Wear-resistant high-pressure-resistant special-shaped PC bucket and production method thereof

A special-shaped, water-bucket technology, which is applied in the wear-resistant and high-pressure-resistant special-shaped PC water bucket and its production field, can solve the problems of reducing the aesthetics of the bucket, reducing the service life of the bucket, and poor wear resistance, so as to improve the anti-oxidation performance and reduce the Aging speed, the effect of not easy to crack

Pending Publication Date: 2021-12-14
QINGYUAN JINGKEXIN PLASTIC PROD CO LTD
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] PC material is often used to produce buckets, but its wear resistance is not good, and it is prone to scratches during use, which reduces the aesthetics of the bucket. At the same time, the PC bucket in the prior art has poor compressive performance. It is prone to cracking during the process, reducing the service life of the bucket

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Wear-resistant high-pressure-resistant special-shaped PC bucket and production method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0028] like figure 1 According to the present invention, a wear-resistant high-pressure shaped PC bucket includes 90 copies of the following weight: 10 parts of the polycarbonate, 10 parts of acrylonitrile - styrene copolymer, 5 parts of glass, 5 parts of the wear, acrylic acid 5 parts of vinegar, 1 toughening agent, 5 antioxidants, 3 anti-aging agents, 1 stabilizer, 0.2 parts of coupling agent and 2 lubricants.

[0029] In the present embodiment, the glass fibers use the alkali-free glass fiber, the alkali-free glass fibers can be well fused with polycarbonate, so that the shaped PC bucket has a higher impact strength, better mechanical strength, Significantly improve the pressure resistance.

[0030] In the present embodiment, the abrasive agent uses a polyether modified silicone oil, an amino modified silicone oil, an epoxy modified silicone oil and a silicone-acrylate copolymer, and is capable of goodness with polycarbonate by the wear resistant. The compatibility can effectiv...

Embodiment 2

[0043] like figure 1 According to the present invention, there is a wear-resistant high-pressure shaped PC bucket comprising 100 parts of the following weight: 100 parts of polycarbonate, 30 parts of acrylonitrile - styrene copolymer, 15 parts of glass fiber, 15 wear-resistant, acrylic acid 20 parts of vinegar, 5 parts of toughening agent, 10 antioxidants, 5 parts of anti-aging agent, 3 stabilizers, 1 part of the coupling agent and 5 parts of lubricant.

[0044] In the present embodiment, the glass fibers use the alkali-free glass fiber, the alkali-free glass fibers can be well fused with polycarbonate, so that the shaped PC bucket has a higher impact strength, better mechanical strength, Significantly improve the pressure resistance.

[0045] In the present embodiment, the abrasive agent uses a polyether modified silicone oil, an amino modified silicone oil, an epoxy modified silicone oil and a silicone-acrylate copolymer, and is capable of goodness with polycarbonate by the wear...

Embodiment 3

[0058] like figure 1 According to the present invention, a wear-resistant high-pressure shaped PC bucket includes 95 parts of the following weight ratio, 20 parts of polycarbonitrile, 20 parts of acrylonitrile, 10 parts of glass fiber, 10 wear-resistant, acrylic acid 13 parts of vinegar, 3 toughening agents, 7 antioxidants, 4 parts of anti-aging agent, 2 stabilizers, 0.6 parts of coupling agent and 3 parts of lubricant.

[0059] In the present embodiment, the glass fibers use the alkali-free glass fiber, the alkali-free glass fibers can be well fused with polycarbonate, so that the shaped PC bucket has a higher impact strength, better mechanical strength, Significantly improve the pressure resistance.

[0060] In the present embodiment, the abrasive agent uses a polyether modified silicone oil, an amino modified silicone oil, an epoxy modified silicone oil and a silicone-acrylate copolymer, and is capable of goodness with polycarbonate by the wear resistant. The compatibility can ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention belongs to the technical field of PC bucket production, and particularly relates to a wear-resistant high-pressure-resistant special-shaped PC bucket and a production method thereof. The bucket comprises the following raw materials in parts by weight: 90-100 parts of polycarbonate, 10-30 parts of an acrylonitrile-styrene copolymer, 5-15 parts of glass fibers, 5-15 parts of a wear-resistant agent, 5-20 parts of an acrylate copolymer, 1-5 parts of a flexibilizer, 5-10 parts of an antioxidant, 3-5 parts of an anti-aging agent, 1-3 parts of a stabilizer, 0.2-1 part of a coupling agent and 2-5 parts of a lubricant. According to the special-shaped PC bucket, the produced special-shaped PC bucket has good wear resistance through the wear-resistant agent, the phenomenon of scratching is not prone to occurring in a using process, and the attractiveness of the special-shaped PC bucket can be guaranteed; and since the acrylonitrile-styrene copolymer and the glass fiber are well compatible with polycarbonate, the produced special-shaped PC bucket shows good pressure resistance, flexibility and rigidity, can bear large pressure and is not prone to cracking, and the pressure resistance of the special-shaped PC bucket is remarkably improved.

Description

Technical field [0001] The present invention relates to the field of PC bucket production techniques, in particular a wear-resistant high-pressure shaped PC bucket and its production methods. Background technique [0002] The PC is a brief agreed with polycarbonate, and the polycarbonate is Polycarbonate, referred to as PC engineering plastics. PC is an uncompletex thermoplastic resin with excellent performance, with excellent electrical insulation, elongation, dimensional stability and chemical resistance, heat resistance and cold resistance; also has self-extinguishing, flame retardant, non-toxic , Can be coloring and other advantages. [0003] PC material is often used to produce water buckets, but its wear resistance is poor, and the process of use is prone to scratch, it reduces the beauty of the bucket, and the pressure-resistant performance in the prior art is poor, in use The process of cracking occurs during the process, reducing the service life of the bucket. Inventiv...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L69/00C08L33/20C08L83/12C08L83/08C08L83/06C08L43/04C08L33/04C08L51/04C08K13/04C08K7/14C08K5/13C08K5/29C08K5/527
CPCC08L69/00C08L2201/08C08L33/20C08L83/12C08L83/08C08L83/06C08L43/04C08L33/04C08L51/04C08K13/04C08K7/14C08K5/13C08K5/29C08K5/527
Inventor 戴碧光
Owner QINGYUAN JINGKEXIN PLASTIC PROD CO LTD
Features
  • R&D
  • Intellectual Property
  • Life Sciences
  • Materials
  • Tech Scout
Why Patsnap Eureka
  • Unparalleled Data Quality
  • Higher Quality Content
  • 60% Fewer Hallucinations
Social media
Patsnap Eureka Blog
Learn More

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2025 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com