Ceramic glazed tile surface anti-slip agent and preparation method thereof

A technology of ceramic glaze and anti-slip agent, which is applied in the direction of anti-fouling/underwater coating, paint containing biocide, coating, etc. It can solve the problems of difficult cleaning and easy wear of anti-slip agent, so as to improve the anti-slip ability and increase the Friction coefficient, effect of increasing friction

Active Publication Date: 2021-08-20
上海世卿防滑防护科技有限公司
View PDF8 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] In order to solve the problem that the existing anti-slip agent is easy to be worn after long-term use, and the uneven structure on the surface of the brick body is not easy to clean, the invention provides an anti-slip agent on the surface of ceramic glazed tiles and a preparation method thereof, so that the anti-slip agent and The surface of ceramic glazed tiles is effectively combined to play a good anti-slip effect and has a good sterilization effect at the same time

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Ceramic glazed tile surface anti-slip agent and preparation method thereof
  • Ceramic glazed tile surface anti-slip agent and preparation method thereof
  • Ceramic glazed tile surface anti-slip agent and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0013] This embodiment provides an anti-slip agent for the surface of ceramic glazed tiles, and the anti-slip agent is applied on the glaze layer of the ceramic glazed tiles.

[0014] A surface anti-slip agent for ceramic glazed tiles, composed of a solvent, particles dispersed in the solvent, and a dispersant, auxiliary agent, surfactant and fluoride salt dissolved in the solvent;

[0015] Wherein, the parts by weight of each component are: 4 parts of granule, 2 parts of dispersant, 2 parts of auxiliary agent, 13 parts of surfactant, 14 parts of fluoride salt, and the balance is solvent.

[0016] Wherein, the solvent is water, the particles are nano titanium dioxide, the dispersant is polyvinyl alcohol, the auxiliary agent is a mixture of silicon dioxide and triethanolamine, and the fluoride salt is potassium fluoride.

[0017] Wherein, the preparation method of tensio-active agent is:

[0018] S1: Add 150mL low-hydrogen silicone oil and 100mL trans-3-pentenoic acid into the...

Embodiment 2

[0038] This embodiment provides an anti-slip agent for the surface of ceramic glazed tiles, and the anti-slip agent is applied on the glaze layer of the ceramic glazed tiles.

[0039] A surface anti-slip agent for ceramic glazed tiles, composed of a solvent, particles dispersed in the solvent, and a dispersant, auxiliary agent, surfactant and fluoride salt dissolved in the solvent;

[0040] Wherein, the parts by weight of each component are: 10 parts of granule, 7 parts of dispersant, 9 parts of auxiliary agent, 21 parts of surfactant, 22 parts of fluoride salt, and the balance is solvent.

[0041] Wherein, the solvent is water, the particle is nano titanium dioxide, the dispersant is sodium polyacrylate and ethyl acetate, the auxiliary agent is a mixture of silicon dioxide and triethanolamine, and the fluoride salt is potassium fluoride.

[0042] Wherein, the preparation method of tensio-active agent is:

[0043] S1: Add 150mL low-hydrogen silicone oil and 100mL trans-3-pent...

Embodiment 3

[0058] This embodiment provides an anti-slip agent for the surface of ceramic glazed tiles, and the anti-slip agent is applied on the glaze layer of the ceramic glazed tiles.

[0059] A surface anti-slip agent for ceramic glazed tiles, composed of a solvent, particles dispersed in the solvent, and a dispersant, auxiliary agent, surfactant and fluoride salt dissolved in the solvent;

[0060] Wherein, the parts by weight of each component are: 4 parts of granule, 2 parts of dispersant, 2 parts of auxiliary agent, 13 parts of surfactant, 14 parts of fluoride salt, and the balance is solvent.

[0061] Wherein, the solvent is water, the particles are nano titanium dioxide, the dispersant is diethylene glycol dimethyl ether, the auxiliary agent is a mixture of silicon dioxide and triethanolamine, and the fluoride salt is potassium fluoride.

[0062] Wherein, the preparation method of tensio-active agent is:

[0063] S1: Add 150mL low-hydrogen silicone oil and 100mL trans-3-pentenoi...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention belongs to the technical field of anti-slip materials, and particularly relates to a ceramic glazed tile surface anti-slip agent and a preparation method thereof. The ceramic glazed tile surface anti-slip agent is composed of a solvent, and particles, a dispersing agent, an auxiliary agent, a surfactant and a fluoride salt which are dissolved in the solvent, the solvent is water, the particles are nanometer titanium dioxide, the dispersing agent is one or a mixture of more of polyvinyl alcohol, sodium polyacrylate, ethyl acetate and diethylene glycol dimethyl ether, the auxiliary agent is a mixture of silicon dioxide and triethanolamine, and the fluoride salt is potassium fluoride. After being treated by the anti-slip agent prepared by the invention, the anti-slip agent is effectively combined with the surface of the ceramic glazed tile, so that a good anti-slip effect is achieved, and meanwhile, a good sterilization effect is achieved.

Description

technical field [0001] The invention relates to the technical field of anti-slip materials, in particular to a surface anti-slip agent for ceramic glazed tiles and a preparation method thereof. Background technique [0002] With the improvement of the production technology of ceramic floor tiles, people welcome them because of their better decorative effects, but the surface of these products is very smooth. At present, anti-slip tiles are mainly applied on the brick body by applying anti-slip agents, corrosive agents or high-temperature printing glazes. The surface has an uneven structure, but the applied anti-slip layer will be gradually worn out with the prolongation of use time, thus losing the anti-slip effect. The integrity and decorative effect of the glaze layer on the surface of the tiles, and the lines are not easy to clean, and long-term use will cause harm to people's health. Therefore, it is very necessary to develop floor tiles that are environmentally friendly...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D5/14C09D7/61C09D7/63C09D7/65
CPCC09D5/14C09D7/61C09D7/63C09D7/65
Inventor 王永生
Owner 上海世卿防滑防护科技有限公司