Electromagnetic shielding wave-absorbing material and manufacturing process thereof
A wave-absorbing material and electromagnetic shielding technology, applied in the fields of magnetic/electric field shielding, flat products, electrical components, etc., can solve the problems that wave-absorbing powder cannot be added evenly, mass production is time-consuming and laborious, and thick sheets cannot be made. , to achieve the effect of easy control of product size, small investment in equipment, and small demand for personnel
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Example Embodiment
[0027] Example 1
[0028] An electromagnetic shielding absorbing material that includes the following components by weight:
[0029] CPE7130 powder is 6 servings
[0030] Iron silicon chromium absorbing powder 13 parts.
[0031] The production process of electromagnetic shielding absorbing material is as follows:
[0032] (1): CPE7130 powder with a weight of 6 parts is added to the mixer for 10 minutes of mixing;
[0033] (2): Add 13 parts of iron silicon chromium suction powder to the densely refined CPE7130, and mix CPE7130 and iron silicon chromium absorbing powder evenly through the principle of kneading;
[0034] (3): The mixed material is put into the granulation equipment, and the mixture particles with a length of no more than 2mm are created, and the mixture particles with stable performance are obtained after air cooling
[0035] (4): The mixture particles are extruded by the extruder and then the calender is pressed to obtain a wave-absorbing material with uniform thick...
Example Embodiment
[0039] Example 2
[0040] An electromagnetic shielding absorbing material that includes the following components by weight:
[0041] CPE7130 powder is 6 servings
[0042] Iron silicon chromium absorbing powder 13 parts.
[0043](1): CPE7130 powder with a weight of 6 parts is added to the mixer with a heating temperature of 135 °C to start the machine for 8 minutes of sealing;
[0044] (2): Add 13 parts of iron silicon chromium suction powder to the densely refined CPE7130, and mix CPE7130 and iron silicon chromium absorbing powder evenly through the principle of kneading;
[0045] (3): the mixed materials are put into the granulation equipment, the equipment temperature parameters are 60 °C in area A, 80 °C in area B, 120 °C in area C, and the length is not more than 2 mm of mixture particles, which are dried by water cooling and air to obtain stable performance of mix particles;
[0046] (4): The mixture particles are extruded by the extruder and then the calender is pressed to ...
Example Embodiment
[0048] Example 3
[0049] An electromagnetic shielding absorbing material that includes the following components by weight:
[0050] CPE7130 powder is available in 7 servings
[0051] Iron silicon chromium absorbing powder 14 parts.
[0052] The production process of electromagnetic shielding absorbing material is as follows:
[0053] (1): CPE7130 powder with a weight of 7 parts is added to the mixer for 9 minutes of sealing;
[0054] (2): Add 14 parts of iron silicon chromium absorbing powder to the densely refined CPE7130, and mix cpE7130 and iron silicon chromium absorbing powder evenly through the principle of kneading;
[0055] (3): The mixed material is put into the granulation equipment, and the mixture particles with a length of no more than 2mm are created, and the mixture particles with stable performance are obtained after air cooling
[0056] (4): The mixture particles are extruded by the extruder and then the calender is pressed to obtain a wave-absorbing material wit...
PUM
Property | Measurement | Unit |
---|---|---|
Thickness | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap