Hydrophobic material for insulin syringe and its processing method

A technology of hydrophobic materials and syringes, applied in the field of medical materials, can solve the problems of increased workload and cost, waste of raw materials, etc., and achieve the effects of improving automation, saving raw materials, and improving heat resistance

Active Publication Date: 2021-12-28
PROMISEMED HANGZHOU MEDITECH
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] Injection molding is a method of producing industrial products. At present, when producing needle seats, protective sleeves, core rods and outer jackets of syringes, cold runner injection molding processes are usually used, and a large amount of syringes are processed by cold runner injection molding processes. waste, resulting in waste of raw materials, and after injection molding, robots or workers are required to separate the injection molded parts from the flow channel, which increases the workload and cost

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Hydrophobic material for insulin syringe and its processing method
  • Hydrophobic material for insulin syringe and its processing method
  • Hydrophobic material for insulin syringe and its processing method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0079] Embodiment 1: A kind of processing molding method of insulin syringe:

[0080] This embodiment provides a method for processing and molding hydrophobic materials for insulin syringes, including:

[0081] 1) Preparation of p-hydroxybenzoic acid modified starch:

[0082] 20kg of p-hydroxybenzoic acid was dissolved in 4L of distilled water to form a hydroxybenzoic acid solution, and the pH of the solution was adjusted to 3.5 with 1mol / L sodium hydroxide solution; 40kg of cornstarch (molecular weight 80000) was added to the p-hydroxybenzoic acid solution , ultrasonic (frequency is 20kW, power density is 0.3W / cm 2 ) for 40 minutes, left standing at room temperature for 14 hours, and then dried in a 60°C oven for 5 hours until the solid content was greater than 90%; then the product was ball milled for 20 minutes at a ball milling rate of 300r / min, and reacted at 130°C for 8 hours. The product was washed with deionized water to remove unreacted p-hydroxybenzoic acid, and dr...

Embodiment 2

[0095] Example 2: Another processing method for insulin syringes:

[0096] This example provides another method for processing and molding hydrophobic materials for insulin syringes. Its components and preparation methods are basically the same as in Example 1, except that in this example, in the process of preparing p-hydroxybenzoic acid modified starch , the addition amount of cornstarch and p-hydroxybenzoic acid were 40kg and 16kg respectively, and the degree of esterification of p-hydroxybenzoic acid modified starch was 0.08.

Embodiment 3

[0097] Example 3: Another processing method for insulin syringes:

[0098] This example provides another method for processing and molding hydrophobic materials for insulin syringes. Its components and preparation methods are basically the same as in Example 1, except that in this example, in the process of preparing p-hydroxybenzoic acid modified starch , the addition amount of cornstarch and p-hydroxybenzoic acid were 40kg and 24kg respectively, and the degree of esterification of p-hydroxybenzoic acid modified starch was 0.12.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
melt flow indexaaaaaaaaaa
breaking strengthaaaaaaaaaa
impact strengthaaaaaaaaaa
Login to View More

Abstract

The method belongs to the technical field of medical materials, and discloses a hydrophobic material for insulin syringes and a processing and molding method thereof. Polylactic acid is used as the main material, and p-hydroxybenzoic acid-modified starch, stearic acid-modified magnesium oxide, and titanic acid are added. The potassium whisker compound and the auxiliary agent are prepared by the hot runner injection molding process to prepare the insulin syringe. The process steps are simple and easy to realize, the production cycle is short, the degree of automation is improved, the prepared syringe has high transparency, can be completely degraded and the degradation rate is fast, Excellent mechanical properties, heat resistance and aging resistance.

Description

technical field [0001] The method belongs to the technical field of medical materials, and specifically relates to a hydrophobic material for an insulin syringe and a processing and molding method thereof. Background technique [0002] With the advancement of medical technology, medical operations are becoming more and more stringent, and injections are the basis of medical procedures, and most medical procedures require injections. At present, the syringe materials are mainly polypropylene, polyvinyl chloride, etc., which are low in cost and high in transparency. However, the toughness of polypropylene material is poor, especially at low temperature, which greatly limits the further application of polypropylene; PVC material itself is relatively hard, so it needs to add a large amount of plasticizer and other additives to make it It becomes soft and elastic, but when the infusion device made of modified polyvinyl chloride plastic comes into contact with the liquid medicine...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08L67/04C08L3/06C08K9/10C08K9/04C08K3/22C08K7/08
CPCC08L67/04C08L2201/10C08L2201/06C08L2201/08C08K2003/222C08K2201/011C08L3/06C08K9/10C08K9/04C08K3/22C08K7/08
Inventor 胡超宇鲁艳石家涵
Owner PROMISEMED HANGZHOU MEDITECH