutes...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a nano-resin multifunctional ceramic tile interface agent, which is prepared from the following raw materials: 60%-80% of water, 15%-20% of polyvinyl alcohol, 0.1%-0.3% of a defoaming agent, 0.5%-1% of nano-resin fibers, 1%-1.5% of a cement penetrant and 0.5%-1% of a preservative. According to the invention, the nano-resin multifunctional ceramic tile interface agent provided by the invention is prepared from the raw materials in a reasonable proportion, and only multi-stage heating and stirring mixing are needed, so that the technological process is simple and easy to control, and the production cost is effectively reduced; expanded polyvinyl alcohol particles are adopted, so that melting treatment is easy, and the time is shortened; the nano resin fibers are added, so that the coagulation problem is effectively solved, and the coating uniformity is ensured; and due to the water-based characteristic, the nano resin fibers can be directly mixed with concrete raw materials for use and are beneficial to mixing, so that the production and processing convenience and the use stability can be greatly improved.

Description

technical field [0001] The invention relates to the technical field of interface agents, in particular to a nano-resin multifunctional tile interface agent. Background technique [0002] Under the current social development conditions, more and more concrete buildings are used. In order to ensure safety and aesthetics, ceramic tiles are generally pasted on the concrete surface for decoration. In order to improve the surface adhesion of concrete and ensure the stability of pasting In order to improve the adhesion properties of the concrete surface, an interface agent is required. [0003] However, the existing interface agent components are relatively complex, which is not conducive to controlling the process flow during preparation and production, which not only greatly reduces production efficiency and increases costs, but also has insufficient performance of the interface agent. Coagulation occurs, resulting in insufficient surface uniformity, poor improvement effect, and...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09D129/04C09D7/65C09D7/61
Inventor 孙龙海
Owner 孙龙海
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap