Rubber recycled concrete and preparation method thereof

A technology for recycled concrete and rubber, which is applied in sustainable waste treatment, solid waste management, climate sustainability, etc., and can solve problems such as weak bonding ability, low elastic modulus of rubber powder, and reduced strength

Inactive Publication Date: 2021-07-06
WUHAN INSTITUTE OF TECHNOLOGY
View PDF3 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, rubber powder is a hydrophobic material, which makes it weak in bonding ability with cement and other cementitious materials, and cannot form a good bonding interface. Moreover, the elastic modulus of rubber powder

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0035] The mass ratio of each raw material of rubber recycled concrete is cement: natural coarse aggregate: recycled coarse aggregate: natural fine aggregate: recycled fine aggregate: water: rubber powder: nano silicon dioxide: polycarboxylate superplasticizer=1: 2.05:0.88:1.089:0.47:0.46:0.011:0.005:0.015, the water-binder ratio of the rubber recycled concrete is 1:2.17.

[0036] Concretely, the preparation method of above-mentioned rubber recycled concrete comprises the following steps:

[0037] Step 1: Quantitative weighing, weighing all the required raw materials according to the corresponding mixing ratio.

[0038] Step 2: adding natural fine aggregate, recycled fine aggregate and rubber powder into the collecting pan and stirring evenly to form mixture A;

[0039] Step 3: adding natural coarse aggregate and recycled coarse aggregate to the collecting pan and stirring evenly to form mixture B;

[0040] Step 4: Add polycarboxylate superplasticizer and water into the aggr...

Embodiment 2

[0046] The mass ratio of each raw material of rubber recycled concrete is cement: natural coarse aggregate: recycled coarse aggregate: natural fine aggregate: recycled fine aggregate: water: rubber powder: nano silicon dioxide: polycarboxylate superplasticizer=1: 2.08:0.88:1.089:0.48:0.47:0.011:0.015:0.017, the water-binder ratio of the rubber recycled concrete is 1:2.17.

[0047] Specifically, the preparation method of the above-mentioned rubber recycled concrete includes the following steps.

[0048] S1: Quantitative weighing, weighing all the required raw materials according to the corresponding mixing ratio.

[0049] Step 2: adding natural fine aggregate, recycled fine aggregate and rubber powder into the collecting pan and stirring evenly to form mixture A;

[0050] Step 3: adding natural coarse aggregate and recycled coarse aggregate to the collecting pan and stirring evenly to form mixture B;

[0051] Step 4: Add polycarboxylate superplasticizer and water into the agg...

Embodiment 3

[0057] The mass ratio of each raw material of this rubber recycled concrete is cement: natural coarse aggregate: recycled coarse aggregate: natural fine aggregate: recycled fine aggregate: water: rubber powder: nano silicon dioxide: polycarboxylate water reducer=1 :2.12:0.88:1.089:0.47:0.46:0.011:0.031:0.025, the water-binder ratio of the rubber recycled concrete is 1:2.17.

[0058] Specifically, the preparation method of the above-mentioned rubber recycled concrete includes the following steps.

[0059] S1: Quantitative weighing, weighing all the required raw materials according to the corresponding mixing ratio.

[0060] Step 2: adding natural fine aggregate, recycled fine aggregate and rubber powder into the collecting pan and stirring evenly to form mixture A;

[0061] Step 3: adding natural coarse aggregate and recycled coarse aggregate to the collecting pan and stirring evenly to form mixture B;

[0062] Step 4: Add polycarboxylate superplasticizer and water into the a...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Slumpaaaaaaaaaa
Compressive strengthaaaaaaaaaa
Slumpaaaaaaaaaa
Login to view more

Abstract

The invention relates to rubber recycled concrete and a preparation method thereof. The mass ratio of cement to natural coarse aggregate to recycled coarse aggregate to natural fine aggregate to recycled fine aggregate to water to rubber powder to nano silicon dioxide to a polycarboxylic acid water reducing agent is 1: (2.03-2.12): (0.87-0.91): (1.04-1.14): (0.47-0.49): (0.46-0.52): (0.011-0.057): (0.005-0.031): (0.011-0.026), the water-binder ratio of the rubber recycled concrete is 1: (2-2.17), the recycled fine aggregate and the recycled coarse aggregate are waste gas concrete, the natural fine aggregate is natural river sand, the natural coarse aggregate is limestone gravel, the particle size of the recycled fine aggregate is 0.075-4.75 mm, the particle size of the recycled coarse aggregate is 5-20 mm, the particle size of the natural fine aggregate is 0.075-4.75 mm, and the particle size of the natural coarse aggregate is 5-25 mm. According to the rubber recycled concrete disclosed by the invention, waste gas concrete and rubber can be utilized, the rubber recycled concrete has excellent mechanical properties, and the problem of poor compression resistance of recycled concrete in the prior art is solved.

Description

technical field [0001] The invention belongs to the technical field of recycled concrete preparation, and in particular relates to a rubber recycled concrete and a preparation method thereof. Background technique [0002] With the development of the automobile industry, a large number of waste rubber tires have been produced. According to statistics, more than 50 million waste rubber tires are produced in my country every year, and only a small part of waste tires are processed every year. A large number of untreated waste tires will bring huge environmental problems. With the in-depth advancement of industrialization and urbanization, the construction industry is developing rapidly, the amount of construction waste is increasing, and the consumption of resources is further accelerating. According to statistics, my country's urban construction waste accounts for 60% to 70% of the total construction waste. The total amount of construction waste accounts for 30% to 40% of th...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C04B28/04C04B18/16C04B18/22C04B14/06
CPCC04B28/04C04B18/16C04B18/22C04B14/06C04B2111/00008C04B2201/50C04B14/068C04B18/12C04B2103/302Y02W30/91
Inventor 陈旭勇程子扬詹旭吴巧云屠艳平
Owner WUHAN INSTITUTE OF TECHNOLOGY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap