Environment-friendly smokeless burning incense and preparation method thereof
An environmentally friendly, incense-burning technology, which is applied in the direction of floor fabrics, household utensils, religious or ceremonial utensils, etc., can solve the problem of harming human health, difficulty in satisfying consumers' pursuit of incense burning aesthetics, and products that do not meet the requirements of burning incense To achieve the effect of good adjustability by addressing issues such as safety and general technical conditions and index requirements
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Example Embodiment
[0020] Example 1, the present invention has an environmentally friendly smokeless ignorant, in the preparation:
[0021] 1 Preparation of powder mixture by weight, the raw material includes 12% of the cypress powder, 25% of the plant binder, 7% silicon compound, 1% magnesium hydroxide, 2% hydroxide, 1% iron oxide, will Plant binders are ground to 80-200 mesh, and the remaining raw materials are ground to 200-500 purposes;
[0022] 2 Mix the raw material in step 1 and form a powder mixture;
[0023] 3 Preparation of aqueous solution in weight, the raw material comprises 2% of potassium nitrate, 1% sodium bicarbonate, 49% water; potassium nitrate and sodium bicarbonate dissolve and stir well, form aqueous solution;
[0024] 4 Stirring the powder mixture with aqueous solution in a mixer for 15 minutes to form a soft block shape;
[0025] 5 Extruded the blockage of the block, dry and pack.
[0026] Burning experiments of the refined fragrance of the present invention: Take 10 forming ...
Example Embodiment
[0027] Example 2, the present invention has an environmentally friendly smokeless osmic flavor, in the preparation:
[0028] 1 Preparation of powder mixture by weight, the raw material includes 10% of the mucuofan, 18% of the plant binder, 6% silicon compound, 2% magnesium hydroxide, 3% aluminum hydroxide, 1.5% iron oxide, The plant binder was ground to 80-200 mesh, and the remaining raw materials were ground to 200-500 mesh;
[0029] 2 Mix the raw material in step 1 and form a powder mixture;
[0030] 3 Aqueous solution is prepared by weight percent, the raw material comprises 3% podium nitrate, 1.5% sodium bicarbonate, 55% water; potassium nitrate and sodium bicarbonate dissolves and stir well, and form aqueous solution;
[0031] 4 Stirring the powder mixture with aqueous solution into the mixer for 20 minutes to form a soft block shape;
[0032] 5 Extruded the blockage of the block, dry and pack.
[0033] Burning experiments in the form of the invention: Take 10 forming fragran...
Example Embodiment
[0034] Example 3, the present invention has an environmentally friendly smokeless flavor, in the preparation:
[0035] 1 Preparation of powder mixture by weight, the raw materials include: 18% incexic powder, plant adhesive, 8%, silicon compound 2%, 2% hydroxide, and 1% iron oxide, The plant binder was ground to 80-200 mesh, and the remaining raw materials were ground to 200-500 mesh;
[0036] 2 Mix the raw material in step 1 and form a powder mixture;
[0037] 3 Aqueous solution was prepared according to the weight percent, the raw material comprised 2.5% nitrate, 0.5% sodium bicarbonate, 44% water; potassium nitrate and sodium bicarbonate were dissolved and stirred evenly, and formed aqueous solution;
[0038] 4 Stirring the powder mixture with aqueous solution into the mixer for 20 minutes to form a soft block shape;
[0039] 5 Extruded the blockage of the block, dry and pack.
[0040] Burning experiments in the present invention: 10-forming fragrant lighting and observing the ...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap