Edible oil-resistant high-impact-resistant heat-resistant polycarbonate material and preparation method thereof
A polycarbonate, high-impact technology, used in the field of edible oil-resistant high-impact and heat-resistant polycarbonate materials and their preparation, can solve the failure of the 125°C heat-resistant ball pressure test, affect household and household appliances, and meet the It does not have problems such as the use environment, and achieves the effects of improving strength, improving impact resistance, and improving edible oil resistance.
Active Publication Date: 2021-06-18
GUANGDONG KUMHO SUNNY POLYMER MATERIAL
View PDF11 Cites 1 Cited by
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
[0003] Although polycarbonate has many of the above advantages, it is very sensitive to cooking oil and other oils. Once its parts come into contact with oil, it is prone to stress cracking, which seriously affects household and home appliances, such as switch panels, range hood panels and The safety of polycarbonate products such as oil boxes in the kitchen environment
[0004] In the prior art, PET-modified polycarbonate is used to improve the chemical resistance of polycarbonate. It needs to add a large proportion of PET to achieve the effect, which leads to a significant decrease in the heat resistance of the material, making PET-modified polycarbonate materials The 125°C heat-resistant ball pressure test failed, and could not meet the requirements of the use environment
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View moreImage
Smart Image Click on the blue labels to locate them in the text.
Smart ImageViewing Examples
Examples
Experimental program
Comparison scheme
Effect test
Embodiment Construction
[0031] The technical solutions of the present invention will be further described below in combination with specific embodiments.
[0032] Examples and comparative examples
[0033] The edible oil-resistant high-impact heat-resistant polycarbonate material of each embodiment and comparative example was prepared according to the following steps:
[0034] S1) Weigh polycarbonate, siloxane copolymerized polycarbonate, epoxy-modified silicon-acrylic acid copolymerized resin, antioxidant and lubricant according to parts by weight, place them in a mixer and mix them evenly to obtain a mixture ;
[0035] S2) The mixture obtained in S1) is sent into a twin-screw extruder through a metering device, and under the conveying, shearing and mixing of the screws, the materials are melted and mixed, melted and extruded, cooled and granulated to obtain the resistant Edible oil high impact heat resistant polycarbonate material. The temperature of the twin-screw extruder from the feeding port...
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More PUM
| Property | Measurement | Unit |
|---|---|---|
| melt flow index | aaaaa | aaaaa |
| melt flow index | aaaaa | aaaaa |
Login to View More
Abstract
The invention discloses an edible oil-resistant high-impact-resistant heat-resistant polycarbonate material and a preparation method thereof. The edible oil-resistant high-impact-resistant heat-resistant polycarbonate material comprises the following raw materials by weight: 67 to 97 parts of polycarbonate, 0 to 30 parts of siloxane copolymerized polycarbonate, 3 to 20 parts of epoxy modified silicon-acrylic acid copolymer resin, 0.1 to 1 part of an antioxidant, and 0.1-1 part of a lubricant. The edible oil-resistant high-impact-resistant heat-resistant polycarbonate material disclosed by the invention not only has good edible oil resistance, but also keeps relatively good impact resistance and heat resistance, and also has relatively low material cost. The invention further provides a preparation method of the edible oil-resistant high-impact-resistant heat-resistant polycarbonate material, and the preparation method is simple in process and has a good cost advantage.
Description
technical field [0001] The invention relates to the technical field of polymer materials, in particular to an edible oil-resistant high-impact and heat-resistant polycarbonate material and a preparation method thereof. Background technique [0002] Polycarbonate (PC) is an amorphous thermoplastic engineering plastic with excellent optical transparency, excellent impact toughness and heat resistance. It has been widely used in electronic appliances, home appliances, aerospace and other fields. [0003] Although polycarbonate has many of the above advantages, it is very sensitive to cooking oil and other oils. Once its parts come into contact with oil, it is prone to stress cracking, which seriously affects household and home appliances, such as switch panels, range hood panels and The safety of polycarbonate products such as oil boxes in the kitchen environment. [0004] In the prior art, PET-modified polycarbonate is used to improve the chemical resistance of polycarbonate....
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More Application Information
Patent Timeline
Login to View More Patent Type & Authority Applications(China)
IPC IPC(8): C08L69/00C08L83/06
CPCC08L69/00C08L2201/08C08L2205/025C08L2205/03C08L2201/10C08L83/06
Inventor 王敏查超单桂芳周霆辛敏强
Owner GUANGDONG KUMHO SUNNY POLYMER MATERIAL