A kind of antibacterial non-woven fabric and its preparation process

A non-woven, benzaldehyde technology, used in non-woven fabrics, rayon manufacturing, textiles and papermaking, etc., can solve the problem of mildew on the surface of non-woven fabrics, reduce breeding, improve toughness, and improve antibacterial effects. Effect

Active Publication Date: 2021-10-01
浙江雅宝无纺布制品有限公司
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] In order to improve the problem that mildew will appear on the surface of non-woven fabrics after being placed for a long time, the application provides an antibacterial non-woven fabric and its preparation process

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of antibacterial non-woven fabric and its preparation process
  • A kind of antibacterial non-woven fabric and its preparation process
  • A kind of antibacterial non-woven fabric and its preparation process

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0036] The application discloses an antibacterial non-woven fabric, comprising the following raw materials: polypropylene resin; 3,4-dihydroxy-5-nitro-benzaldehyde; nano-TiO 2 , its preparation process comprises the following steps:

[0037] S1. Preparation of fiber filaments; 50 parts of polypropylene resin, 8 parts of nano-TiO 2 and 10 parts of 3,4-dihydroxy-5-nitro-benzaldehyde were extruded and melted at 170°C, stirred and reacted for 30 minutes, spun at a flow rate of 0.5g / min, and cooled to room temperature to obtain fiber filaments;

[0038] S2. Preparation of the fiber web; loosening and carding the fiber filaments in S1, and then laying them into a fiber web;

[0039] S3. the preparation of non-woven fabric; 2 Acupuncture at a density of 200 needles / cm 2 Acupuncture at a density of 1000 needles / cm 2 Needle punching at a certain density to produce a non-woven fabric.

[0040] The content of each component is shown in Table 1 below.

Embodiment 2

[0042] The application discloses an antibacterial non-woven fabric, comprising the following raw materials: polypropylene resin; 3,4-dihydroxy-5-nitro-benzaldehyde; nano-TiO 2 , its preparation process comprises the following steps:

[0043] S1. Preparation of fiber filaments; 60 parts of polypropylene resin, 10 parts of nano-TiO 2 and 12 parts of 3,4-dihydroxy-5-nitro-benzaldehyde were extruded and melted at 180°C, stirred and reacted for 40 minutes, spun at a flow rate of 0.5g / min, and cooled to room temperature to obtain fiber filaments;

[0044] S2. Preparation of the fiber web; loosening and carding the fiber filaments in S1, and then laying them into a fiber web;

[0045] S3. the preparation of non-woven fabric; 2 Acupuncture at a density of 800 needles / cm 2 Acupuncture at a density of 4000 needles / cm 2 Needle punching at a certain density to produce a non-woven fabric.

[0046] The content of each component is shown in Table 1 below.

Embodiment 3

[0048] The application discloses an antibacterial non-woven fabric, comprising the following raw materials: polypropylene resin; 3,4-dihydroxy-5-nitro-benzaldehyde; nano-TiO 2 , its preparation process comprises the following steps:

[0049] S1. Preparation of fiber filaments; 55 parts of polypropylene resin, 9 parts of nano TiO 2 and 11 parts of 3,4-dihydroxy-5-nitro-benzaldehyde were extruded and melted at 175°C, stirred and reacted for 35 minutes, spun at a flow rate of 0.5g / min, and cooled to room temperature to obtain fiber filaments;

[0050] S2. Preparation of the fiber web; loosening and carding the fiber filaments in S1, and then laying them into a fiber web;

[0051] S3. the preparation of non-woven fabric; 2 Acupuncture at a density of 500 needles / cm 2 Acupuncture at a density of 2500 needles / cm 2 Needle punching at a certain density to produce a non-woven fabric.

[0052] The content of each component is shown in Table 1 below.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The application relates to the field of non-woven fabrics, and specifically discloses an antibacterial non-woven fabric and a preparation process thereof. An antibacterial non-woven fabric, comprising the following raw materials in parts by weight: 50-60 parts of polypropylene resin; 10-12 parts of 3,4-dihydroxy-5-nitro-benzaldehyde; 8-10 parts of nano TiO 2 . The preparation process is as follows: S1. preparation of fiber filaments; S2. preparation of fiber web; S3. preparation of non-woven fabric. The antibacterial non-woven fabric of the present application adopts 3,4-dihydroxy-5-nitro-benzaldehyde, and the aldehyde group in the molecular structure of 3,4-dihydroxy-5-nitro-benzaldehyde can interact with microbial cells The combination of amino groups on the enzyme molecular structure inhibits the enzyme activity, thereby inhibiting the cell growth and proliferation of microorganisms, reducing the growth of microorganisms on the surface of non-woven fabrics, thereby reducing the mildew on the surface of non-woven fabrics and improving the non-woven fabric. The antibacterial effect of the woven fabric; in addition, the preparation process of the present application needle-punches the fiber layer by dividing the density, which improves the compactness of the connection between the fiber filaments and makes the non-woven fabric obtained have better toughness.

Description

technical field [0001] The application relates to the field of non-woven fabrics, more specifically, it relates to an antibacterial non-woven fabric and its preparation process. Background technique [0002] Non-woven fabrics, also known as non-woven fabrics, are composed of oriented or random fibers. It is called cloth because of its appearance and certain properties. [0003] The non-woven fabrics in the prior art are widely used in the medical and health industry, and are widely used in production and life. For example, it is widely used in paper diapers, sanitary napkins, panty liners, wet wipes, Band-Aids, masks, food packaging bags and other products. [0004] The inventor found that after the non-woven fabric is placed for a long time, mildew will appear on the surface, which affects the processing and use of the non-woven fabric, and needs to be improved. Contents of the invention [0005] In order to improve the problem that mildew will appear on the surface of...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): D04H1/46D04H1/4291D01F1/10D01F6/06
Inventor 陆臣省陆文俊
Owner 浙江雅宝无纺布制品有限公司