Water-absorbency resin composition

A resin composition, water-absorbent technology, applied in the direction of absorbent pads, medical science, bandages, etc., can solve the problems of liquid permeability or gel strength becoming low, deterioration, urine leakage out of disposable diapers, etc.

Inactive Publication Date: 2006-10-25
NIPPON SHOKUBAI CO LTD
View PDF5 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The problem is that when a water-absorbent resin is used as an absorbent structure of a disposable diaper, the water-absorbent resin deteriorates with time, so that its liquid permeability or gel strength becomes low, causing urine to leak out of the disposable diaper
However, the existing technology only enhances the urine resistance, and as for the light resistance, it is the same as the result without adding glycine chelating agent

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Water-absorbency resin composition

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0118] Under stirring conditions, 60% sulfuric acid was added into a commercially available pentasodium diethylenetriaminepentaacetic acid aqueous solution (40% solid content) to adjust the pH to a range of 1.8 to 2. The resulting solution was left to stand for a while, and then deposited diethylenetriaminepentaacetic acid was filtered off, washed with pure water and dried at 60°C.

[0119] The total content of nitrilotriacetic acid (salt) in the commercially available diethylenetriaminepentaacetic acid pentasodium is about 5%, but through the above-mentioned treatment, the nitrilo group in the obtained diethylenetriaminepentaacetic acid The total content of triacetic acid (salt) was reduced to 35ppm of diethylenetriaminepentaacetic acid.

[0120] Add 0.05 parts of ethylene glycol diglycidyl ether, 1 part of propylene glycol, 3 parts of water and 1 part of isopropyl to 0.002 parts of diethylenetriaminepentaacetic acid obtained above with a reduced total content of nitrilotriac...

Embodiment 2

[0123] The water-absorbent resin composition (2) was obtained in the same manner as in Example 1, except that the amount of diethylenetriaminepentaacetic acid in the treatment agent solution was changed to 0.01 part (diethylenetriaminepentaacetic acid in the obtained composition The mixing ratio of the water-absorbent resin (A) is 100ppm).

[0124] The total content of nitrilotriacetic acid (salt) in the water absorbent resin composition (2) was measured. As a result, the content was equal to or less than 0.1 ppm of the composition, so it could not be measured. Table 1 shows the measurement results of physical properties of the water-absorbent resin composition (2).

Embodiment 3

[0126] Diethylenetriaminepentaacetic acid (obtained in Example 1) having a reduced total nitrilotriacetic acid (salt) content was dissolved in water to prepare a 0.07% aqueous solution. 3 parts of this solution was sprayed on 100 parts of the water-absorbent resin (B) (obtained in Reference Example 1), and then dried at 80°C to obtain a water-absorbent resin composition (3) (in which diethylenetriaminepentaacetic acid The mixing ratio is 21 ppm of the water absorbent resin (B).

[0127] The total content of nitrilotriacetic acid (salt) in the water absorbent resin composition (3) was measured. As a result, the content was equal to or less than 0.1 ppm of the composition, so it could not be measured. Table 1 shows the measurement results of physical properties of the water-absorbent resin composition (3).

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
adsorption capacityaaaaaaaaaa
adsorption capacityaaaaaaaaaa
particle diameteraaaaaaaaaa
Login to view more

Abstract

The present invention provides a water-absorbent resin composition comprising a water-absorbent resin and a water-soluble deodorant, and exhibiting no-load absorption of not less than 30 g / g and elution of degraded extractable components of not more than 20 % by weight, the absorption under a load of 1.9 kPa is not less than 28 g / g, and the reduction ratio of bad smell is not less than 40%. The absorbent resin composition has deodorizing ability.

Description

[0001] This application is a divisional application of the Chinese patent application with the application number CN00136418.9 and the invention name "water-absorbent resin composition". technical field [0002] The present invention relates to a water absorbent resin composition. Specifically, the present invention relates to a water-absorbent resin composition which is excellent in urine resistance and light resistance and which is less colored. In addition, the present invention relates to a water-absorbent resin composition also having excellent deodorizing ability. Background technique [0003] In recent years, water-absorbent resins have been widely used as components of hygienic articles such as disposable diapers, sanitary napkins, and incontinence sheets for the purpose of allowing the water-absorbent resins to absorb body fluids such as urine and menstrual blood. [0004] As for the above-mentioned water-absorbent resins, the following examples are known: partiall...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C08L101/00A61L15/22A61L15/46A61L15/60C08K5/17
CPCA61L15/46A61L15/60C08K5/175C08L33/02
Inventor 三宅浩司藤野真一中村将敏和田克之
Owner NIPPON SHOKUBAI CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap