Preparation method for glass fiber reinforced plastic water collector

A water collector and glass fiber reinforced plastic technology, which is applied in the field of water collectors, can solve the problems of inapplicability and exceed the softening temperature of PVC and PP materials, and achieve the effect of preventing softening and deformation and increasing water collection efficiency.

Pending Publication Date: 2021-04-20
ANHUI HANGDA ENVIRONMENTAL PROTECTION TECH
View PDF7 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] Ordinary cooling tower water receiver is made of PVC or PP material, but if the cooling tower is under standard working conditions, the water temperature entering the tower exceeds 80°C, and the outlet air temperature will also exceed 75°C, which exceeds the softening temperature of PVC and PP materials. Be applicable

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment

[0033] The preparation method of the FRP water eliminator described in this embodiment comprises the following steps:

[0034] S1. Prepare the water eliminator sheet mold and corrosion-resistant resin;

[0035] S2. Coating a release agent on the water eliminator sheet mold;

[0036] S3. Apply the gel coat layer after the release agent is dried;

[0037] S4. Build-up coating: coating resin and fiber in a single cycle until the required thickness is reached;

[0038] S5. Curing and demoulding, placing the product that has been laminated and coated after step S4 together with the mold in a normal temperature environment for curing, and demoulding after the laminate is cured to obtain a water eliminator sheet;

[0039] S6. Assembly: Assemble multiple water eliminator pieces into a water eliminator, and connect adjacent water eliminator pieces through brackets. The bracket is made of ABS material.

[0040] The fiberglass water eliminator proposed in this technical solution uses...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
lengthaaaaaaaaaa
epoxy equivalentaaaaaaaaaa
Login to View More

Abstract

The invention provides a preparation method for a glass fiber reinforced plastic water collector. The preparation method comprises the following steps that S1, a water collector sheet mold and corrosion-resistant resin are prepared; S2, the water collector sheet mold is coated with a release agent; S3, a gel coat layer is coated after the release agent is dried; S4, lamination coating is carried out, and specifically, the resin and fibers are circularly coated once until the required thickness is reached; S5, curing stripping is carried out, specifically, a product obtained after lamination coating in the step S4 and the mold are placed in a normal-temperature environment together to be cured, and stripping is carried out after lamination curing to prepare a water collector sheet; and S6, assembling is carried out, specifically, multiple water collector sheets are assembled into the water collector, and the adjacent water collector sheets are connected through a support. According to the glass fiber reinforced plastic water collector provided by the technical scheme, glass fiber reinforced plastic is formed by the resin and the fibers to serve as a water collector sheet material, the supports made of ABS materials are used for connection, high temperature resistance can be achieved so as to prevent softening deformation, and the strength, corrosion resistance and durability are far higher than those of a common water collector.

Description

technical field [0001] The invention relates to the technical field of water eliminators, in particular to a method for preparing a glass fiber reinforced plastic water eliminator. Background technique [0002] The water eliminator (also known as the water eliminator) in the cooling tower is a water-saving device used to reduce the entrainment of water droplets in the air discharged from the cooling tower. [0003] A water eliminator is installed in the cooling tower, and the discharged air carries a lot of water after flowing through the water spray and water distribution system. Before the air exits the cooling tower, the water eliminator in the cooling tower is used to collect the water, so as to prevent the loss of circulating cooling water and rusting of equipment caused by floating water, and at the same time protect the environment and avoid pollution to the surrounding environment. We know that the loss of cooling water in cooling towers without water eliminators is...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): B29C70/34B29C70/54C08L77/00C08L63/00C08K7/14C08K5/092C08K3/22C08K3/34C08K3/36C08K3/38C08K13/04C08J5/04
Inventor 储斌
Owner ANHUI HANGDA ENVIRONMENTAL PROTECTION TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products