High-permeability PVC artificial leather and application thereof
What is Al technical title?
Al technical title is built by PatSnap Al team. It summarizes the technical point description of the patent document.
A kind of artificial leather, permeability technology, applied in textiles and papermaking, etc., can solve problems affecting PVC artificial leather and so on
Pending Publication Date: 2021-05-14
南通中奥车用新材料有限公司
View PDF0 Cites 2 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
PVC artificial leather with high permeability is very popular, but excessive pursuit of high permeability will affect other properties of PVC artificial leather, such as tensile resistance, peel strength, cold resistance, high temperature resistance, etc.
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Examples
Experimental program
Comparison scheme
Effect test
Embodiment 1
[0048] Embodiment 1: High permeability PVC artificial leather one:
[0049] A kind of high-permeability PVC artificial leather, the PVC artificial leather component is by weight:
[0050] The weight fraction of polyvinyl chloride is 20 parts, the weight fraction of tetraethylenepentamine is 5 parts, the weight fraction of modified polyvinyl chloride is 10 parts, the weight fraction of self-made adhesive is 5 parts, the weight fraction of soybean protein is 5 parts, and the weight fraction of natural resin is 5 parts, 2 parts by weight of vegetable oil, 10 parts by weight of vinyl acetate-ethylene copolymer emulsion, 2 parts by weight of plasticizer, 2 parts by weight of stabilizer, and 2 parts by weight of foaming agent.
[0051] The preparation method of this PVC artificial leather is as follows:
[0052] (1) Under normal pressure, put the polyvinyl chloride resin with a weight fraction of 20 parts into the reactor in a dry state, and directly carry out the chlorination reac...
Embodiment 2
[0060] Embodiment 2: High permeability PVC artificial leather one:
[0061] A kind of high-permeability PVC artificial leather, the PVC artificial leather component is by weight:
[0062] The weight fraction of polyvinyl chloride is 40 parts, the weight fraction of tetraethylenepentamine is 10 parts, the weight fraction of modified polyvinyl chloride is 15 parts, the weight fraction of self-made adhesive is 10 parts, the weight fraction of soybean protein is 10 parts, and the weight fraction of natural resin is 10 parts, 5 parts by weight of vegetable oil, 15 parts by weight of vinyl acetate-ethylene copolymer emulsion, 5 parts by weight of plasticizer, 5 parts by weight of stabilizer, and 5 parts by weight of foaming agent.
[0063] The preparation method of this PVC artificial leather is as follows:
[0064] (1) Under normal pressure, put the polyvinyl chloride resin with a weight fraction of 40 parts into the reactor in a dry state, and directly carry out the chlorination ...
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
PUM
Login to view more
Abstract
The invention discloses high-permeability PVC artificial leather and application thereof. The high-permeability PVC artificial leather is prepared from polyvinyl chloride, tetraethylenepentamine, modified polyvinyl chloride, a self-made adhesive, soybean protein, natural resin, vegetable oil, vinyl acetate-ethylene copolymer emulsion, a plasticizer, a stabilizer and a foaming agent. Polyvinyl chloride molecules subjected to chlorination treatment improve the thermal deformation temperature and the dissolving property of the material, and meanwhile, the processed material has good cohesiveness; the chlorinated polyvinyl chloride is modified by tetraethylenepentamine, so that the tensile strength of the material is enhanced to the maximum extent; the self-made adhesive utilizes vinyl acetate-ethylene copolymer emulsion, modified natural resin, modified vegetable oil and modified soybean protein, so that the peel strength of the PVC artificial leather is improved; and when the artificial leather is prepared, calendaring film forming and foaming treatment on the two sides are carried out at the same time, the foaming treatment provides more pressure for calendaring film forming, so that the material and the cloth base are combined more tightly, and the foaming time is shortened.
Description
technical field [0001] The invention relates to the technical field of PVC artificial leather, in particular to a high-permeability PVC artificial leather and its application. Background technique [0002] With the continuous progress and development of PVC production and processing technology, PVC artificial leather has not only greatly improved in quality, but also has an increasing variety of designs and colors. PVC artificial leather with high permeability is very popular, but excessive pursuit of high permeability will affect other properties of PVC artificial leather, such as tensile resistance, peel strength, cold resistance, high temperature resistance, etc. [0003] Therefore, for the performance optimization of high-permeability PVC artificial leather, the performance is improved without affecting its permeability, and it has a good development prospect. Therefore, it is very necessary to prepare a high-permeability PVC artificial leather with high tensile strengt...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).
Invalid Date:Actual expiry date is based on effective date or publication date of legal transaction data of invalid patent.