A method for forming high-strength, formaldehyde-free plywood without adhesives and self-bonding

A formaldehyde release and self-adhesive technology, used in wood heating, wood processing details, can opening and dipping, etc., can solve the problem of inability to prepare self-adhesive plywood, and achieve wide application value, high mechanical strength, and good bonding effect. Effect

Active Publication Date: 2022-01-25
NORTHEAST FORESTRY UNIVERSITY
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] The present invention solves the problem that the prior art cannot prepare self-adhesive, high-strength, environmentally friendly, and highly stable plywood, and provides a method for forming high-strength, formaldehyde-free plywood without adhesives and self-adhesive

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A method for forming high-strength, formaldehyde-free plywood without adhesives and self-bonding
  • A method for forming high-strength, formaldehyde-free plywood without adhesives and self-bonding
  • A method for forming high-strength, formaldehyde-free plywood without adhesives and self-bonding

Examples

Experimental program
Comparison scheme
Effect test

specific Embodiment approach 1

[0035] Specific embodiment one: the present embodiment is a kind of non-adhesive, self-adhesive to form the method for high-strength, formaldehyde-free plywood, and it is carried out according to the following steps:

[0036] 1. Cleaning:

[0037] Soak the wood in distilled water or ethanol solution, ultrasonically clean it for 1h-3h, and then vacuum-dry it for 1h-24h at a temperature of 60°C-180°C to obtain the cleaned wood;

[0038] The thickness of the wood is 0.5 mm to 2.5 mm;

[0039] 2. Dehemicellulose:

[0040] Soak the cleaned wood in the dehemicellulose solution, heat it in a water bath at a temperature of 60°C to 90°C for 2h to 10h, and then soak it in deionized water at a temperature of 20°C to 30°C 1h to 3h, and repeated soaking 2 to 4 times to obtain dehemicellulose-defiberized wood;

[0041] The mass percent of the dehemicellulose solution is 1% to 30%;

[0042] 3. Delignification:

[0043] Soak the dehemicellulosed wood in the delignification solution, heat...

specific Embodiment approach 2

[0058] Embodiment 2: This embodiment is different from Embodiment 1 in that the wood described in step 1 is coniferous or broad-leaved. Others are the same as in the first embodiment.

specific Embodiment approach 3

[0059] Specific embodiment three: the difference between this embodiment and specific embodiment one or two is that the dehemicellulose solution described in step 2 is a mixed solution of sodium hydroxide and sodium sulfite, sodium hypochlorite solution, sodium sulfite solution or anthraquinone solution. Others are the same as in the first or second embodiment.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
densityaaaaaaaaaa
tensile strengthaaaaaaaaaa
Login to View More

Abstract

The invention discloses a method for forming high-strength and formaldehyde-free plywood without adhesive and self-bonding, which relates to a method for forming plywood without adhesive and self-bonding. The invention aims to solve the problem that the prior art cannot prepare plywood with self-bonding, high strength, environmental friendliness and strong stability. Preparation method: 1. cleaning; 2. hemicellulose removal; 3. delignification; 4. activation treatment; 5. dissolution treatment; 6. regeneration treatment. The invention is a method for forming high-strength and formaldehyde-free plywood without adhesives and self-bonding.

Description

technical field [0001] The invention relates to a method for forming plywood without adhesive and self-adhesive. Background technique [0002] With the rapid development of engineering construction and furniture decoration industry, the demand for wood has increased sharply, and the development of wood-based panel industry is the main way to improve wood utilization and save wood resources. Wood-based panels are boards or molded products made of wood or other non-wood plants as raw materials, separated by mechanical processing, and with or without adding chemical adhesives. The number of its extended products is as high as hundreds, mainly including three major categories of products: plywood, shaving (chip) board and fiberboard. [0003] Plywood is made by peeling wood sections into veneers or sliced ​​into thin wood chips, and then glued together with adhesives. In order to reduce the anisotropic characteristics of wood, the plywood has uniform characteristics and stable ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B27K3/04B27K3/08B27K5/00B27K5/04
CPCB27K3/04B27K5/001B27K3/08B27K5/04
Inventor 甘文涛董晓菲唐剑夫尚莹王耀星李连震李坚
Owner NORTHEAST FORESTRY UNIVERSITY