PVB (polyvinyl butyral) film as well as preparation method and application thereof

A film and antioxidant technology, used in chemical instruments and methods, adhesives, adhesive additives, etc., can solve the problems of inability to achieve high ultraviolet transmittance, reduce ultraviolet transmittance, etc., and achieve high light stability and thermal oxygen stability. , Excellent UV transmittance, high light transmittance

Pending Publication Date: 2021-11-05
建滔(佛冈)特种树脂有限公司
View PDF2 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the addition of UV absorbers will greatly reduce the transmittance of ultraviolet rays, and cannot achieve the effect of high UV transmittance. Therefore, in order to obtain high ultraviolet (UV) film, it is necessary to solve the negative impact of ultraviolet rays on the film after it passes through the film.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • PVB (polyvinyl butyral) film as well as preparation method and application thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0032] Specific steps are as follows:

[0033] 1) Plasticizer mixing: Dissolve free radical scavenger, antioxidant and quencher in plasticizer; mix 20g 770, 10g 1010, 10g168, 5g bis(3,5-di-tert-butyl-4 -Hydroxybenzyl phosphate monoethyl ester) Nickel is dissolved in 2.4kg triethylene glycol diisocaprylate (plasticizer), the temperature of heating and dissolving is 70°C, after complete dissolution, add 3g silane coupling agent and stir evenly, keep warm 60min standby.

[0034] 2) Mix and extrude the PVB resin powder and the plasticizer prepared in step 1) according to the mass ratio of 71:29, process, melt and plasticize, pass through the mold, make PVB film, cool and shape, and obtain the finished product.

Embodiment 2

[0036] Specific steps are as follows:

[0037]1) Plasticizer mixing: Dissolve free radical scavenger, antioxidant and quencher in plasticizer; mix 20g 770, 10g 1010, 10g168, 5g 2,2'-thiobis(4-tert Butylphenoxy)nickel was dissolved in 2.4kg of triethylene glycol diisocaprylate (plasticizer), and the temperature for heating and dissolving was 70°C. After complete dissolution, 3g of silane coupling agent was added and stirred evenly, and kept warm for 60 minutes for later use.

[0038] 2) Mix and extrude the PVB resin powder and the plasticizer prepared in step 1) according to the mass ratio of 71:29, process, melt and plasticize, pass through the mold, make PVB film, cool and shape, and obtain the finished product.

Embodiment 3

[0040] Specific steps are as follows:

[0041] 1) Plasticizer mixing: Dissolve free radical scavenger, antioxidant and quencher in plasticizer; 20g GW-540, 10g 1010, 10g168, 5g 2,2'-thiobis(4 - tert-butylphenoxy)nickel was dissolved in 2.4kg triethylene glycol diisocaprylate (plasticizer), and the temperature of heating and dissolving was 70°C. After it was completely dissolved, add 3g of silane coupling agent and stir evenly, and keep warm for 60min spare.

[0042] 2) Mix and extrude the PVB resin powder and the plasticizer prepared in step 1) according to the mass ratio of 71:29, process, melt and plasticize, pass through the mold, make PVB film, cool and shape, and obtain the finished product.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a PVB (Polyvinyl Butyral) film as well as a preparation method and application thereof. The PVB film comprises the following components: PVB resin, a plasticizer, an antioxidant, a quenching agent and a free radical scavenger. The PVB film prepared by the invention has good adhesion to glass, high ultraviolet transmittance, high light transmittance and strong aging resistance under the condition of not absorbing ultraviolet rays.

Description

technical field [0001] The invention relates to the technical field of polyvinyl butyral (PVB) materials, in particular to a PVB film and its preparation method and application. Background technique [0002] In recent years, with the rapid development of construction and automobile industries, PVB film is also called PVB film or PVB interlayer. It is the best material for making laminated safety glass in the world today. PVB film is made of PVB resin. The resin is non-toxic, odorless, non-corrosive, not easy to burn, and has good light transmission, insulation, weather resistance, wear resistance, water resistance, oil resistance, and aging resistance. Plexiglass has special adhesion and light transmission properties. Therefore, PVB films with high strength and moisture resistance can be widely used in automobiles, buildings, various bulletproof glasses, aerospace vehicles, military instruments, solar cells, composite shock-absorbing steel plates for industry, etc., and ha...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C09J129/14C09J11/06C03C27/12B32B17/06B32B17/00B32B7/12
CPCC09J129/14C09J11/06C03C27/10B32B17/06B32B17/00B32B7/12C08K5/0091C08K5/103
Inventor 林家宝
Owner 建滔(佛冈)特种树脂有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap