Micro-crystal color art coating as well as preparation method and application thereof

A kind of art paint and microcrystalline technology, applied in the direction of coating, etc., can solve the problems of not being covered, not crossing and blending, single hue, etc., achieving the effect of fine gloss, fine texture, and reducing construction time

Pending Publication Date: 2022-02-08
厦门富思特新材料科技有限公司
View PDF2 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The purpose of the present invention is to provide a kind of microcrystalline color art paint in order to overcome the single hue problem that existing art paint exists, adopt base paint as the dispersing matrix of colorant, the colorant of different colors can be dispersed into microparticles, and then Basically, the granulation gel solution is used to form an external package for the dispersed color particles, and at the same time ensure that the color of the color particles is not covered, no cross-color and fusion, and a stable and uniform dispersion system is formed after the color dots are granulated. Under the action of outsourcing varnish, it forms a good adhesion effect with the wall, and can be sprayed at one time, without pre-treatment such as scraping putty layer, and post-treatment such as polishing the surface, which greatly facilitates construction

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Micro-crystal color art coating as well as preparation method and application thereof
  • Micro-crystal color art coating as well as preparation method and application thereof
  • Micro-crystal color art coating as well as preparation method and application thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0068] Prepare microcrystalline color paint, raw material consumption is as follows:

[0069] Granulating glue solution: base paint: thickener: outsourcing varnish mass ratio = 18:65:2:15, wherein, the composition of the mass fractions of each component of the base paint is as follows, and the total of each component is 100%:

[0070]

[0071] Use the above-mentioned base paint to disperse the coloring material to obtain the color base paint. The specific ratio is as follows:

[0072] Color ratio of yellow base paint

[0073]

[0074] Red base paint color ratio

[0075] Base paint 99.3%

[0076] Iron oxide red 0.69%

[0077] Carbon black 0.01%.

[0078] The mass ratios of the 2 colored dots determined in this embodiment are shown in Table 1:

[0079] Table 1 Example 1 color point mass ratio table

[0080] tinted base paint yellow base paint red base paint Mass ratio 0.9 0.1

[0081] That is to say, the yellow base paint and the red base pa...

Embodiment 2

[0095] Prepare microcrystalline color paint, raw material consumption is as follows:

[0096] Granulating glue solution: base paint: thickener: mass ratio of outsourcing varnish = 18:65:2:15, where

[0097] The mass fraction of each component of the base paint is composed as follows, and the total of each component is 100%:

[0098]

[0099]

[0100] Use the above-mentioned base paint to disperse the coloring material to obtain the color base paint. The specific ratio is as follows:

[0101] Light red base paint color ratio:

[0102] Base paint 99.7%

[0103] Iron Oxide Red 0.3%

[0104] Crimson base paint color ratio:

[0105] Base paint 98.65%

[0106] Iron Oxide Red 1.35%

[0107] Ratio of brown base paint:

[0108]

[0109] The 3 colored dot mass ratios determined in this embodiment are shown in Table 2:

[0110] Table 2 Example 2 color point mass ratio table

[0111] tinted base paint light red base paint dark red base paint Brown base pa...

Embodiment 3

[0124] Prepare microcrystalline color paint, raw material consumption is as follows:

[0125] Granulating glue solution: base paint: thickener: mass ratio of outsourcing varnish = 18:65:2:15, where

[0126] The mass fraction of each component of the base paint is composed as follows, and the total of each component is 100%:

[0127]

[0128] Use the above-mentioned base paint to disperse the coloring material to obtain the color base paint. The specific ratio is as follows:

[0129] Color ratio of beige base paint:

[0130] Base paint 99.98%

[0131] Blush blue 0.02%

[0132] Light gray base paint color ratio:

[0133] Base paint 99.7%

[0134] Carbon black 0.28%

[0135] Blush blue 0.02%

[0136] Medium gray base paint ratio:

[0137] Base paint 99.2%

[0138] Carbon black 0.78%

[0139] Blush blue 0.02%

[0140] Brown base paint ratio:

[0141] Base paint 98.5%

[0142] Carbon black 0.08%

[0143] Iron Oxide Red 0.9%

[0144] Iron Oxide Yellow 0.5%

[0145...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
Login to View More

Abstract

The invention relates to a micro-crystal color art coating as well as a preparation method and application thereof. The micro-crystal color art coating is prepared from the following raw materials in percentage by weight: 15-20% of a granulation glue solution, 60-70% of base paint, 10-20% of outer coating varnish and 0.1-10% of a thickening agent. The preparation method of the micro-crystal color art coating comprises the following steps of: mixing the base paint and pigment (at least comprising particles in two different colors) for color mixing, adding the granulation glue solution for dispersion and color point granulation, adding the thickening agent for adjusting the viscosity, adding the outer coating varnish, and stirring well to obtain the micro-crystal color art coating. The micro-crystal color art coating belongs to colorful coatings, and contains two or more types of colorful particles. A more colorful decorative effect can be drawn according to design,and the aesthetic needs of people can be met. Meanwhile, the coating can be directly sprayed and is convenient to construct.

Description

technical field [0001] The invention relates to the technical field of coatings, in particular to a microcrystalline color art coating and a preparation method and application thereof. Background technique [0002] With the great development of our country's economy and the great improvement of people's living standards, the traditional pure-color interior wall paint has gradually changed to the use of art paint for decoration in terms of decorative effect. However, the traditional art paint has a long construction period on the one hand, and on the other hand The construction is more difficult and the price is more expensive, which limits its application. In terms of color, art paints usually use a single color. This is because when different colors are mixed in the paint, it is easy to cross colors or merge into new colors. It cannot maintain the original two colors when they are alone, so it is impossible to realize the simultaneous existence of multiple colors. colorful...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D133/04C09D7/61C09D7/65
CPCC09D143/04C09D7/61C09D7/65C08L43/04C08L1/02C08K3/013C08K3/34
Inventor 刘东华武文斌吴择炜朱同林颜宇强
Owner 厦门富思特新材料科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com