A heating and wear-resistant carpet and its preparation method
What is Al technical title?
Al technical title is built by PatSnap Al team. It summarizes the technical point description of the patent document.
A carpet and acetate fiber technology, applied in the direction of carpet, rayon manufacturing, rayon filament made of cellulose derivatives, etc., can solve the problems of decreased thermal insulation performance and poor wear resistance.
Active Publication Date: 2021-11-02
南通铭源纺织有限公司
View PDF5 Cites 0 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
[0003] With the development of human beings, carpets made of cotton and linen can only meet the general needs of people's lives, but they often have poor wear resistance and can only achieve heat insulation performance. If they are used for a long time, the heat insulation performance will also decrease.
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Examples
Experimental program
Comparison scheme
Effect test
Embodiment 1
[0032] A heating and wear-resistant carpet, mainly comprising:
[0033] 10 parts of film, 10 parts of textile fabric.
[0034] A method for preparing a heating and wear-resistant carpet, the preparation method of the heating and wear-resistant carpet is:
[0035] (1) Add tetraacicular nano-zinc oxide to an anhydrous ethanol solution that is 4 times the mass of tetraacicular nano-zinc oxide, add lauric acid that is 0.02 times the mass of tetraacicular nano-zinc oxide, and stir at room temperature at 400rpm for 12h Finally, centrifuge to remove the lower layer of mud, add absolute ethanol to the mud again to wash and centrifuge again, repeat washing and centrifugation for 3 times, dry the centrifuged product in an oven at 80°C for 1 hour, grind and pass through a 100-mesh sieve, Prepare modified zinc oxide;
[0036] (2) Put the nitrile rubber and modified zinc oxide into the internal mixer according to the mass ratio of 200:1. After mixing for 5 minutes, add a plasticizer 0.00...
Embodiment 2
[0047] A heating and wear-resistant carpet, mainly comprising:
[0048] 20 parts of film, 20 parts of textile fabric.
[0049] A method for preparing a heating and wear-resistant carpet, the preparation method of the heating and wear-resistant carpet is:
[0050] (1) Add tetraacicular nano-zinc oxide to an anhydrous ethanol solution that is 4 times the mass of tetraacicular nano-zinc oxide, add lauric acid that is 0.02 times the mass of tetraacicular nano-zinc oxide, and stir at room temperature at 800rpm for 12h Finally, centrifuge to remove the lower layer of mud, add absolute ethanol to the mud again to wash and centrifuge again, repeat washing and centrifugation for 3 times, dry the centrifuged product in an oven at 80°C for 2 hours, grind and pass through a 100-mesh sieve, Prepare modified zinc oxide;
[0051] (2) Put the nitrile rubber and modified zinc oxide into the internal mixer according to the mass ratio of 240:1. After mixing for 7 minutes, add a plasticizer 0.0...
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
PUM
Login to view more
Abstract
The invention discloses a heating and wear-resistant carpet and a preparation method thereof, and relates to the technical field of carpet production. When the present invention prepares heat-generating and wear-resistant carpets, it is formed by pressing a film and a textile fabric, the film is nitrile rubber, and the textile fabric is woven from modified acetate fiber; the film is prepared by blending modified zinc oxide with nitrile rubber, It can not only eliminate stress concentration, enhance the wear resistance of nitrile rubber, but also vulcanize the rubber, increase the cross-linking density, and further enhance the wear resistance of nitrile rubber; branched to acetate fiber, and then aminated to prevent the carpet from easily absorbing water molecules in the air, thereby hindering the heating of the carpet; when pressed with the film, the amino group on the surface of the textile fabric will react with the lauric acid in the film, making the film and textile The fabrics are tightly connected; the heating and wear-resistant carpet prepared by the invention not only has good wear resistance, but also can feel temperature changes faster when heating.
Description
technical field [0001] The invention relates to the technical field of carpet production, in particular to a heating and wear-resistant carpet and a preparation method thereof. Background technique [0002] Carpet is generally a floor covering made of natural fibers such as cotton, hemp, silk, wool, or chemical synthetic fibers, which are braided, tufted, or woven by hand or mechanical processes. It is one of the traditional arts and crafts categories with a long history in the world. [0003] With the development of human beings, carpets made of cotton and linen can only meet the general needs of people's lives, but they often have poor wear resistance and can only achieve heat insulation performance. If they are used for a long time, the heat insulation performance will also decrease. Therefore, it is very promising to research and invent a kind of carpet that can generate heat and be wear-resistant. The present invention applies for research and preparation of a heating...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).